Addition cure Electronic Potting Silicone Rubber
1. Product Feature of Addition cure Electronic Potting Silicone Rubber
Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã?�PPã?�ABSã?�PVC, etc. and metal materials.
2. Typical Application of Addition cure Electronic Potting Silicone Rubber
HY-9055 electronic potting silicone rubber could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
3. Technical Guidelines of of Addition cure Electronic Potting Silicone Rubber
a, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
b, Mixing Ratio: part A: part B = 1:1
c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4.Notes of Addition cure Electronic Potting Silicone Rubber
a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux
b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.
PACKAGE
40Kg/pail as a set (Part A 20Kg + Part B 20Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months when stored at 24C in tightly closed original packages.
2. This kind of product is non-dangerous product, which could be transported as general chemicals.
3. Storage beyond the expired date doesnot necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
-
We are supplier and exporter of Ferro Silicon. Ferro silicon Specs: Si:75%min. and Si:72%min. C:0.2%max. S:0.02%max. P:0.04%max. Al:2.0%max.1.5%max.and 1.0%max .Commodity: Ferro Silicon Low Al Specs: Si:75%min. C:0.2%max. S:0.02%max. P:0.04%max.Al:0.1%max.0.3%max.and0.5%max. In 1mt plastic woven bags. Ferro Silicon Ferro Silicon has a melting point of 1200�¯�¿�½?�?�°C to 1250�¯�¿�½?�?�°C with a boiling point of 2355�¯�¿�½?�?�°C and Ferro Silicon contains about 2% of calcium and alluminium. Ferro Silicon, as an additive to the production process of ferrous metals, will impart several desirable properties upon the resultant alloy. Some of the primary benefits of adding Ferro Silicon to an alloy is to improve the corrosion resistant properties of the new compound, as well as to add to the high temperature heat- resistance properties of the new alloy, for example, in the production of silicon steel for use in transformer cores.
We are exporter of Ferro Silicon. FerroChrome is a kind of Ferro alloy which is formed by Ferro and Chrome,it is an important alloy addition in steel making. Ferrochrome (Fe Cr) is an alloy of chromium and containing between 50% and 70% chromium.
Silicon metal #3303 Si:99.0%min. Fe:0.3%max. Al:0.3%max. Ca:0.03%max. Size:10-100mm,90%min. In plastic woven bags of 1 mt each. Ferro silicon, ferro silicon powder, ferro silicon briquette.
We offer superior quality sponge iron that is also known as direct- reduced iron. Our offered sponge iron is made for high grade, 65-70 fe Min fem-80%, fet-90-92%, s-0.04% max. Loose in form of lumps. Sponge iron filter material In industry through a sponge iron production equipment is widely applied iron phosphorus reduction method, method of reduction of iron ore concentrate, etc., the rolling iron phosphorus or ore concentrate after reduced iron press down into pieces, into the roasting tube into the kiln roasting, produce the high quality reduced iron. Sponge iron filter material for the first time into the deaerator, must first after backwashing, remove the sponge iron residue on the surface of the filter material float ash impurities.
Supplier: Remelted zinc ingots, pwg zinc ingots, zinc dross, zinc ash, zinc oxide, lead dross, magnesium ingots, all grades, silicon metal, lead ore/ concentrate, zinc concentrate/sulphide
Buyer: Zinc dross, zinc ash or skimming from hot dip galvanizing process, zinc fines, zinc die cast scraps, lead dross, brass and copper scraps
Addition cure silicon rubber for artificial stone products pplications: It mainly use for making molds for resin, stone, gypsum and cement product with medium size. Addition cure silicon rubber for artificial stone products Typical Datasheet : Item No Color Hardness (A°) Viscosity (CS) Tensile-strength( kgf /cm2 ) Tear-strength (kgf /cm2) Elongation-break(%) Mixing Ratio of silicone and catalyst Application(most for resin, stone, gypsum and cement product to make moulds) HY-E635 Translucent 35±2 8000±2000 =60 =13 =400 1:1 Addition cure silicon rubber for artificial stone products Points of attention: 1,Prone to poisoning, can not mix with condensation, ionic compounds containing N, S-, P, organic matter and of Sn, As, Hg, Ph., easy molding plastic poisoning, resulting in the phenomenon of not curing. 2,Comparing with Condensation cure silicone, Addition cure silicone's adhesive properties to be worse. 3,Addition cure silicone affect by temperature greatly when cured under room temperature. 4,Addition cure silicone is easy to poisoning, please clean the tools which are used for condensation silicone rubber, so that it can avoid poisoning. It’s fobidden to add the pigment or powder to addition cure silicone rubber arbitrarily,it’s easy to make the catalyst to be poisoning. 5,Addition cure silicone rubebr has two-component, the component A and component B, please pay attention to clean the component A containers before using for the component B, and vice versa 6,In order to avoid the hardness change, we should mix the component A and component B according to its mixing ratio strictly, no atter it’s 1 : 1 or 10 : 1.
Addition cure silicone can be used for cake, candy food grade products mold making, addition cure silicone features low shrinkage.(features for low viscotity , good operation. Excellent performance. 25kg/drum and 200kg/drum
Supplier: 1. soya meal gmo & non gmo. 2. canadian wheat 3. canadian red lentil 4. canadian green peas. 5. red seats oil. 6. soya oil. 7. non gmo granular fine white sugar icumsa 45 8 urea fertilizer, sulphur 9. ethanol 10 . degummed soya crude oil, non gmo yellow corn, canadian premium quality all purpose white flour 11. canadian canola seed, canola oil, canola meal all shipment able to proceed, under 100% lc at sight condition
We are a leading supplier of electroplating chemicals, industrial polishing and welding consumables, water treatment, powder coating, fertilizers. We stock and carry an extensive range of ready to use chemicals. We deal with so many different chemicals and we would like you to contact us for more information about our different chemicals and products.