Corundum brick (sintered corundum brick) with dense alumina clinker as raw material made of corundum brick. The brick has a high melting point, stable performance at high temperatures, room temperature and high temperature mechanical strength and wear resistance is good. Anti-metal erosion and anti-oxidation, superior performance.
z
Copper Smelting furnace use High Alumina Corundum Fire Brick have stable quality and excellent durability.Copper Smelting furnace use High Alumina Corundum Fire Brick are made mainly of calcined alumina, mullite, corundum of high purity.Copper Smelting furnace use High Alumina Corundum Fire Brick have low porosity, excellent hot strength and creep resistance, and good volume stability at high temperature, Copper Smelting furnace use High Alumina Corundum Fire Brick have been developed to meet the most demanding specifications for various industrial applications. Brand Properties HT-98 HT-95 HT-90 HT-85 Chemical Composition (%) Al2O3% 98.5 95 90 85 SiO2% 0.3 3.0 9.0 13 Fe2O3% 0.2 0.2 0.5 0.5 Apparent Porosity (%) 18 18 18 20 Bulk Density (g/cm3) 3.1 2.95 2.9 2.75 Cold Crushing Strength (MPa) 90 80 80 70 Refractoriness Under Load (�ºC) 1700 1650 1650 1700 Permanent Linear Change (%) 0.1 0.2 0.2 0.3 Main Applications Carbon reactor furnace Pertrochemical furnace Industry ceramic kiln Refractory tunnel kiln Various high-temp Furnace Copper Smelting furnace use High Alumina Corundum Fire Brick 1.High refractoriness, 2.High-temperature endurable. 3.Good corrosion resistance. 4.Good spalling resistance and wear resistance. 5.Good thermal shock resistance. 6.High mechanical strength. 7.High-temperature creep rate is low. 8.Good volume stability at high temperature.
Corundum brick and chrome corundum brick is the petrochemical industry gas furnace and the furnace key refractory lining material. Corundum brick is α-Al2O3 as the main component of the special refractory material, has been widely used in high temperature, high pressure, chemical erosion and mechanical wear serious ammonia gasification furnace, ethylene engineering gas furnace, carbon black reactor and other important petrochemical heat The lining of the device. Chromium corundum brick is pure Al2O3 and Cr2O3 as the main raw material synthesis, compared with pure corundum brick, it has better performance, such as refractoriness, load softening deformation temperature, bending strength, high temperature creep, high temperature volumetric stability And resistance to slag corrosion.
Corundum brick and chrome corundum brick is the petrochemical industry gas furnace and the furnace key refractory lining material. Corundum brick is α-Al2O3 as the main component of the special refractory material, has been widely used in high temperature, high pressure, chemical erosion and mechanical wear serious ammonia gasification furnace, ethylene engineering gas furnace, carbon black reactor and other important petrochemical heat The lining of the device. Chromium corundum brick is pure Al2O3 and Cr2O3 as the main raw material synthesis, compared with pure corundum brick, it has better performance, such as refractoriness, load softening deformation temperature, bending strength, high temperature creep, high temperature volumetric stability And resistance to slag corrosion.
