Neo's family of acrylated alkyd are specially designed medium oil resins based on Oxidising mixed fatty acid. They are pale yellow viscous liquid. They are completely soluble in aromatic hydrocarbons, ketones, esters, higher alcohol, glycol ethers, insoluble in aliphatic hydrocarbons and water. They are compatible with short oil alkyds, acrylated alkyds, amino resins and are incompatible with medium and long oil alkyd resins. They find extensive application in Varnishes for metal decoration and for manufacture of fast drying enamel coatings. These resins impart excellent water, petrol, oil resistance properties to finished products.
* Very fast drying time * Very Good abrasion resistance * Light Color with good yellowing resistance * Very Good compatibility with majority long and medium air dry alkyd resins * Varnish for parquet floor * Furniture finishes and Yacht varnishes * Wood varnishes * Pigment decorative for interior use * Oil % 61% * Type of Polyol Penta * Type of isocyanate Aromatic isocyanate * Free isocyanate content 0% * Solvent White Spirit * Oil type Soya bean oil * Solid Content 55 +/- 2% * Viscosity Gardner @250C @55% WS Z1-Z3 * Viscosity CP @250C @55% WS 2700 - 4600 * Acid Value mg KOH/gm solid 2 max * Color Gardner 5 max
Excellent hardness excellent Gloss * Excellent film leveling and fast solvent release properties * Good sanding properties * Excellent chemical resistance * Recoat-ability and fast drying characteristics * General purpose for Industrial 2K * Urethane two-components primers for metal, wood and aluminum substrates. * Urethane two-components Matt & Gloss finishes and sealers with easy sandability * NC sealers and Matt & Gloss top coat
WQ-869 Specification of Water Based Solid Acrylic Resin Confidential It is recommended that WQ-869 and Joncryl@HPD696 are replaceable to each other as they have the same performances (Joncryl @HPD696) WQ-869 is a high molecular composition acrylic resin which can improve pigment dispersition, maintain a fine gloss and sustain paint stability. The combination of high pigment loading and low viscosity will allow the manufacturers to strength color settlement with delicate gloss finish, meanwhile, the formulating flexibility will not be decreased in one way or another. Paint made from WangQin acrylic polymers and resins is superior to any traditional resins with regard to liquid flow, stability, gloss finish and solubility. The paint processing control and stringent quality assurance have guaranteed a consistent and reliable product quality. Whether applied to screen printing, flexo printing or gravure printing, WangQin acrylic resin is capable of ensuring superior adhesion, sharpness and color rich diversity. Those benefits are well competing with brands such as BASF, HANWHA but also providing significantly and enhanced performances and improved adds-on value for investment from cost point of view. Considering similar product performances and much more cost-effective factors, it is recommended to use WangQin Water based HANWHA: S-70, S-120, S-820, S-20 WQ-869 Key Features & Benefits: Excellent Pigment Dispersition High Transparency and Super gloss efficiency Long-life Color Endurance High Molecular Weight General Information: Classic Physical Characteristics Appearance Transparent Solid Solid Content >99% Acid Value 215 Softening Point() 155 Average Molecular Weight 16500 Tg ( 102
FEATURES * Good Gloss & Gloss retention, very light Color I non yellowing characteristics (Isocyanate currant selective). * Medium Tg and molecular weight I good drying and forms hard and moderately flexible film. * Good pigment wet ability, good leveling and excellent adhesion to various surfaces.
