Ganeshas Aim Industries Private Limited

PRODUCT DATA SHEET ACID RESISTANT BRICK Material : FIRECLAY Type Acid Resistant Brick Size (mm) : 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : * We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: * Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions - Heavy thermal shock Characteristic Fireclay Type Acid Resistant Brick - Test Standard Bulk Density, lbs/ft3 - 2.25 to 2.30 ASTM C-20 Water Absorption, % - 0.1 to 1.8 ASTM C-20 Apparent Porosity, % - 4.05 to 4.14 ASTM C-20 Acid Solubility (H2SO4), Loss in Mass,% - 6.1 to 6.8 ASTM C-279 Modulus of Rupture, Mpa - 14.6 ASTM C-67 Compressive Strength, PSI - 15500 to 17250 ASTM C-67 Abrasion Resistant , Volume in mm3 - 71 to 96 EN 102 Surface Hardness, MOHS Scale - 7 Thermal Conductivity, BTU-in/hr-ft-F - 6.94 to 7.12 ASTM C-236 Thermal Expansion Coefficient,in/in/Fx10-6 - 2.6 to 2.8 EN 103

PRODUCT DATA SHEET ACID RESISTANT BRICK Material : RED SHALE Type Acid Resistant Brick Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions Heavy thermal shock Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick Characteristic RED SHALE ACID RESISTANT BRICK Test Standard Bulk Density, gm/cc - 2.3 to 2.35 ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968 Apparent Porosity, % -0.5 to 1.75 S 4860 Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279 Modulus of Rupture, PSI -2133 to 3555 ASTM C-67 Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968 Abrasion Resistant , Volume in mm3 -69 to 85 EN 102 Surface Hardness, MOHS Scale - 7

Magnesia Bricks Description Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application. Magnesia Bricks Features: It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature. Magnesia Bricks Application Basic open-hearth furnace for steelmaking Electric furnace bottom and wall Permanent lining of oxygen converter Non-ferrous metal metallurgy furnace Hyperthermia tunnel kiln Lining of rotary cement kiln Heating furnace bottom and wall Regenerative chamber of glass furnace Magnesia Bricks Properties High Refractoriness Good alkaline slag erosion resistance High apparent initial softening temperature Good thermal conductivity High thermal expansion Magnesia Bricks Manufacturing Process Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.

Insulation Bricks

Refractory Fire Brick

Acid / Alkali Resistant Tiles/Bricks * Our Acid proof tiles, Acid alkali resistant tiles, Chemical resistant tiles are fully vitrified tiles which are manufactured using special non ferrous clay, processed at extremely high temperatures this process causes the raw materials to fuse and form a compact mass with an extremely low water absorption of less than 0.5% resulting in the formation of a very strong body with a flexural strength of 38 N/mm2, solid through color fade proof with a very hard surface Mohs hardness of 7. * The acid resistant tiles come in a range of sizes and thicknesses from ranging from 8-25mm. Our acid proof tiles meet stringent specification norms of IS 4457:2007 and relevant ASTM/DIN standards which ensure excellent performance in Acid/Alkali/Chemical (expect Hydrofluoric acid and its derivatives). Corrosion Protection Applications * Factory Floors subject to corrosion from Chemicals, Acids, Oil & Solvents * Pickling tank and surrounding areas * Food & Beverage Industry flooring * Battery rooms and Control rooms * Demineralization plants * Walls of washing and Paint shop areas * Acid Resistant Tiles Manufacturers India * Our acid proof tiles provide excellent abrasion resistance, anti-skid properties for worker safety and high aesthetic appeal. We also provide specialized corner tiles for reducing chances for acid attack through construction joints. Our standard sizes are 200x100, 200x200 & 300x300 millimeters.