Corundum mullite poly light brick is a new type of energy efficient refractory material, can directly contact the flame, with high temperature, high thermal shock stability, high strength, small thermal conductivity and other characteristics. Widely used in ceramic roller kiln, shuttle kiln, cracking furnace, hot stove and a variety of electric furnace lining, door bricks, kiln tiles and so on. Characteristics 1.Low thermal conductivity, with a good thermal insulation effect 2.Low hot melt, due to low thermal conductivity, mullite series of light insulation brick accumulated little heat, in the intermittent operation of energy-saving effect is obvious 3.High purity,high refractoriness,and the high alumina content make it maintain good performance in a reducing atmosphere. 4.High thermal compressive strength 5. Extend the life of the lining 6.Could make in special shape to reduce the application amount of bricks. Al2O3 62 62 KO2+NaO20.10.08 Fe2O30.50.5 Bulk Density g/cm3 0.9 1.0 Cold Compressive Strength mpa 4.5 5.5 Refractoriness Under Load 1#1500 1500 Reheating liner change 15002h,0.1Mpa -1.5 -1 Refractorinessb 1700 1750
It is produced by foam coagulation technique. Features: 1. It has advantages with small bulk density, high cold crushing strength, and high refractoriness under load, small dimension tolerance and good thermal shock resistance. 2. It has the lowest and most stable thermal conductivity in various insulating refractory bricks. 3. It can reduce the total weight of furnace body and the thickness of furnace wall effectively, improve heat efficiency, lower energy consumption, improve work conditions and production efficiency, and considerable economic benefit can be obtained. Application: It is not only widely used in insulating layers of various of thermal processing equipments, such as hot blast furnace, coke oven, glass kiln, etc, but also apply to linings in parts of furnace without strong high-temperature molten material erosive. Item High Alumina Insulating LG-1.0 LG-0.9 LG-0.8 LG-0.7 LG-0.6 LG-0.5 LG-0.4 Al2O3 % 48 Fe2O3 % 2.0 Bulk Density g/cm3 1.0 0.9 0.8 0.7 0.6 0.5 0.4 Cold Crushing Strength Mpa 3.92 3.43 2.94 2.45 1.96 1.47 0.78 Thermal Conductivity Coefficient w/m.k 0.45 0.45 0.35 0.35 0.3 0.25 0.20 Test Temperature of Permanent Linear Change Rate 2% C 1400 1400 1400 1350 1350 1250 1250
High alumina firebricks are classified according to the alumina content which is from lowest 48% to highest 95%, manufactured from mineral of bauxite, corundum, etc. By mixing, press-forming, drying, sintering and machining. High alumina bricks feature stable mechanical strength and thermal shock resistance, with high refractoriness of no lower than 1880¡æ, high alumina bricks are commonly used as refractory lining exposed to heat directly or backup insulation linings in various types of industrial kiln or laboratory furnace. Wooden pallets
Fused cast azs block has strong glass corrosion resistance and high thermal shack stability. The products are adopting superior material, with process by special arc furnace forming it. This fuse cast technology got nearly no suffers from electrode pollution. Application Can be used at parts where chemical erosion is serious and temperature changes frequently, such as fire spurting mouth and regenerator joints, end port of furnace etc Wooden pallets
Silica bricks are the main species of silica-based refractories, where the mass fraction of SiO2 is not less than 93%. Silica brick is a typical acid refractory bricks, the acid slag has a good resistance to Al2O3, FeO, Fe2O3 and other oxides also has good resistance, but the resistance to alkaline slag is poor, easy to CaO, K2O, Na2O and other oxides and damage. Features: 1.Good acid and erosion resistance, powerful anti high-temperature strength. 2.Soften melting temperature is 1620~1670 °C. 3.Low thermal shock resistance. 4.Natural silica as raw material, plus regular mineralizer. 5.Ensure good bonding and structural strength of furnace. 6.Good heat resistance and long service life. Application: 1.Glass melting furnace, ceramic frit kiln, sodium silicate furnace, soaking furnace, ceramic kiln, etc 2.Coke oven's coking chamber, combustion chamber walls, steel open-hearth's regenerator and sediment chamber, etc. 3.Load-bearing parts of high temperature hot air furnace and acid open-hearth furnace roof, etc. Items Fire Proof Thermal Insulating SiC+SiO2,% 30 - Al2O3,% 65 50 Bulk Density,g/cm3 2.65 - Apparent Porosity,% 19 25 Cold Compressive Strength,Mpa 90 40 Refractoriness UnderLoad, ºC 1650 1680 ThermalShock Resistance,cycles(1100 ºC,water cooling) 20 20 Thermal Conductivity,w/m.k(350 ºC) 2.5 1.4
High Alumina Brick, RefractoryHigh Alumina Brick, High Alumina Fire Brick for Blast Furnace Low creep high alumina brick for blast furnace is made of corundum, mullite "sillimanite, andalusite and kyanite" and high quality bauxite clinker as raw material by shaping at high pressure and sintering at high temperature. Characteristic: 1.The content of AL2O3 is 48%. 2.High refractoriness. The temperature is up to 1750~1790�ºC, it belongs to High-duty Refractory. 3.High refractoriness under load. The URL is higher than fireclay brick as the high content of Al2O3, however, it is lower than silica brick because of mullite crystal does not form reticular tissue. 4.Excellent slag resistance. High alumina brick is a kind of neutral refractory material so it enjoys excellent resistance to acid slag and alkali slag corrosion. Application: The main markets for low creep high alumina brick are building lining of hot-blast stove, blast furnace, coke oven, rotary kilns of cement and so on. High Alumina Brickis made fromhigh grade bauxite,it has the advantage of high refractoriness under load,long service time,good thermalinsulation performance andso on