Description
VGROUT6 is a non-shrink, pourable cementitious grouting mortar with extended working time to suit local ambient temperatures.
- Excellent flowability
- Good dimensional stability
- High strengths, adjustable consistency
Product name: VGROUT6
Compressive strength: M60 (N/mm2) / 60 Mpa / 8700 psi
Mixing ratio:
- 25kgs powder: 4,0L water
- 5kgs powder: 0,8L water
ADVANTAGES
- Easy to mix and apply
- Flowable consistency (according to mix)
- Rapid strength development
- Non-corrosive
- Non-toxic
- Iron and chloride free
- Shrinkage-compensated
- Good pumping properties
Application
- Where exceptional one day and ultimate compressive strengths are required.
- Applications requiring a pumpable grout.
- Non-shrink grouting of machinery and equipment, base plates sole plates, precast panels, beams, columns and curtain walls.
- Grouting of railing posts, foundations, windmills, compressors, etc.
- For grouting rebar, bolts, dowels and pins, etc
- Applications where a non-shrink grout is needed for maximum effective bearing area to transfer optimum load.
Color: Gray powder
Mixing:
Add clean water to suitable mixing bucket. Mix slowly and continuously to form a homogeneous mixture
- VGROUT6 25kg barrel required approximately 4.0 litres of clean water
- VGROUT6 5kg barrel required approximately 0.8 litres of clean water
The mixed materials is immediately ready to use and should be used within 30-60 minutes after mixing.
The Ground Granulated Blast Furnace Slag (GGBS/GGBFS) is a type of eco-friendly green building material and high quality secondary cementitious material for concrete and cement. It is recognized as one of the best secondary cementations material for building high durable concrete stricture in the world today! GGBS has taken over a top place of high-performance cement and concrete mineral additives with its unique characteristics of hydration, low-price raw material. GGBS is obtained by quenching molten iron blast furnace slag (a by-product of iron and steel making) in water or steam. It is then further grounded into the desired fineness in terms of the required particle size distribution. The main components of blast furnace slag are CaO (30-50%), SiO2 (28-38%), Al2O3 (8-24%), and MgO (1-18%). The other important aspect of GGBS is its superiority in concrete durability which extends the lifespan of buildings from fifty years to a hundred years. APPLICATIONS Soil stabilization Mortar Used in combination with Portland cement Pre-cast concrete Ready mix concrete Specialist projects
Acid / Alkali Resistant Tiles/Bricks * Our Acid proof tiles, Acid alkali resistant tiles, Chemical resistant tiles are fully vitrified tiles which are manufactured using special non ferrous clay, processed at extremely high temperatures this process causes the raw materials to fuse and form a compact mass with an extremely low water absorption of less than 0.5% resulting in the formation of a very strong body with a flexural strength of 38 N/mm2, solid through color fade proof with a very hard surface Mohs hardness of 7. * The acid resistant tiles come in a range of sizes and thicknesses from ranging from 8-25mm. Our acid proof tiles meet stringent specification norms of IS 4457:2007 and relevant ASTM/DIN standards which ensure excellent performance in Acid/Alkali/Chemical (expect Hydrofluoric acid and its derivatives). Corrosion Protection Applications * Factory Floors subject to corrosion from Chemicals, Acids, Oil & Solvents * Pickling tank and surrounding areas * Food & Beverage Industry flooring * Battery rooms and Control rooms * Demineralization plants * Walls of washing and Paint shop areas * Acid Resistant Tiles Manufacturers India * Our acid proof tiles provide excellent abrasion resistance, anti-skid properties for worker safety and high aesthetic appeal. We also provide specialized corner tiles for reducing chances for acid attack through construction joints. Our standard sizes are 200x100, 200x200 & 300x300 millimeters.
Product: Buttweld Fittings Brand: Renaissance Pipe Fitting Inc. Sizes: Refer to the specification Condition: New Rating:4.4, based on 172 reviews price: Start from 15 USD Buttweld Fittings and socketweld Fittings in Stainless steel and seamless, Pipe Caps, ANSI B16.9 Fittings, carbon steel, ANSI B16.28 Fittings, Equal and reducing crosses, MSS-SP-43 Fittings, Equal and reducing tees, caps, Lap joint Stub End supplier. RFP India is exporters of butt weld fittings and prepares them in a range of designs as per the provisions of our customers. There are many types of fittings such as Seamless, Welded, Fabricated, and more with Stainless Steel Butt Weld Fittings, Duplex Steel Butt Weld Fittings, Aluminium Butt Weld Fittings, Titanium Butt Weld Fittings, Carbon Butt Weld Fittings, and so on. Made up of by using high standard quality material along with quite sophisticated and high machines, our variety of butt weld fittings is quite recognized for its zero-defects, superior performance, and high quality. These butt weld pipe fittings are made up of by using high standard quality stainless steel, making these fittings anti-corrosive, making them nonaligned, and as well as making them survive intense temperature conditions. Sourced from reliable vendors, these fittings are highly acknowledged for their high tensile strength, durability, and accurate alloy composition. We offer butt weld fittings in several types like elbow, tee, return bends, reducer, stub-ends, cap, cross, insert, collar, and more.