Waterborne Acrylic Modified Saturated Polyester Resin Can be cured at between 120 150. Even higher temperature, it has good yellowing resistance. It is suitable for coil coating and can coating. It has very good results for dipping primer applications. It is also for clear gloss protective coating. Performance Advantages: Low odor LOW VOC Non yellowing, even at high temperature curing Good hardness development Applications: All kinds of baking systems Metal primer and topcoats Industrial applications Spray, roller, brush or dipping can be used. 1, Product Composition: Waterborne Acrylic Modified Saturated Polyester Resin, Cosolvent 2, Typical Data: Type of polymer Waterborne acrylic modified saturated polyester resin Non-volatile(%) 70±2 Viscosity( 25, mpa*s) 30-70* PH ---- Neutral.agent Non neutralization OH value on solids (mgKOH/g) 105 Air dry Inapplicable Cross-Linking with amino resin Applicable Grinding Applicable Drying speed better Corrosion resistance better weatherability better PS:The Viscosity with*is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether 3, Product Properties: Good hardness (>4H), high gloss; Good flexibility; Good solvent resistance; Low temperature fast cross-linking (110. 20minutes); Excellent shear stability, can be grinded with dispersions directly. 4, Instructions: WL-182 can be diluted with water after neutralization by N,N-dimethyl ethanolamine the amount of which is about 4-5%of WL-182.It has tocombine waterborne amino resin to make baking coating. The suggested amount is about 20-30% of WL-182 by weight. The baking temperatureis above 120. The baking conditions and film properties are related with the amino resins used. Right amount of waterborne acidic catalysts canbe added when using methyl etherified amino resin(recommended adding amount is 0.5-1% of WL-182), which can accelerate solidifying. PH value of the coating system can always be adjusted with organic amine or ammonia. Viscosity of the dispersion will increase as the PH valueincreases. The resin can help to wet pigments, so wetting agent may reduce. 5, Storage: It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections. 6, Applications: Amino-baking top coatings. 7, Note: The specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.
Waterborne Acrylic Modified Saturated Polyester Resin Can be cured at between 120150. Even higher temperature, it has good yellowing resistance. It is suitable for coil coating and can coating. It has very good results for dipping primer applications. It is also for clear gloss protective coating. Performance Advantages: Low odor LOW VOC Non yellowing, even at high temperature curing Good hardness development Applications: All kinds of baking systems Metal primer and topcoats Industrial applications Spray, roller, brush or dipping can be used. 1, Product Composition: Waterborne Acrylic Modified Saturated Polyester Resin, Cosolvent 2, Typical Data: Type of polymer Waterborne acrylic modified saturated polyester resin Non-volatile(%) 70±2 Viscosity( 25, mpa*s) 30-70* PH ---- Neutral.agent Non neutralization OH value on solids (mgKOH/g) 105 Air dry Inapplicable Cross-Linking with amino resin Applicable Grinding Applicable Drying speed better Corrosion resistance better weatherability better PS:The Viscosity with*is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether 3, Product Properties: Good hardness (>4H), high gloss; Good flexibility; Good solvent resistance; Low temperature fast cross-linking (110 20minutes); Excellent shear stability, can be grinded with dispersions directly. 4, Instructions: WL-182 can be diluted with water after neutralization by N,N-dimethyl ethanolamine the amount of which is about 4-5%of WL-182.It has tocombine waterborne amino resin to make baking coating. The suggested amount is about 20-30% of WL-182 by weight. The baking temperatureis above 120â??. The baking conditions and film properties are related with the amino resins used. Right amount of waterborne acidic catalysts canbe added when using methyl etherified amino resin(recommended adding amount is 0.5-1% of WL-182), which can accelerate solidifying. PH value of the coating system can always be adjusted with organic amine or ammonia. Viscosity of the dispersion will increase as the PH valueincreases. The resin can help to wet pigments, so wetting agent may reduce. 5, Storage: It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections. 6, Applications: Amino-baking top coatings. 7, Note: The specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.
Type - 2K Epoxy Resins NVM - 75% Color Gardner - 6 Max. Viscosity - 12000 - 21000 Packaging - 30kg/195kg Features/Applications - Greener 2K Epoxy Resin CNSL Technology Low Hardener Requirement Inbuilt Anticorrosive Properties Excellent Flexibility Formulation Cost Reduction High DFT Coatings
Excellent Gloss & Gloss retention, excellent color / non yellowing characteristics High viscosity, medium Tg and high molecular weight / good drying and forms hard and moderately flexible film Excellent pigment wet ability and good resistance to detergents and soaps. As a decorative and quick drying paints. Industrial quality quick drying paints / as acrylic topcoat for textured paints. Road marking paints / for pavements / kerb stones / pathways. clear lacquers for PVC leather cloth / over lacquering and Metallizing / coatings for electronic equipment like TV / video and similar items. Scratch resistant protective coats and polycarbonate glazing.
We manufacture alkyd resin for paint industries