Description
Two component, air drying, high solids, Epoxy coating. The product has the advantage of epoxy resin composition with speciality pigment, which facilitates one-coat, high build application for high performance. The product can be applied on minimum prepared surface and is designed to completely wet the substrate. Excellent adhesion is obtained on a variety of intact surfaces including over old coating and tightly adherent rust. The composition has been balanced to a convenient mixing ratio by volume with excellent application characteristics. The low solvent content reduces the problem of lifting of the paint film and adhesion failure by blistering and pin holing. This assures a stable long term performance.
Recommended Use :-
It is mainly recommended in those areas where blasting is impractical or impossible. Uses include steel structures in Industrial plants, bridges, tank exteriors, oil tanks, pipes, marine atmosphere, cooling towers, etc. It has good resistance to spillage and fumes of acids, alkalis, fresh and salt water. Recommended as a primer on suitably cleaned mild steel surface in various Fertilizer units, Refineries, Chemical and other plants, Transportation industries, steel plants, cement plants, power plants, pulp and paper industries, pharmaceutical industries, etc. for application on tank exteriors, structural steel, pipelines, machineries, vessels, etc.
Physical Data
COLOUR : Selected industrial shades
FINISH : Semi glossy
SOLIDS BY VOLUME : 80 + 2%
THEORETICAL SPREADING RATE : 10 sq.mt. / ltr. at a recommended DFT of 80
FLASH POINT : Base : Above 25C Hardener : Above 25C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30�°C) : SURFACE DRY : 4 hours FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
Application Data :-
MIXING RATIO : Base : Hardener ( As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
RECOMMENDED DFT : 75-100 mic.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous topcoats.
Dyo hb epoxy primer Excellent adhesion over galvanized surfaces. High resistance against corrosion, hummidity and chemicals. Its high thixotropric nature provides it to be applied as thick layer. It resists temperature up to 150 c degrees without change in colour. Drying speicifications: 8 h at 20 c degrees 50 min. At 80 c degrees 30 min. At 100 c degress 20 min. At 140 c degrees Packaged in 24.5 kg can
A high build two pack MIO pigmented epoxy primer with excellent water & chemical resistance . The product is very effective in marine and corrosive chemical environment. It has outstanding abrasion resistance and conforms to BS 5493 when used in combination with Wellguard epoxy / polyurethane topcoats. It has excellent wear resistance and exterior durability.
An anticorrosive primer/ intermediate topcoat based on high molecular, two pack, epoxy-polyamide resin system and anticorrosive pigment excellent drying, adhesion and abrasion resistance properties.
Industrial Finishes & Epoxy Ps1201- Penetrating Sealer (Sb) Ps1201- Texotile Epoxy Primer Ps1301- Red Oxide Primer Ps1311- Synthetic Primer Ps1351- Synthetic Wood Primer Ps1401- Zinc Phosphate Primer Ps1471- Quick Drying Primer (Matt) Ps1501- Epoxy Primer Clear Ps1551- Epoxy Primer Ps1552- Epoxy Red Oxide Primer Ps1554- Epoxy Zinc Chromate Primer Ps1601- Etch Primer Ps1701- Epoxy Zinc Rich Primer Ps2011- Epoxy Putty Ps2401- Texoile Epoxy Compound Ps2501- Synthetic Undercoat Ps3001- Synthetic Alkyd Topcoat Enamel (Standard) Ps3005- Synthetic Alkyd Topcoat Enamel (Standard) Ps3105- Thermoplastic Topcoat (White) Ps3106- Chlorinated Rubber Topcoat PS3151- THERMOPLASTIC TOPCOAT (CLEAR) PS3201- QUICK DRYING ENAMEL PS3251- SYNTHETIC TOPCOAT CLEAR PS3261- SYNTHETIC ALKYD TOPCOAT ENAMEL (SEMI GLOSSY) PS3271- PARQUET VARNISH PS3351- SYNTHETIC ALKYD TOPCOAT ENAMEL (MATT) PS3401- ALUMINUM PAINT PS3402- ALUMINUM PAINT HEAT RESISTANCE PS3501- STOVING TOPCOAT PS3601- EPOXY FLOOR COATING PS3651- EPOXY TOPCOAT CLEAR PS3751- ACRYLIC ROAD MARKING PAINT PS3751- THERMOPLASTIC TOPCOAT PS3851- ACRYLIC 2K TOPCOAT (HB) BASECOAT METALLIC (1K) -XXXXX BASECOAT METALLIC (2K)- XXXXX ACRYLIC 2K PRIMER- XXXXX CR ROAD MARKING PAINT- XXXXX DIPPING ENAMEL- XXXXX PU BASECOAT CLEAR-XXXXX PU BASECOAT PIGMENTED- XXXXX PU TOPCOAT CLEAR- XXXXX PU TOPCOAT CLEAR (ACRYLIC)- XXXXX PU TOPCOAT PIGMENTED- XXXXX QUICK DRYING PRIMER (SG) - XXXXX PS1302 - Synthetic Red Oxide Primer Commercial THINNERS ZINC SILICATE PRIMER- XXXXX PS1302 - Synthetic Red Oxide Primer Commercial