Our Bath Material goes beyond primary aluminum production, finding applications in aluminum scrap recycling and various industrial processes. Whether you're involved in glass, enamel, ceramics manufacturing, or other industries, our Bath Material proves to be a versatile and valuable resource. Explore the high-quality Bath Material solutions offered by Gremlog , providing excellence in electrolyte materials for diverse industrial application Discover the versatility of our cryolite offerings, available in a range of sizes tailored to meet diverse industry requirements. Our commitment to precision and customization ensures that our high-quality cryolite aligns seamlessly with the specific needs of your aluminum smelting processes, providing optimal performance and efficiency.Choose from our meticulously graded sizes, including : 0-5 mm; 5-20 mm; 20-40 mm; 0-40 mm; 5-40 mm;
Incoloy Alloy 902 is a high-strength, heat-resistant, and corrosion-resistant alloy material with excellent mechanical properties and oxidation resistance. It is an iron-based high-temperature alloy composed of elements such as chromium, nickel, molybdenum, copper, aluminum, titanium, and zirconium. The main features of Incoloy Alloy 902 include: Corrosion resistance: Incoloy Alloy 902 has strong corrosion resistance and can resist the corrosion of many strong acids, alkalis, and saltwater environments. Therefore, it is widely used in the chemical, marine, and petroleum industries. Oxidation resistance: Incoloy Alloy 902 has excellent oxidation resistance and can be used for a long time in high-temperature environments without failure. Therefore, it is widely used in equipment and devices operating in high-temperature oxidation environments. High-strength performance: Incoloy Alloy 902 has extremely high strength and hardness, can withstand high stress and high loads, and is therefore widely used in high-strength fields such as aerospace, nuclear industry, etc. Good machinability: Incoloy Alloy 902 has good machinability and can be formed and processed by various methods such as hot working and cold working, suitable for the manufacture of products in various shapes and specifications. In summary, Incoloy Alloy 902 is an excellent high-temperature alloy material with excellent corrosion resistance, oxidation resistance, and high-strength performance. It is widely used in the manufacture of equipment and devices operating in high-temperature, high-pressure, and corrosion-resistant environments. Incoloy alloy 902 is a nickel-iron-chromium alloy with additions of molybdenum and niobium. Here are some international standards and specifications for this alloy: American standards: AMS 5221, AMS 5223, AMS 5225, AMS 5226, AMS 5230, AMS 5231, AMS 5542, AMS 5676, AMS 5717, AMS 5718, AMS 5719, AMS 5738, AMS 5801, AMS 5803, AMS 5804, AMS 5806, AMS 5580, ASTM B366, ASTM B408, ASTM B564, ASTM B649, ASTM B670, ASME SB-366, ASME SB-408, ASME SB-564, ASME SB-649, ASME SB-670 European standards: EN 2.4665 German standards: DIN NiCr21Mo14W, DIN 2.4665 British standards: BS HR 202 Japanese standards: JIS NW 4990 We can provide the following the form:Incoloy alloy902 coil; Incoloy alloy902 strip;Incoloy alloy902 plate;Incoloy alloy902 sheets; Incoloy alloy 902 tube; Incoloy alloy 902 pipe;Incoloy alloy 902 flat; Incoloy alloy902 bar BS: HR 202/JIS:NW 4990/UNS:N09902/W.Nr:2.4665
Incoloy Alloy 908 is a high-temperature, high-strength, and highly corrosion-resistant alloy composed of elements such as nickel, chromium, molybdenum, and iron. It is a single-phase austenitic alloy, typically formed by casting and forging. Chemical composition: The chemical composition of Incoloy Alloy 908 is composed of elements such as nickel, chromium, iron, molybdenum, vanadium, manganese, tantalum, silicon, carbon, phosphorus, and sulfur. Nickel content is 40-45%, chromium content is 20-23%, iron content is 16-19%, and molybdenum content is 8-10%. Mechanical properties: Incoloy Alloy 908 has excellent high-temperature and high-strength performance. Its tensile strength is 135 ksi (930 MPa) (minimum), yield strength is 70 ksi (480 MPa) (minimum), and elongation is 25% (minimum). Physical properties: The density of Incoloy Alloy 908 is 8.14 g/cm�³, the melting point is 1338�°C (2440�°F), the thermal conductivity is 11.7 W/m�·K (100�°C), and the coefficient of thermal expansion is 13.7 �¼m/m-K (20-100�°C). Corrosion resistance: Incoloy Alloy 908 has excellent corrosion resistance, especially in high-temperature, high-pressure, and highly corrosive environments. It can withstand the corrosion of corrosive media such as sulfuric acid, hydrochloric acid, nitric acid, and fluoride, and can resist chloride stress corrosion cracking (SCC). The international standard designations for Incoloy alloy 908 include UNS N09908 and W.Nr. 1.4876. There are also corresponding standards and specifications in different countries and regions, such as AMS and ASTM standards in the United States, EN standards in Europe, and JIS and JPI standards in Japan. Here are the specific standards and designations for Incoloy alloy 908 in different countries: United States: AMS 5545, AMS 5546, AMS 5547, AMS 5549, ASTM B408, UNS N09908 Germany: DIN 17752, DIN 17753, DIN 17754, W.Nr. 1.4876 United Kingdom: BS HR 6 Europe: EN 10095 Japan: JIS H4551, JPI-SB46 We can provide the following the form:Incoloy alloy908 coil; Incoloy alloy908 strip;Incoloy alloy908 plate; Incoloy alloy908 sheets; Incoloy alloy908 tube; Incoloy alloy908 pipe;Incoloy alloy908 flat; Incoloy alloy908 bar GB:HR 6/JIS:H4551/UNS:N09908/W.Nr:1.4876
