Poly naphthalene sulfonate formaldehyde is high range water-reducing and an anion surface active agent based on polyalkyaryl- sulphonate.
Technical spefication:
Solid content 92% min
Moisture 8.0 % max
Fineness 5.0% max
Ph value 7 - 9
Chlorides content 2.0% max
Surface tension 68-72 mn/m
Cement flowing rate 230mm min
Concrete reducing water rate 18% min
Sodium sulfate content 18% max (5%max is also available)
Poly naphthalene sulfonate formaldehyde produces concrete with extremely workable characteristics referred to as high slump. Pns also allows concrete to be produced with very low water/cement ratios at low or normal slumps.Poly naphthalene sulfonate formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation.
Addition ratespoly naphthalene sulfonate formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%.Poly naphthalene sulfonate formaldehyde directionprepare solutions as required.Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%).The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds.
Packed in plastic film bag wrapped with plastic woven sack with a net weight of 25kg each.
Product Description High Range Water-Reducing Admixture Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture Uses Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation Sodium Naphthalene Sulphonate Formaldehyde Specification: Solid Content :96.42% PH value :8.3 Chlorides Content :0.25% Sodium Sulfate Content :4.4%. For powder: woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg.
Product Description High Range Water-Reducing Admixture Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture Uses Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation Sodium Naphthalene Sulphonate Formaldehyde Specification: Solid Content :93% PH value :8.42 Chlorides Content :0. 39% Sodium Sulfate Content :16% Addition Rates Sodium Naphthalene Sulphonate Formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%. Sodium Naphthalene Sulphonate Formaldehyde Direction Prepare solutions as required. Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%). The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds. Sodium Naphthalene Sulphonate Formaldehyde Package, Storage & Handling For powder: Woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg. 25kg in PP woven bag lined with plastic film
Product Description High Range Water-Reducing Admixture Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture Uses Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation Sodium Naphthalene Sulphonate Formaldehyde Specification: Solid Content :96.42% PH value :8.3 Chlorides Content :0.25% Sodium Sulfate Content :4.4% Addition Rates Sodium Naphthalene Sulphonate Formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%. Sodium Naphthalene Sulphonate Formaldehyde Direction Prepare solutions as required. Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%). The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds. Sodium Naphthalene Sulphonate Formaldehyde Package, Storage & Handling For powder: Woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg. 25kg in PP woven bag lined with plastic film
Product Description: High Range Water-Reducing Admixture Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture Uses: Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation Sodium Naphthalene Sulphonate Formaldehyde Specification: Solid Content :96.42% PH value :8.3 Chlorides Content :0.25% Sodium Sulfate Content :4.4% Addition Rates: Sodium Naphthalene Sulphonate Formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%. Sodium Naphthalene Sulphonate Formaldehyde Direction Prepare solutions as required. Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%). The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds. Sodium Naphthalene Sulphonate Formaldehyde Package, Storage & Handling. For powder: Woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg.
Supplier: Series of concrete admixtures, polycarboxylate superplasticizers, melamine based superplasticizer, aliphatic superplasticizer, poly naphthalene formaldehyde sulfonate superplasticizer
Sodium naphthalene formaldehyde is high range water-reducing and an anion surface active agent based on polyalkyaryl- sulphonate. Technical spefication: Solid content 92% min Moisture 8.0 % max Fineness 5.0% max Ph value 7 - 9 Chlorides content 2.0% max Surface tension 68-72 mn/m Cement flowing rate 230mm min Concrete reducing water rate 18% min Sodium sulfate content 18% max (5%max is also available) Sodium naphthalene formaldehyde produces concrete with extremely workable characteristics referred to as high slump. Pns also allows concrete to be produced with very low water/cement ratios at low or normal slumps.Sodium naphthalene formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation. Addition ratessodium naphthalene formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%.Sodium naphthalene formaldehyde directionprepare solutions as required.Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%).The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds. Packed in plastic film bag wrapped with plastic woven sack with a net weight of 25kg each.
