Electronic Potting Silicone Rubber

Product Feature of Electronic Potting Silicone Rubber HY-9055 silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)PP ABS PVC, etc. and metal materials. 2. Typical Application of Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. 3. Technical Guidelines of of Electronic Potting Silicone Rubber a, Pls put part A and part B in separate container and stir evenly before mixing the two part together. b, Mixing Ratio: part A: part B = 1:1 c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring. Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80?100?, the silicone will cure in 15 minutes; while in 25? room temperature, the silicone will cure around 8 hours.

electronic potting silicon Rubber Characteristics 1. No toxicity, solventless, no odor or cure by-product. 2.No significant exotherm or shrinkage during curing. 3.Flexible curing schedule, can be cured at room temperature (R.T.) or at elevated temperature. 4.Very stable to changes of temperature, stability over wide temperature range (-50 to 200 C). 5.Good thermal conductivity. 6.Excellent dielectric properties for maintaining and protection of existing electrical insulation requirements. 7.Excellent weather resistance and waterproof property for protection from moisture and dust contamination. 8.Relative easier removal benefits to repair of electrical/electronic devices 9.Green environmental protection. Applicationof electronic potting silicon Rubber - high powered electronics - LED, LCD electronic display - circuit board - PCB substrate,etc - Precision Electronic Components, - DC/DC module and circuit board protection which requires high transparency and recovery. electronic potting silicon Rubber Warm Tips 1. The electronic potting silicon rubber should be sealed storage.The mixture should be used up at once, avoid causing waste. 2. The electronic potting silicon rubber belongs to non-dangerous goods, but keep away from mouth and eyes. 3. When electronic potting silicon rubber gets stratified after a period of storage, Please mix the electronic potting silicon rubber evenly before using, it does not affect the performance

Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã??PPã??ABSã??PVC, etc. and metal materials. 2. Typical Application of Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.

Electronic potting compound silicone Technical guidelines of electronic potting silicon rubber 1, please put part a and part b in separate container and stir evenly before mixing the two part together. 2, weight ratio: part a: part b = 1:1 3, deaeration the mixture under 0.08 m pa for 3 minutes. 4, the temperature influences the curing time of 9355 electronic potting silicon rubber. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. Warm tips of electronic potting silicon rubber: 1.The following material may hinder the curing of the product.So please apply after summary experiment. When necessary, please clean the application areas. Condensation silicone which not completely cured or organic tin compounds Sulfur, sulfide and sulfur rubber materials. Amine compounds as well as contains the amine materials. Pewters solder flux. 2. Should be sealed storage.The mixture should be used up at once, avoid causing waste. 3. Electronic potting silicon rubber belongs to non-dangerous goods, but keep away from mouth and eyes. 4. When electronic potting silicon rubber gets stratified after a period of storage, please mix 9301 evenly before using, it does not affect the performance. 20kgs/drum, 25kgs/drum, 200kgs/drum

Addition cure Electronic Potting Silicone Rubber 1. Product Feature of Addition cure Electronic Potting Silicone Rubber Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã?�PPã?�ABSã?�PVC, etc. and metal materials. 2. Typical Application of Addition cure Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. 3. Technical Guidelines of of Addition cure Electronic Potting Silicone Rubber a, Pls put part A and part B in separate container and stir evenly before mixing the two part together. b, Mixing Ratio: part A: part B = 1:1 c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring. 4.Notes of Addition cure Electronic Potting Silicone Rubber a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas. Organotin compound or Condensation silicone with organotin Sulphur, sulfide and sulfur rubber materials. Amine compounds as well as contains the amine materials. Pewters solder flux b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste. c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes. d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance. PACKAGE 40Kg/pail as a set (Part A 20Kg + Part B 20Kg) SHELF LIFE AND TRANSPORTATION 1. Twelve(12) months when stored at 24C in tightly closed original packages. 2. This kind of product is non-dangerous product, which could be transported as general chemicals. 3. Storage beyond the expired date doesnot necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons. -

Black color pcb electronic potting silicone hy-215   Technical parameters for pcb electronic potting silicone Properties indexPart aPart b Before curingAppearenceBlack fluidColorless / yellowish fluid Viscosisty (cps)2500±500- Features when operationMixing ratio ( by weight)10:1 Operating time (25c /min)20~30 Curing time ( hr, basically cured)3 Curing time ( hr, perfectly cured)24 Hardness(shore a)15+/-3   After curingThermal conductivity[w( m·k)]=0.4 Dielectric strength( kv/mm)=25 Dielectric permittivity(1.2mhz)3.0~3.3 Volume resistivity(o·cm)=1.0×1016 Fire resistance94-v1    (pls note all data of  pcb electronic potting silicone rubber with black color above is in 25c with 55% humidity conditions. We don't guarantee a same date if testing under different conditions, or when data was regenerated).   Warm tips for for pcb electronic potting silicone  1. Sealing pakage for storage. The mixture should be used up at once to avoid wasting.  2. Silicone belongs to non-dangerous goods, but keep away form mouth and eyes.  3. When it gets stratified after a period of storage, please mix hy-210# evenly before using,       it does not affect the performance.     Shelf life and transportation 1. Twelve(12) months when stored at 25c in original unopened packages. 2. This is a non-dangerous product, it can be transported as general chemicals. 3. Products exceed the storage life should be confirmed normal before using.

Product specifications : silicon rubber band Rubber band, 1x1mm, dia 4.5cm, 100g, cmc-red Rubber band, 1x1mm, dia 7cm, 400g, cmc-red Rubber band, 1x3mm, dia12cm, 100g, cmc-amber Rubber band, 1x8mm, dia12cm, 100g, cmc-amber Quantity required : initially 10000 pieces Shipping term : fob

Addition cure silicon rubber for artificial stone products pplications: It mainly use for making molds for resin, stone, gypsum and cement product with medium size. Addition cure silicon rubber for artificial stone products Typical Datasheet : Item No Color Hardness (A°) Viscosity (CS) Tensile-strength( kgf /cm2 ) Tear-strength (kgf /cm2) Elongation-break(%) Mixing Ratio of silicone and catalyst Application(most for resin, stone, gypsum and cement product to make moulds) HY-E635 Translucent 35±2 8000±2000 =60 =13 =400 1:1 Addition cure silicon rubber for artificial stone products Points of attention: 1,Prone to poisoning, can not mix with condensation, ionic compounds containing N, S-, P, organic matter and of Sn, As, Hg, Ph., easy molding plastic poisoning, resulting in the phenomenon of not curing. 2,Comparing with Condensation cure silicone, Addition cure silicone's adhesive properties to be worse. 3,Addition cure silicone affect by temperature greatly when cured under room temperature. 4,Addition cure silicone is easy to poisoning, please clean the tools which are used for condensation silicone rubber, so that it can avoid poisoning. It’s fobidden to add the pigment or powder to addition cure silicone rubber arbitrarily,it’s easy to make the catalyst to be poisoning. 5,Addition cure silicone rubebr has two-component, the component A and component B, please pay attention to clean the component A containers before using for the component B, and vice versa 6,In order to avoid the hardness change, we should mix the component A and component B according to its mixing ratio strictly, no atter it’s 1 : 1 or 10 : 1.

Molding hardness : 30 & 70 Origin - guangdong, china (mainland) Quantity required : 150 ton Shipping terms : cnf Destination port : iran Payment terms : l/c