Toroidal magnetic cores are made of a Fe-based thin (20 microns) nanocrystalline ribbon and have low loss, high induction of saturation, high operating temperature (up to 150 C), high magnetic permeability. Magnetic cores have a negative temperature coefficient of losses that provides stabilization mode transformer temperature.
Application in power high- frequency transformers push-pull,bicyclic SMPS, DC-DC converters, audiotransformers.
High permeability provides good electromagnetic connection of windings and low leakage inductance values.
HIGHLIGHTS OF THE MATERIAL:
Induction amplitude, Bm (25 C) 1,2 T
Induction amplitude, Bm (90 C) 1,1 T
Curie temperature, Tc 570 C
Magnetostriction less than 0,5 x10 ^ -6
Magnetic Permeability (100 kHz) - up to 20,000
Co-based amorphous core in plastic container
1. high permeability
2.Thickness (1820 mkm)
3. Annealing in transverse field, permeability more than 100000, very low loss, flat hysteresis loop
4. Common-mode filter chokes, current transformers, including for precise electronic electricity meters, protective cutout, High Frequency power transformers in SMPS, audio transformers, etc.
5.D from 4-32mm
Ribbon wound magnetic core is placed into hard protective container of glass-polyamide and mechanically fixed with silicone sealant.
Co-based amorphous ribbon wound magnetic core is placed into hard protective container of glass-polyamide and mechanically fixed with silicone sealant.Size veries:outer D =4-32mm.The container has rounded edges and is designed for direct winding of a thick wire. The container provides reliable mechanical protection and preservation of amorphous material's properties. All materials comply with UL94V-1 / 0.
1. High permeability
2.Thickness (1820 mkm)
3. Annealing in transverse field, permeability more than 100000, very low loss, flat hysteresis loop
4. KEY FEATURES OF THE AMORPHOUS MATERIAL:
Induction amplitude, Bm (25C) 0.59 T
Induction amplitude, Bm (90C) 0.50 T
Curie temperature, Tc 220C
Operating temperature range -60C ... 100C
Magnetostriction less than 0.110^-6
Typical permeability (10 kHz) - 120 000
Typical permeability (100 kHz) - 35 000
Co-based amorphous core in plastic container
1. high permeability
2.Thickness (18-20 mkm)
3. Annealing in transverse field, permeability more than 100000, very low loss, flat hysteresis loop
4. Application: Common-mode filter chokes, current transformers, including for precise electronic electricity meters, protective cutout, High Frequency power transformers in SMPS, audio transformers, etc.
KEY FEATURES OF THE AMORPHOUS MATERIAL:
Induction amplitude, Bm(25C) 0.62 T
Induction amplitude, Bm(90C) 0.54 T
Squareness ratio Br/Bm (@ 100 kHz, 80 A/m) at least 0.90
Dry-type transformer.Power range is:100-20000-30000 kVA.
Durable to instantenous temperature changes and also to short-circuit.
100% protected from moisture.It cant get fired has an ability to extinguish the fire.
Does not contain any Halogen or Nitrogen.Price changes due to power range.