VN SEAL 109 is a liquid applied, crack bridging 2 pack acrylic polymer modified cementitious waterproofing coating system with moderate to high degree of elasticity depending on system buildup Advantages - Crack-bridging & Elastic - Good Impermeability against water ingress - Highly water resistant, arrest salt petre and prevent carbonation - Extremely good bonding with high abrasion resistance - Simple application and fast curing - It has excellent adhesion to concrete, brickwork and corrugated asbestos cement sheets Appication - Used as a seamless, impervious coating on flat roof for both exposed and concealed waterproof coating system - Basements - Water retaining structures - Underground concrete structures, pits, basins, sumps etc. - Used as waterproofing coating on concrete, screed, mortar, brick tiles, cement tiles, plaster or porous stone substrates Packaging 1) Part (A+B) : 28 kg ready to mix units x 2 sets Part A is grey power: 20kg/Barrel Part B is white milky liquid: 8kg/Barrel 2) Part (A+B) : 14 kg ready to mix units x 2 sets Part A is grey power: 10kg/Barrel Part B is white milky liquid: 4kg/Barrel Shelf life 12 months from the production date Storage conditions Keep in cool and dry places
VNSEAL 104W is a two component, white colour, flexible cementitious waterproofing membrane consisting of a synthetic resin mixed with a blend of selected cement and well-graded fillers. When mixed, VNSEAL 104W becomes a smoooth slurry and is easily applied by brush, roller or suitable spraying equipment. VNSEAL 104W can be applied onto damp substrates. The cured membrane is flexible, durable and weather resistant and has excellent adhesion to most building substrates. Its unique chemical structure provides a breathable membrane that is permeable to water vapour and yet impermeable to water. VNSEAL 104W is capable of bridging hairline cracks. Typical Uses: Waterproofing of Basement walls and lift pits Waterproofing of potable water tanks, waterproofing of reservoirs, culverts, storm drains, canal, water retaining and water excluding structures. Waterproofing of kitchens and toilets Waterproofing of balconies and planter boxes Waterproofing of swimming pools and water features Waterproofing to precast gable end walls Waterproofing to RC flat roof (re-roofing-exposed and concealed applications) and gutters. Waterproofing to external wall prior to installation of claddings. Advantages: Pre-packed Easy to mix and apply Excellent waterproofing qualities â?? able to withstand high hydrostatic pressure Excellent adhesion to concrete, masonry, ceramics, natural and artificial Flexible able to bridge hairline cracks up to 2mm Does not contain chloride or other corrosive salts which cause efflorescence Non toxic- suitable for use in waterproofing of potable water tanks Able to withstand light foot tracfficking Can be applied onto damp substrates Weathering resistant Mixing Instructions: Pour Part A (liquid) into Part B (White powder)container and mix with a slow speed mechanical mixer until homogenous and lump free. Allow the mix to stand for 5 minutes and re-stir manually before use. Application: For horizontal and vertical surfaces, a roller, brush or spray gun, may be used to apply the slurry. Care must be taken to ensure that air is not entrapped in the membrane Apply the first coat of VNSEAL 104W and allow it to dry. At the same time, ensure that all joints and corners are properly coated, preferable with a brush. Allow membrane to dry for approximately 2 hours before application of the second coat VNSEAL 104W the professionals choice of quality products and system for building construction Shelf life Expiry date 12 months from the production date Storage conditions Dry, cool, shaded place Packaging 1) Combo A: 4kg - B: 2kg Component A is White powder: 4kg/barrel Component B is milky white liquid: 2kg/plastic can 2) Combo A: 10kg - B: 5kg Component A is White powder: 10kg/barrel Component B is milky white liquid: 5kg/plastic can 3) Combo A: 20kg - B: 10kg Component A is White powder: 20kg/barrel Component B is milky white liquid: 10kg/plastic can
Offset Industries (we supply various grades as per customer requirement) via coater & duct application