It is calcined by asphalt coke and sponge coke in the 1350ºC calcined kiln,which is obtained the lower volatile matter products. Widely used in chemical smelting, mechanical casting, petroleum exploration and other industries.
    Spe
Grad
F.C(%) Ash(%) Moisture(%) V.M(%)
S(%)
N(ppm)
Size
CPC 98min 0.5max 0.5max 0.7max 0.7max 1000-2000max .
As clients' demands.
CPC 98min 0.5max 0.5max 0.7max 0.5max 1000-2000max
CPC 98min 0.5max 0.5max 0.7max 0.1max 1000-2000max
Packing .
As clients' demands.
It is made from low sulfur and low nitrogen petroleum coke by 2,500-3,500ºC temperature graphite annealing. As a high-purity carbon material, it has characteristics of high fixed carbon content, low sulfur, low ash, low resitance etc. It can be used as carbon raiser (Recarburizer) to produce high quality steel, cast iron and alloy.
    Spe
Grad
F.C(%) Ash(%) Moisture(%) V.M(%)
S(%)
N(ppm)
Size
GPC 98.5min 0.5max 0.5max 0.5max 0.05max 300max .
As clients' demands.
Packing .
As clients' demands.
F.C:98%Min Ash:0.3%Max V.M:0.5%Max S:0.05%Max Moisture:1.0%Max
Graphite petroleum coke-GPC: is made from low sulfur and low nitrogen petroleum coke by 2500-3500°C temperature graphite annealing.As a highpurity carbon material, it has characteristics of high fixed carbon content,low ash,low sulfur,low resitance etc. GPC can be used as carbon raiser (Recarburizer) to produce high quality steel,cast iron and alloy.
1.Mainly used in steelmaking in electrical stove, screening water, shipbuilding sandblast to remove rust.
2.Can reduce the cost of steelmaking effectively by replacing the traditional petroleum coke of carburant.
3.Used for steel making,can improve the Carbon content in steel-melting and Ductile iron foundry.
ackaging Details: water-proof plastic woven bag, 1000kg per bag or as your requirements.
Delivery Time: Within 20 days after receipt of prepayment.
Remark: Chemical composition and size can be optimized by the customers' requirements.
Usage:
Graphite petroleum coke can be widely used as carbon raiser (Recarburizer) to produce high quality steel, cast iron and alloy.Excellent performance and stability. Proper carburizing agents can help reduce the cost of smelting and improve the quality of smelting metals and castings.
Fixed Carbon 98.5% S0.5% Ash Content 0.5 Volatile Matter0.5% Moisture0.3
Size:0-0.3mm;0.3-1mm;0-1mm;0-3mm;1-3mm;1-5mm;3-5mm;3-20mm;20-50mm;50mm
size can be optimized by the customers' requirements.
1MT per bag, or can be pack on your requirements
Delivery Details:10-30 days after order:
Accepted Delivery Terms:FOB
Accepted Payment Currency:USD, EUR,CNY
Accepted Payment Type:T/T
Nearest Port:Tianjin port
Usage:
Graphite petroleum coke can be widely used as carbon raiser (Recarburizer) to produce high quality steel, cast iron and alloy.Excellent performance and stability. Proper carburizing agents can help reduce the cost of smelting and improve the quality of smelting metals and castings.
Semi-coke is light black; characterized by high fixed carbon, high specific resistance, high chemical activity, low ash content,
low sulfur and Low phosphorus; wildly applied to such industries as chemical industry, metallurgic industry, gas-making
industry, etc.; used to produce Calcium Carbide,Ferrosilicon, FerroNickel,Silicon Carbide, Silico Manganese, Fertilizer, etc
1.Advantage of semi coke than Met Coke in production of Ferro-alloy smelting as deoxidizer
Price is cheaper than Met Coke
High fixed carbon (84% max)
Low ash (9% max)
Low Phosphorus (0.03% max)
Low Sulfur (0.4%max)
High specific resistance
High chemical activity
High conductivity to lower the electric power
Type Chemical Composition(%)
F.C. Sulphur Ash V.M. Moisture
SQA-GPC-98.5 98.5 0.05 0.7 0.8 0.5
Size: 0.2-1mm, 1-5mm, 3-8mm, 5-10mm, 10-25mm Or according to customer's requirements
Packing: 1MT bags Or 25kg bags Or according to customer's requirements
Supply Ability: 1000MT per month
A-----Semi coke lump:used in ferroalloy industry such as FeSi ,FeNi,and Calcium Carbide .
F.C 83%min
Ash 9%max
V.M 8%max
S 0.4%max
P 0.01-0.03%
Size : 6-18 mm 15-35 mm 90%min
Moisture 15%max
B -----Semi coke Powder used for sinter plant , blast furnace and steel manufacturing.
F.C 76%min
Ash 12%max
V.M 12%max
S 0.4%max
P 0.03-0.05%max
Size 0-6 mm 90%min
Moisture 15%max
Shipping: By sea
Packaging:
1.Bulk in container MOQ: 200 MT
2.Bulk in vessel MOQ: 5000 MT
Payment: T/T L/C
Port: Tianjin, Rizhao, Qingdao, Dongjiakou, Jingtang
Product indication:
Fc:>86.5%
S:<0.6%
Ash:<12.5%
V.M:<1.5%
Moisture:<5%
Size: 30-80mm
Used for iron manufacture, steelmaking, non-ferrous metals smelting so on.
Both blast furnace coke and foundry coke are made by baking a blend of selected coking coals in certain high temperature without contact with air until almost all of the volatile matter is driven off. The resulting product, coke, consists principally of carbon, as listed in above table. By-products are crude coal tar, light oils, and ammonia, etc.
Generally speaking, chemistry, size, and strength have been considered the most important properties for use in the blast furnace. Other important factors are coke reactivity and csr (coke strength after reactivity), which deal with the amount and size of pores and walls, porosity, and density. Carbon textures and microstructure are two main factors that affect the reactivity, stability, and the coke strength after reaction.