Corundum mullite poly light brick is a new type of energy efficient refractory material, can directly contact the flame, with high temperature, high thermal shock stability, high strength, small thermal conductivity and other characteristics. Widely used in ceramic roller kiln, shuttle kiln, cracking furnace, hot stove and a variety of electric furnace lining, door bricks, kiln tiles and so on. Characteristics 1.Low thermal conductivity, with a good thermal insulation effect 2.Low hot melt, due to low thermal conductivity, mullite series of light insulation brick accumulated little heat, in the intermittent operation of energy-saving effect is obvious 3.High purity,high refractoriness,and the high alumina content make it maintain good performance in a reducing atmosphere. 4.High thermal compressive strength 5. Extend the life of the lining 6.Could make in special shape to reduce the application amount of bricks. Al2O3 62 62 KO2+NaO20.10.08 Fe2O30.50.5 Bulk Density g/cm3 0.9 1.0 Cold Compressive Strength mpa 4.5 5.5 Refractoriness Under Load 1#1500 1500 Reheating liner change 15002h,0.1Mpa -1.5 -1 Refractorinessb 1700 1750
Supplier: Mullite corundum bricks
It is produced by foam coagulation technique. Features: 1. It has advantages with small bulk density, high cold crushing strength, and high refractoriness under load, small dimension tolerance and good thermal shock resistance. 2. It has the lowest and most stable thermal conductivity in various insulating refractory bricks. 3. It can reduce the total weight of furnace body and the thickness of furnace wall effectively, improve heat efficiency, lower energy consumption, improve work conditions and production efficiency, and considerable economic benefit can be obtained. Application: It is not only widely used in insulating layers of various of thermal processing equipments, such as hot blast furnace, coke oven, glass kiln, etc, but also apply to linings in parts of furnace without strong high-temperature molten material erosive. Item High Alumina Insulating LG-1.0 LG-0.9 LG-0.8 LG-0.7 LG-0.6 LG-0.5 LG-0.4 Al2O3 % 48 Fe2O3 % 2.0 Bulk Density g/cm3 1.0 0.9 0.8 0.7 0.6 0.5 0.4 Cold Crushing Strength Mpa 3.92 3.43 2.94 2.45 1.96 1.47 0.78 Thermal Conductivity Coefficient w/m.k 0.45 0.45 0.35 0.35 0.3 0.25 0.20 Test Temperature of Permanent Linear Change Rate 2% C 1400 1400 1400 1350 1350 1250 1250
Supplier: Fire clay brick, high alumina brick, mullite brick, corundum brick
Supplier: Zircon refractory brick, sintering zircon corundum brick, zircon mullite brick, sintered mullite refractory brick, high purity corundum refractory brick, corundum mullite brick, low creep corundum mullite brick, chrome zircon mullite brick, chrome zircon corundum brick, zircon brick
Supplier: Andalusite brick, cordierite mullite, corundum mullite brick, high alumina brick, clay brick, combined brick, 7/9/37 holes checker brick and castable series, ceramic fire-resistant ball
Services: Shipping
Mullite bricks refer to high-alumina refractories with mullite as the main crystalline phase, and the general alumina content is between 65% ~ 75%. It is mainly used for hot blast furnace top, blast furnace body and bottom, glass melting furnace regenerator, ceramic sintering kiln, petroleum cracking system dead angle furnace lining, etc. Mullite bricks have high refractoriness, up to more than 1790 C, and have good thermal shock resistance. There are two types: sintered mullite bricks and fused mullite bricks. The crystallization of fused mullite is larger than that of sintered mullite, and the thermal shock resistance is better than that of sintered products. Aluminum content: 65-90% Standard brick size: 230*115*65mm Compressive strength at room temperature: 100-120MPa Good thermal shock resistance:
Corundum brick (sintered corundum brick) with dense alumina clinker as raw material made of corundum brick. The brick has a high melting point, stable performance at high temperatures, room temperature and high temperature mechanical strength and wear resistance is good. Anti-metal erosion and anti-oxidation, superior performance. z
Mullite lightweight brick It was made of mullite and other fine raw refractory materials with advanced techniques. It is a kind of new popular energy-saving material widely used in metallurgy, ceramics, glass and chemical industry, glass and chemical industry as high temperature liner, such as in pyrolyzers, chemical industry furnace, metallurgy industry furnace, heating furnace, electric resistance furnace, roller kiln, tunnel kiln and shuttle kiln.