High Performance Naphthalene Superplasticizer For Concrete CAS No. 9008-63-3 Basic Information: It is a high range water reducer, high concentration naphthalene-based superplasticizer, also named Naphthalene Sulfonate Formaldehyde Condensate SNF, PNS and FDN etc. Na2SO4 has 3 grades:5% 10% 18% for exporting markets,in domestic we also have 3% 23% Na2SO4 content FDN.It contains no chloride, non-corrosive to steel bars, non-poisonous, odorless, and non-flammable. 1. Application Method and Notice 1,Blend dosage range is 0.5-1.2%. Appropriate blend dosage can be selected according to project object and the materials used during application. 2,FDN powder is recommended to be applied in solution. It can be used in dry form, but make sure mix it thoroughly with concrete. 3,If this product is applied with adoption of stagnant water blending method or post-blend approach, water reduction and dispersion will be better. 4,This product can be formulated with concrete additives of other varieties. It can be "double blended" with blending materials such as fly ash, ground slag, etc. But the blend dosage shall be calculated based on the total of cementing materials. 5,When this product is used for the first time or cement variety is changed, concrete trial preparation shall be conducted according to the adopted materials and construction requirements in the field. Construction mixing rate shall be adjusted based on testing result to serve as instruction for construction blending. 1.Suitable for long-distance construction projects type pumping concrete. 2.Suitable for compounding normal concrete,high-performance concrete,high-strength concrete and ultra-high strength concrete. 3.Suitable for impervious,antifreezed and high durability concrete. 4.Suitable for high-performance and high flowing concrete,self-leveling concrete,fair-faced concrete and SCC(self compact concrete). 5.Suitable for high dosage of mineral powder type concrete. 6.Suitable for mass concrete that used in expressway, railway, bridge, tunnel, water conservancy projects, ports, wharf, underground etc.
Sodium Naphthalene Formaldehyde (SNF-Superplasticizer for Concrete) CAS Code: 36290-04-7 SNF a high range water reducer, commonly referred to as a super plasticizer, also named Naphthalene Sulphonate Formaldehyde Condensate (short name: SNF, PNS, NSF, etcâ?¦) SNF is made from naphthalene, sulfuric acid, formaldehyde and liquid alkali, through sulfonation, hydrolyzation, condensation and neutralization reaction and then drying to powder. SNF-A5% contains very small chloride. Thus, it meets the requirements of chemical admixture specifications for concrete: ASTM Designation C 494 as a Type F admixture, GB8076-2008 and GB50119-2003. Usage SNF produces concrete with extremely workable characteristics referred to as high slump. SNF also allows concrete to be produced with very low water/cement ratios at low or normal slumps. SNF is ideal for use in pre stress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation. SNF will also fluidize concrete, making it ideal for tremie concreting or other applications where high slumps are desired. SNF is compatible with Portland Cement, Normal Portland cement, Portland Slag Cement, Fly-ash Cement, Portland Pozzolanic Cement, etc.
Our products- based superplasticizers can be divided into high-concentration products (Na2SO4 content 10%) according to the Na2SO4 content in the product content. Performance 1. When the strength and slump of the crucible are basically the same, the amount of cement can be reduced by 10-25%. 2. When the water-cement ratio is constant, the initial slump of concrete increases by more than 10cm, and the water reduction rate can reach 15-25%. 3. It has a significant early strength and strengthening effect on cockroaches, and the strength increases by 20-60%. 4. Improve the working capacity of concrete and comprehensively improve the physical and mechanical properties of concrete. 5. It has good adaptability to various cements and is compatible with other types of concrete admixtures. 6. Especially suitable for the following concrete projects: fluid concrete, plasticized concrete, steam concrete, impermeable concrete, waterproof concrete, natural curing precast concrete, steel and prestressed reinforced concrete, high-strength ultra-high-strength concrete. 7. The slump of concrete has a great loss over time, and the slump loss in half an hour is close to 40%.