Black color pcb electronic potting silicone hy-215
Technical parameters for pcb electronic potting silicone
Properties indexPart aPart b
Before curingAppearenceBlack fluidColorless / yellowish fluid
Viscosisty (cps)2500±500-
Features when operationMixing ratio ( by weight)10:1
Operating time (25c /min)20~30
Curing time ( hr, basically cured)3
Curing time ( hr, perfectly cured)24
Hardness(shore a)15+/-3
After curingThermal conductivity[w( m·k)]=0.4
Dielectric strength( kv/mm)=25
Dielectric permittivity(1.2mhz)3.0~3.3
Volume resistivity(o·cm)=1.0×1016
Fire resistance94-v1
(pls note all data of pcb electronic potting silicone rubber with black color above is in 25c with 55% humidity conditions. We don't guarantee a same date if testing under different conditions, or when data was regenerated).
Warm tips for for pcb electronic potting silicone
1. Sealing pakage for storage. The mixture should be used up at once to avoid wasting.
2. Silicone belongs to non-dangerous goods, but keep away form mouth and eyes.
3. When it gets stratified after a period of storage, please mix hy-210# evenly before using,
it does not affect the performance.
Shelf life and transportation
1. Twelve(12) months when stored at 25c in original unopened packages.
2. This is a non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
We offer superior quality sponge iron that is also known as direct- reduced iron. Our offered sponge iron is made for high grade, 65-70 fe Min fem-80%, fet-90-92%, s-0.04% max. Loose in form of lumps. Sponge iron filter material In industry through a sponge iron production equipment is widely applied iron phosphorus reduction method, method of reduction of iron ore concentrate, etc., the rolling iron phosphorus or ore concentrate after reduced iron press down into pieces, into the roasting tube into the kiln roasting, produce the high quality reduced iron. Sponge iron filter material for the first time into the deaerator, must first after backwashing, remove the sponge iron residue on the surface of the filter material float ash impurities.
Supplier: Remelted zinc ingots, pwg zinc ingots, zinc dross, zinc ash, zinc oxide, lead dross, magnesium ingots, all grades, silicon metal, lead ore/ concentrate, zinc concentrate/sulphide
Buyer: Zinc dross, zinc ash or skimming from hot dip galvanizing process, zinc fines, zinc die cast scraps, lead dross, brass and copper scraps
We are a leading supplier of electroplating chemicals, industrial polishing and welding consumables, water treatment, powder coating, fertilizers. We stock and carry an extensive range of ready to use chemicals. We deal with so many different chemicals and we would like you to contact us for more information about our different chemicals and products.