APPLICATION OF SK-HB K-SILICATE MORTAR : * K-SILICATE is used for jointing Acid Resisting brick in construction of vessels in suited for construction of fume chambers and stacks handling hot, dry Acid fumes and vapors. It is also used for jointing chemical resisting stoneware pipes. K-SILICATE cement is good bedding material for Acid â?? Resisting bricks and tiles. The concrete surface needed protection should be dryed, clean and rough. The bricks or tiles will be set with K-SILICATE cement over concrete surface applied with a suitable an impermeable interliner. When Bedding and Jointing Materials are the same. On the treated surface bricks or tiles are bedded to a thickness of about 6 mm and tamp gently with a wooden piece till the paste squeezes out of joints. The paste that is squeezed out of the joint should be removed by trowel with good finishing. After the mortar of the joint is dryed treat the joints with 20% Hydrochloric Acid Solution by means of brush. A.R.lining should be always in contact with Acid and not with water. Concrete subtract like Floor, Wall, tanks and similar surface should be protected with a membrane of Bitrok Mastic or compound steel tanks should be protected with rubber or PVC subjected to chemical conditions and temperature of chemical media. The Brick lining is recommended over the protective layer of Bitrok Mastic. When Bedding and Jointing Materials are Different. Spread the silicate type mortar about 6 to 8 mm thick on the back of the tile or brick. Press the tile on the bed leaving required space for joints between tiles for bricks. After the bedding mortar is set, fill Mp the joints with specified cement.PRODUCT DATA SHEET FOR SK-HB ( K-SILICATE) MORTAR A general purpose cement for acid conditions Resistant to High & medium concentrations of most of the common organic and inorganic acids except Hydroflouric acid. Recommended where the concentration of the acid is high suitable for high temperature. Unsuited to aqueous solutions, alkaline conditions. PREPARATIONS OF MORTAR : * Measure 1 part by weight of K-SILICATE solution into a suitable mixing pan. * Add slowly and gradually 3 parts by weight K-SILICATE mortar and mix thoroughly to form a smooth mortar. * In hot season very large batches of mortar will become stiff quite rapidly therefore small batches, not exceeding 4 to 8 kgs. Will be prepared. * The cement mortar will be used before it starts setting.

This is chemical setting Furan based chemical resistant mortar which is combination of Liquid and Powder, when mixed in proper proportion from workable mortar which after setting and curing give of liquid and give black highly cross linked composites. Furan When set and cured is resistant to highly corrosive acids, alkalis and to powerful organic solvents such as ketones, Aromatic and Chlorinated solvents. It has extreme resistant to Acidic & alkalis, Salts, Greases and Detergents. It resists to Organic & Inorganic acids at their boiling temperature. It is suitable against mild chlorine Gas (dry) phosphorous trichloride, pyridine at room temperature. Furan is especially useful where resistance to mixed media such as aqueous acids /alkalis and organic solvents is needed in chemical plant process and waste streams. Carbon filled Furan is used against corrosive effect of hydrofluoric acid & its salts. PREPARATION OF FURANE MORTAR : Mortar consist of Furan solution and Furan powder. The average mixing ratio necessary to obtain mortar with good working consistency is 1 part by weight Solution & 3 part by weight powder. The ratio will vary slightly depending on temperature and working conditions.Stir the liquid thoroughly before using. Place liquid in a suitable shallow mixing pan. Add powder by weight in the solution mix thoroughly and rapidly until all lumps are dispersed and the mortar is completely homogenous. Spread out the mortar in a thin layer, not more than ¾ thick, to dissipate the heat of reaction and lengthen the working life. Batch size can be varied depending upon the temperature and the speed with which the masons are working. Very large batches will become stiff quite rapidly. Make sure that all the Furan Motrar is used from the pan before another batch is mixed.When working at temperature above 40 C, very small batches not more than 2 Kgs, should be prepared. When working at temperature below 15C the liquid should be kept warm.

* PHOSCAST Phoscast : Phosphate Bonded Castables * PURPOSE customers using FBC boilers (Particularly underbed feed FBC boilers) for the protection of inbed coils against erosion potential by applying highly abrasive resistant refractory on inbed coils above fuel feed system. BACKGROUND * Two of such actions are providing special alloy studs on inbed coils and applying highly abrasive resistant refractory on the outer bottom loops of inbed Coils which are above the fuel feed nozzles. * GANESHAS has taken number of approaches to identify the key factors affecting erosion rates with an objective to enhance the life of inbed tubes as well as implementing the corrective action to reduce the erosion rates. Phosphate coatings are often used to protect steel parts against rusting and other types of corrosion * Erosion of inbed coils in fluid bed combustor is unavoidable phenomenon however the rate of metal wastage and thus the life of tubes depends on various factors like ash & fuel properties, design of Combustor / feeding system, flue gas velocities operating conditions etc. It has been also observed that maximum erosion prone inbed coils are those which come above fuel feed nozzles and an area of approximately 1 to 1.5 mts around fuel feed systems are badly affected. APPLICATION Phoscast-90 XR can be applied by ramming with wooden mallet having adequately large head @" dia x 5" length x 10â?? Jong handle). The desired lining or repair thickness is built up in several courses while ramming the mass to uniform thickness. Phoscast refractory should never be trawled to obtain smooth surface; ramming only should finish surface. Any excess mass is to be sliced off with trowel edge and then finished by ramming again for bed coil. Tube application of AFBC boiler, the material pasty mass should be finger pressed into the studs of the tube with maximum force. Finish should be given by pressing the hand palm against material applied, using surgical type thin rubber hand gloves.