One-part Waterborne Epoxy Ester Resin WL-172 epoxy coating contains the following added features: Extremely Long Lasting Flexible & Durable Water resistant High-Gloss Heat Resistant Economical Reduces Maintenance Costs Lead-free Nontoxic Rustproof One Application Only Acid & Saltwater Resistant Protects Against Environmental Hazards High Adhesion 1,Product Composition: Waterborne Epoxy Ester Resin, Cosolvent, Neutralizing Agent, Water 2,Typical Date Type of polymer Waterborne epoxy ester resin Non-volatile(%) 70�±2 Viscosity( 25â??, mpa*s) â?¤200* PH ---- Neutral.agent DMEA OH value on solids (mgKOH/g) ---- Air dry Applicable (Oxidation Cross-linking) Cross-Linking with amino resin Inapplicable Grinding Applicable Drying speed better Corrosion resistance better weatherability better PS:The Viscosity with*is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether 3,Product Properties: Excellent anticorrosion performance, especially for the preparation of anti-rust base coating; Fast drying speed, good hardness; Excellent salt fog-spray resistance and early water resistance: Good storage stability; Excellent shear stability, can be grinded with dispersions directly. 4,Instructions: WL-172 can be diluted with deionized water or lower alcohol or alcohol ether to white emulsion. It can be dried by oxidation cross-linking addingoily/water driers at normal temperature or low-temperature baking. The oily driers need to be diluted by the solvent such as butyl alcohol or ethanolfor use. The water dispersion of WL-172 is stable at neutral or slight alkaline conditions pH value has to be carefully observed in coating production sinceprecipitation may occur if acidic pigments like carbon black are used in the system. PH value of the coating system can always be adjusted triethylamine or N, N-dimthylethanolamine. Viscosity of the dispersion will increase as the PH value increases. 5,Applications: Air-drying or low temperature baking antirust coatings. 6,Note: The specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.
WQ-869 Specification of Water Based Solid Acrylic Resin Confidential It is recommended that WQ-869 and Joncryl@HPD696 are replaceable to each other as they have the same performances (Joncryl @HPD696) WQ-869 is a high molecular composition acrylic resin which can improve pigment dispersition, maintain a fine gloss and sustain paint stability. The combination of high pigment loading and low viscosity will allow the manufacturers to strength color settlement with delicate gloss finish, meanwhile, the formulating flexibility will not be decreased in one way or another. Paint made from WangQin acrylic polymers and resins is superior to any traditional resins with regard to liquid flow, stability, gloss finish and solubility. The paint processing control and stringent quality assurance have guaranteed a consistent and reliable product quality. Whether applied to screen printing, flexo printing or gravure printing, WangQin acrylic resin is capable of ensuring superior adhesion, sharpness and color rich diversity. Those benefits are well competing with brands such as BASF, HANWHA but also providing significantly and enhanced performances and improved adds-on value for investment from cost point of view. Considering similar product performances and much more cost-effective factors, it is recommended to use WangQin Water based HANWHA: S-70, S-120, S-820, S-20 WQ-869 Key Features & Benefits: Excellent Pigment Dispersition High Transparency and Super gloss efficiency Long-life Color Endurance High Molecular Weight General Information: Classic Physical Characteristics Appearance Transparent Solid Solid Content >99% Acid Value 215 Softening Point() 155 Average Molecular Weight 16500 Tg ( 102
Waterborne Acrylic Modified Saturated Polyester Resin Can be cured at between 120 150. Even higher temperature, it has good yellowing resistance. It is suitable for coil coating and can coating. It has very good results for dipping primer applications. It is also for clear gloss protective coating. Performance Advantages: Low odor LOW VOC Non yellowing, even at high temperature curing Good hardness development Applications: All kinds of baking systems Metal primer and topcoats Industrial applications Spray, roller, brush or dipping can be used. 1, Product Composition: Waterborne Acrylic Modified Saturated Polyester Resin, Cosolvent 2, Typical Data: Type of polymer Waterborne acrylic modified saturated polyester resin Non-volatile(%) 70±2 Viscosity( 25, mpa*s) 30-70* PH ---- Neutral.agent Non neutralization OH value on solids (mgKOH/g) 105 Air dry Inapplicable Cross-Linking with amino resin Applicable Grinding Applicable Drying speed better Corrosion resistance better weatherability better PS:The Viscosity with*is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether 3, Product Properties: Good hardness (>4H), high gloss; Good flexibility; Good solvent resistance; Low temperature fast cross-linking (110. 20minutes); Excellent shear stability, can be grinded with dispersions directly. 4, Instructions: WL-182 can be diluted with water after neutralization by N,N-dimethyl ethanolamine the amount of which is about 4-5%of WL-182.It has tocombine waterborne amino resin to make baking coating. The suggested amount is about 20-30% of WL-182 by weight. The baking temperatureis above 120. The baking conditions and film properties are related with the amino resins used. Right amount of waterborne acidic catalysts canbe added when using methyl etherified amino resin(recommended adding amount is 0.5-1% of WL-182), which can accelerate solidifying. PH value of the coating system can always be adjusted with organic amine or ammonia. Viscosity of the dispersion will increase as the PH valueincreases. The resin can help to wet pigments, so wetting agent may reduce. 5, Storage: It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections. 6, Applications: Amino-baking top coatings. 7, Note: The specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.
Waterborne Acrylic Modified Saturated Polyester Resin Can be cured at between 120150. Even higher temperature, it has good yellowing resistance. It is suitable for coil coating and can coating. It has very good results for dipping primer applications. It is also for clear gloss protective coating. Performance Advantages: Low odor LOW VOC Non yellowing, even at high temperature curing Good hardness development Applications: All kinds of baking systems Metal primer and topcoats Industrial applications Spray, roller, brush or dipping can be used. 1, