Two component Epoxy based anticorrosive primer containing red oxide and zinc phosphate as corrosion inhibiting pigments
Recommended Use :-
This product is recommended as a primer on suitably cleaned mild steel surface in various fertilizer units, refineries, chemical and other plants, transportation industries, steel plants, cement plants, power plants, pulp and paper industries, pharmaceutical industries, etc. for application on tank exteriors, structural steel, pipelines, machineries, vessels, etc. The product is recommended as a primer for mild to moderate corrosion conditions. Not to be recommended for immersed water condition.
Physical Data :-
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 ± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt. / ltr. at DFT of 30 �µ
FLASH POINT : Base : Above 23�°C Hardener : Above 23�°C
DRYING CHARACTERISTICS (At 300 C & 65% Relative Humidity) : HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray
THINNER : Epoxy Thinner 190
POT LIFE : 4 hours min at 30C
RECOMMENDED DFT : 30 - 40
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated Rubber and Synthetic Enamel Finish Paints.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix, gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction.
Application : By Brush / By Conventional Spray / By Airless Spray Generally no thinner is required for Brush application; however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in crossed manner, ensuring the uniform application. Use quality brushes for paint application. Add Epoxy Thinner Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the paint through Nylon filter cloth and apply uniformly over the surface. All equipments used for above should be properly clean.
For Conventional Spray application :-
Thinner : Epoxy Thinner 190
Addition : 10-15%
Nozzle Orifice : 1.2 -1.4 mm
Nozzle Pressure : 40-70 p.s.i.
For Airless Spray application :-
Thinner : Epoxy Thinner 190
Addition : Max 5% if required
Nozzle Orifice : 0.37- 0.42mm
Nozzle Pressure : 1400-1800 p.s.i.
Two component Epoxy based anti corrosive primer containing zinc phosphate as corrosion inhibiting pigments
Recommended Use :-
It is an ideal primer where faster turnaround of equipment is desired, Hence making it ideal primer for industrial and Infrastructure equipments, heavy machineries etc exposed to medium corrosive and marine environment. It is also recommended for steel structures in Chemical, Fertilizers, Petrochemical and industrial plants. Not to be used for immersion application.
Physical Data :-
COLOUR : Grey, Yellow, Beige, Red oxide
FINISH : Egg Shell
SOLIDS BY VOLUME : 48 ± 3% (Depends on shade)
THEORETICAL SPREADING RATE : sq.mt / lit at recommended DFT of 30 µ
FLASH POINT : Base : Above 23C Hardener : Above 23C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30C) : DRY TO HANDLE: 3 hr's max FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray
THINNER : Epoxy Thinner 190
POT LIFE : 4 hours min at 30C
RECOMMENDED DFT : 30 - 40 µ.
OVERCOATING INTERVAL : MIN : 2 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous Top coats.
Two component air drying Epoxy based clear primer with Polyamide as curing agent.
Recommended Use :-
This product is recommended as penetrating primer on bare concrete, wooden substrate prior to application of subsequent coating system.
Physical Data :-
COLOUR : Clear
FINISH : Smooth & Glossy
SOLIDS BY VOLUME : 50 �± 3%
THEORETICAL SPREADING RATE : 20 sq.mt. / ltr. at a recommended DFT of 25 �µ
FLASH POINT : Base : Above 23�°C Hardener : Above 23�°C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30�°C) : HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Thorough surface preparation is vital. For best results, saffro recommends mechanical preparation techniques (Eg. mechanical scarifying, grit or sand sweeping),
a) New Concrete Surface :-
New concrete surface should be at least 28 days old and/or have moisture content of less than 5% before proceeding with primer application. Laitance and deposits on new concrete are best removed by light grit blasting, mechanical scarification or grinding. Acid etching may be considered for smaller areas, after etching the floor, it should be thoroughly washed with clean water, and then allowed to dry.
b) Old Concrete Floors :-
Mechanical cleaning methods are strongly recommended on old concrete surfaces, particularly their heavy contamination by oil and grease has occurred or old coatings is present. To ensure good adhesion, all contaminants are removed and the surface thoroughly cleaned of all dust and loose debris. A thorough detergent wash is also recommended followed by thorough cleaning with water and moping it off to a dry state.
Two component, air drying, high solids, Epoxy coating. The product has the advantage of epoxy resin composition with speciality pigment, which facilitates one-coat, high build application for high performance. The product can be applied on minimum prepared surface and is designed to completely wet the substrate. Excellent adhesion is obtained on a variety of intact surfaces including over old coating and tightly adherent rust. The composition has been balanced to a convenient mixing ratio by volume with excellent application characteristics. The low solvent content reduces the problem of lifting of the paint film and adhesion failure by blistering and pin holing. This assures a stable long term performance.
Recommended Use :-
It is mainly recommended in those areas where blasting is impractical or impossible. Uses include steel structures in Industrial plants, bridges, tank exteriors, oil tanks, pipes, marine atmosphere, cooling towers, etc. It has good resistance to spillage and fumes of acids, alkalis, fresh and salt water. Recommended as a primer on suitably cleaned mild steel surface in various Fertilizer units, Refineries, Chemical and other plants, Transportation industries, steel plants, cement plants, power plants, pulp and paper industries, pharmaceutical industries, etc. for application on tank exteriors, structural steel, pipelines, machineries, vessels, etc.
Physical Data
COLOUR : Selected industrial shades
FINISH : Semi glossy
SOLIDS BY VOLUME : 80 + 2%
THEORETICAL SPREADING RATE : 10 sq.mt. / ltr. at a recommended DFT of 80
FLASH POINT : Base : Above 25C Hardener : Above 25C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30�°C) : SURFACE DRY : 4 hours FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
Application Data :-
MIXING RATIO : Base : Hardener ( As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
RECOMMENDED DFT : 75-100 mic.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous topcoats.
Two Component, Air-drying, Epoxy Polyamide Cured Finish Paint.
Recommended Use :-
It Is Recommended As A Top Coat For Structures, Pipelines, Vessels, Equipments And Machineries, Storage Tanks Etc. In Fertilizers And Chemical Plant, Cement Plants, Power Plants, Steel Plants, Pharmaceutical And Petrochemical Complexes, Refineries Etc. Product Is Also Recommended For Application Over Suitable Primer For Oem Industry Like Machine Tools, Pumps, Machineries, Transformers Etc.
Physical Data
Colour : assorted Shades
Finish : glossy / Semi Glossy
Solids By Volume : 40 +3% (depends On Shade)
Theoretical Spreading Rate : 13.33 Sq.mt / Ltr At Recommended Dft Of 30 au Flash Point : base: Above 23 C Hardener: Above 23 C
Drying Characteristics (at 30'c And 65% Relative Humidity) : hard Dry : Overnight Full Cure : 7 Days
Shelf Life : base : 6 Months Hardener : 6 Months
Surface Preparation
This Being A Topcoat, Which Is Applied Over, Primer Or Intermediate Coats, The Surface Should Be Free From Oil, Moisture, Dust And Dirt. Aged Epoxy / Pu Coating Should Be Roughened By Emery Paper Grade 400 / 600 For Better Bonding.
Application Data :-
Mixing Ratio : base : Hardener (as Per Our Recommendation)
Application : by Brush / By Conventional Spray / By Airless Spray
Thinner : 190
Pot Life : 4-6hrs Min At 30 C
Recommended Dft : 30-40 U
Over Coating Interval : min : 8 Hours Max : 24 Hours
Compatibility : can Be Over Coated With Pu, Chlorinated Rubber And Synthetic Enamel Paints.
6599 Paints Coatings Suppliers
Short on time? Let Paints Coatings sellers contact you.
Two component, air-drying, Epoxy polyamide cured finish paint.
Recommended Use :-
It is recommended as a top coat for structures, pipelines, vessels, equipments and machineries, storage tanks etc. in fertilizers and chemical plant, cement plants, power plants, steel plants, pharmaceutical and petrochemical complexes, refineries etc. Product is also recommended for application over suitable primer for OEM industry like machine tools, pumps, machineries, transformers etc.
Physical Data
COLOUR : Assorted Shades
FINISH : Semi glossy
SOLIDS BY VOLUME : 40 �± 3% (Depends on shade)
THEORETICAL SPREADING RATE : 13.33 sq.mt / ltr at recommended DFT of 30 �µ
FLASH POINT : Base: Above 23�° C Hardener: Above 23�° C
DRYING CHARACTERISTICS : SURFACE DRY : 90 minutes max HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
This being a topcoat, which is applied over, primer or intermediate coats, the surface should be free from oil, moisture, dust and dirt. Aged epoxy / PU coating should be roughened by emery paper grade 400 / 600 for better bonding.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : 190
POT LIFE : 4-6hrs min at 30 �° C
RECOMMENDED DFT : 30-40 �µ
OVER COATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with PU, Chlorinated rubber and synthetic enamel paints.
Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.
Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.
Physical Data
COLOUR : Grey
FINISH : Matt
SOLIDS BY VOLUME : 40 �± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT : Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) : SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.
Application Data
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional Spray
THINNER : Thinner 290
POT LIFE : 3 hours min at 30�° C
RECOMMENDED DFT : 30-40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX :24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY : Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.
Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.
Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.
Physical Data :-
COLOUR :- Yellow
FINISH :- Matt
SOLIDS BY VOLUME :- 40 �± 3%
THEORETICAL SPREADING RATE :- 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT :- Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) :- SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE :- BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.
Application Data
MIXING RATIO :- Base : Hardener (As per our recommendation)
APPLICATION :- By Brush / By Conventional Spray
THINNER :- Type 290
POT LIFE :- 3 hours min at 30�° C
RECOMMENDED DFT :- 30-40 �µ.
OVERCOATING INTERVAL :- MIN : 8 hours MAX :24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY :- Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Add Thinner Type 290 into the mix, if required, depending on application method, and stir gently for few minutes. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Strain the paint through Nylon filter cloth of 200 mesh size and apply uniformly over the surface. All equipments used for above should be properly clean.
Application :- By Brush / By Conventional Spray / By Airless Spray
Generally no thinner is required for Brush application, however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in crossed manner and ensuring the uniform application. Use quality brushes for paint application.
For Conventional Spray application :-
Thinner : Type 290
Addition : 10-15%
Nozzle Orifice : 1.2 -1.4 mm
Nozzle Pressure : 40-70 p.s.i.
For Airless Spray application :-
Thinner : Type 290
Addition : Max 5%
Nozzle Orifice : 0.28- 0.37 mm
Nozzle Pressure : 1400-1800 p.s.i.
Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.
Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.
Physical Data
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 �± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT : Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) : SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional Spray
THINNER : Type 290
POT LIFE : 3 hours min at 30�° C
RECOMMENDED DFT : 30-40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY : Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.
Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.
Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.
Physical Data :-
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 �± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT : Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) : SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional Spray
THINNER : Type 290
POT LIFE : 3 hours min at 30�° C
RECOMMENDED DFT : 30-40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX :24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY : Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.
Recommended Use :-
Recommended over putty / primer applied surfaces for better gloss retention and aesthetics in topcoats.
Physical Data :-
COLOUR : Grey, White
FINISH : Egg Shell to Matt
SOLIDS BY VOLUME : 40 �± 3%
SPREADING RATE : 13.3 sq.mt / ltr at recommended DFT of 30 �µ
FLASH POINT : Base : 23�°C Hardener : 23�°C
DRYING CHARACTERISTICS (At 30�°C & 65% Relative Humidity) : SURFACE DRY : 20-30 minutes. HARD DRY : Overnight. FULL CURE : 7 Days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
This being intermediate, it is applied either over primer. The surface should be free from moisture, oil and dust before application. In case of aged epoxy / PU coating or exceeded over coating, the surface should be sufficiently roughened prior to painting.
Application Data :-
MIXING RATIO : Base: Hardener ( As per our recommendation)
APPLICATION : By Brush/ By Conventional Spray / By Airless Spray
THINNER : Type 290
POT LIFE : 4 hours min at 30�° C
RECOMMENDED DFT : 30 -35 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be top coated by PU, epoxy, Chlorinated rubber and synthetic enamel paints. Compatible with Epoxy and zinc rich primers.
Recommended Use :-
This product is a topcoat along with recommended undercoats for use in chemical plants, fertilizer plants, petrochemical and pharmaceutical complex, power plants, cement plants, steel plants, heavy chemicals and off-shore and on-shore industries.
It is recommended for very high chemical resistance and for areas not exposed to direct sunlight. Product is also recommended for application over suitable primer for OEM industry.
Physical Data
COLOUR : Assorted shades
FINISH : Glossy / Semi glossy / Matt
SOLIDS BY VOLUME : 40 ± 3% (Depends on shade)
THEORETICAL SPREADING RATE : 13.33 sq.mt / lt at recommended DFT of 30 µ
FLASH POINT : Base : Above 23 C Hardener : Above 23 C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) : SURFACE DRY : 30 minutes max HARD DRY : Overnight FULL CURE : 7 DAYS.
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
The surface of primer or intermediate coats, over which this product is applied as topcoat, should be free from oil, moisture, dust and dirt. Aged coatings should be roughened by emery paper grade 400 / 600 for better bonding.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional spray / By Airless Spray
THINNER : Type 290
POT LIFE : 3 hours min at 30 C
RECOMMENDED DFT : 30-40 µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be applied over Epoxy and Polyurethane primers, intermediate coats and topcoats.
Two component air drying aromatic polyurethane finish coating
Recommended Use :-
It is recommended as topcoat for Original Equipment Machines, Hygienic, Maintenance painting where mild chemical resistance along with good abrasion resistance and decorative finish are required. Sometimes it is recommended as undercoat of finish coats application for economic benefits.
Physical Data
COLOUR : Assorted shades
FINISH : Glossy / Semi glossy / Matt SOLIDS BY
VOLUME : 40 �± 3% (Depends on shade) THEORETICAL
SPREADING RATE : 13.33 sq.mt / lit at recommended DFT of 30
FLASH POINT : Base : Above 23C Hardener : Above 30C
DRYING CHARACTERISTICS : SURFACE DRY :20 - 30 minutes (At 30C and 65% Relative humidity) HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
This being a Topcoat, which is applied over underneath primer or intermediate coats, the surface should be free from oil, moisture, dust and dirt. Aged coatings should be roughened by emery paper grade 400 / 600 followed by solvent wipe for better bonding.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional spray / By Airless Spray
THINNER : Type 290
POT LIFE : 3 hours min at 30 C
RECOMMENDED DFT : 30-40
OVERCOATING INTERVAL : MIN : 8 hours MAX :24 hours
COMPATIBILITY : Can be applied over Epoxy and Polyurethane primers, intermediate coats and topcoats.
Two-component Air Drying Acrylic Aliphatic, Non Yellowing polyurethane finish coating.
Recommended Use :-
This product has excellent weathering resistance additionally it offers excellent resistance to various industrial chemical fumes and splash. This product is recommended as topcoat with suitable primers and undercoats for use in High Chemical & Saline atmosphere for better aesthetics and corrosion resistance in Chemical, Fertilizers, Petrochemical, industrial plants and also for premium industrial equipments. Not recommended for immersion application.
Physical Data
COLOUR : Industrial Shades
FINISH : Glossy / Semi-glossy
SOLIDS BY VOLUME : 40 + 3% (Depends on shade)
THEORETICAL SPREADING RATE : 13.33 sq.mt / ltr @ recommended DFT of 30
FLASH POINT : Base : Above 23 C Hardener : Above 23C
DRYING CHARACTERISTICS (At 300 C & 65% Relative Humidity) : SURFACE DRY : 30 minutes max HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
This being a topcoat, which is applied over, primer or intermediate coats, the surface should be free from oil, moisture, dust and dirt. Aged epoxy / PU coating should be roughened by emery paper grade 400 / 600 for better bonding.
Application Data :-
MIXING RATIO : Base: Hardener - As per our recommendations
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Type 290
POT LIFE : 4 hours min at 30C
RECOMMENDED DFT : 30- 40 .
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be applied over Epoxy and Polyurethane primers, intermediate coats and topcoats.
Various interior and exterior paints.
All eco-friendly products
Same quality as European products while nearly a half price from their prices
30 years of know-how and experiences
We are producing Anti-corrosive Paint and Industrial Paint.
We have a vision of Paints for the future.
Our mission is to produce suitable products with long term durability that can meet customer's requirement.
For the future of our customers We would like to bring to our customers the most satisfaction about quality and after sale service.
For the future of paint We always aim for better technology, supply improved products better than yesterday.
Theaoson all purpose foamy cleaner is a water-based formula, rich in foam, made of natural green plant-synthesized surfactants and the latest high-tech formulas. It has fast penetration, strong detergency and super deep cleaning efficiency, and can remove any stains easily. This product does not contain phosphate, it is harmless to the environment, the foam is delicate and rich, the smell is aromatic, and it is safe and convenient to use.
It is a water-in-oil system formula, which integrates infiltration, cleaning and glazing at one time. It is rich in cleaning foam, which can effectively remove oil stains and dirt on the treated surface. After use, it can restore the luster of the surface and restore it as new.
Theaoson sticker remover is composed of aerosol can, aerosol valve, paint solution and propellant. This product uses mild remove formula, can effectively dissolve the surface colloid of the removed object, do not corrode the surface of the object, spray and wipe just once, easy to remove.