SMOKELESS FIBERGLASS NEEDLED MAT
Product
Smokeless fiberglass needled mat, ordorless fiberglass needled mat
Material
E-glass
Thickness mm
3mm-10mm
Density
111-50kg/m³
Thermal conductivity
0.032 0.039W/m 25
Max temp.
700
Long term temp.
550
Features
Eco-friendly, smokeless, ordorless
The product (smokeless fiberglass needled mat, odorless fiberglass needled mat) is made from fiberglass as the material.
How is a smokelss fiberglass needled mat manufactured? And what is its feature?
It undergoes a heating process in different stages to carbonize trace organic substances within the fiberglass wool. During the carbonization process, there may be a slight odor and smoke generated. After the baking process, the surface of the product can exhibit either a white or yellowish color, depending on the baking temperature.
Compared to fiberglass wool that hasn't undergone baking, the baked fiberglass wool retains its original properties while eliminating the generation of smoke and odor when subjected to reheating between 200-500C.
Why does an oven(home appliance) need ther thermal insulation(smokeless fiberglass needled mat, odorless fiberglass needled mat)?
This odorless fiberglass needled mat is usually used as thermal insulation( liner or pad) for home appliances such as environmentally sensitive grills, ovens, disinfection cabinet, microwaves and other appliances, which are subject to strict environmental regulations. If a domestic appliance (eg. oven) is added with this thermal insulation , it will be more energy efficient to prevent heat escaping from the oven and it will reach temperature faster and reduce cooking time.
The smokeless fiberglass needled mat is available in rolls or die cut pieces based on requests.
The smokeless mat can be laminated with fiberglass fabric, foil facing, aluglass cloth facing,or coated with self adhesive based on your request.
Small sample pieces are free and freight to collect.
fiberglass needle mat is a good thermal and voice insulation material A.Density toralence +15%-10% B. Heat Resisting 700C degree.Softening temperature: 850 C C.High tensile strength: 350kg/mm ,Modules of elasticity:7300kg/mm ,Elongation at 25 C:4.8%,Flexible: conforms to irregular surfaced D.Corrosion Properties:does not absorb water,rot,mildew,deteriorate or decay. E. Application:Applications Muffler and exhaust insulation ,Automotive catalytic converter, flooring and front dash insulation ,Removable pads,Ship turbines ,Marine, industrial, and process piping ,Power generating equipment,Industrial furnaces and ovens ,Filtration ,Gaskets for air conditioning
Fiberglass wool/ needle mat/ rock wool/ glass wool/ felt/ blankets/ sheet 1. Producing Fiberglass wool is made from fiberglass strands chopped to cut in fixing length, and then after dealing with devillicate, fluffing, needling to make to end product. It is ceaselessly sewn by thousands of stitched. 2. Feature Long time operating temperature: 650°c Thermal coefficient: room temperature 0.035w/ m*k Hygroscopicity: 5% Density: 110-180kg/ m3 3.Usage It is widely used for conductex, iron, non-ferrous metal, chemical, burning industry etc, especially industry filter material in domestic. It is used in car internal decorate, sound absorption, heat insulation, damping, antiflaming, geotextile and insulation materials. 4. Technical parameter Itemthickness (mm)area weight(g/m)density (mm)roll length (mm) Emn334501000-200040 Emn446001000-200040 Emn557501000-200030 Emn669001000-200030 Emn8812001000-200020 Emn101015001000-200020 Emn121218001000-200015 Emn151522501000-200015
e-glass needle mat which is a thermal and acoustic insulation mat. The raw material is e-glass textil fiber roving, diameter 9um.
It is made of randomly yet evenly distributed chopped strands fiber of 50mm or 100mm length stitched by polyester thread. It has high tensile strength and is recommended for Pultrusion process,Uncontinuous winding Process & Laminates. Products Property: No any Binder, good compatible with Multi-Resin Optimal mechanical performance Easy workability and low cost Standard width: 120cm/127cm/160cm Max. width 320cm, Min. width 3.5cm Standard Roll weight: 45/48/60kg
It is made of randomly yet evenly distributed chopped strands fiber of 50mm or 100mm length stitched by polyester thread. It has high tensile strength and is recommended for Pultrusion process,Uncontinuous winding Process & Laminates. Products Property: No any Binder, good compatible with Multi-Resin Optimal mechanical performance Easy workability and low cost Standard width: 120cm/127cm/160cm Max. width 320cm, Min. width 3.5cm Standard Roll weight: 45/48/60kg Packaging: Each roll is wound on paper tube (3"-4"Dia.) with plastic film and packed in individual cardboard box. 16 or 12 cartons per Pallet. The strength of fiberglass stitched mat is stronger than CSM,the price is cheaper. We export large quantity for pipe winding.We can provide big roll to reduce your replacing frequency and save your cost.We suggest stitched mat instead of chopped strand mat for pipe application. Use in close mold applications such as RTM, VARTM, SCRIMP. Can be pultruded when layered with other materials. Stitched construction allows for pattern or die cutting. Stitch Mat will not wash out in RTM process. and can be pre-wet and moved for proper placement in wet lay-up open molding. it gives uniform thickness compared to extra spray-up in open molding. it is low cost alternative for building thickness and stiffness, where the component is not weight critical. Binderless chopped E-Glass, stitched at 7 gauge The chopped strand length is 5cm or 10cm, 10cm for pultusion to improve the strength.
As a subsidiary of a Chinese state-run company. it offers the best quality & most competitive price.
Fiberglass mat In 200, 250, 300 and 450 grams per meter square frp mat 30 or 36 kgs per roll
300g fiberglass mat/ chopped strand mat/ csm/ sheet/ felt 1.Introduction E-glass chopped strand mat is made of randomly distributed chopped strands held tighter by a emulsion/ powder binder. It is compatible with unsaturated polyester, vinylit, epoxy resins. The roll width ranges from 50mm to 2080mm. Special requirements may be available upon request. 2.Usage It is used for processing and manufacturing frp products with getting through hand lay up process, filament winding process and press molding. Typical products is including bathroom accessories, pipe, building material, automobile, furniture, vessel, cooling towers and other frp products 3.Packing Product is manufactured in form of a roll wound on a paper tube and then packed in a plastic film and placed within a cardboard carton. Rolls can be loaded into a container directly or on pallets. 4.Parameter Density(g/m2Moisture content (%Loss on ignition (%Binder typeWidth (mm) 2250.22.1-6.3Powder/ emulsion1040 1270 2080 2500.22.1-6.3Powder/ emulsion1040 1270 2080 3000.22.1-6.3Powder/ emulsion1040 1270 2080 4500.22.1-6.3Powder/ emulsion1040 1270 2080 6000.22.1-6.3Powder/ emulsion1040 1270 2080
Fiberglass stitched mat is made from chopped fiberglass strands or woven roving which is cut into a certain length and randomly dispersed , laid on a roving matrix then stitched together with organic fibers. Fiberglass stitched mat is used in unsaturated polyester resin strenthen, primarily in pultrusion, rtm, filament winding and hand lay-up processed. Such as pultruded parts, pipes, storage tanks, wind generator blades and other frp products. Product properties: 1. Even thickness, high wet tensile strength retention 2. Directional properties and strengths same to woven roving 3.Enough hollows on surface to make it good permeability 4. Flexibility to design variety weaving structures 5. Stable structure required to achieve maximum tensile strength properties. Shrink film packing and sealing and then package them with carton.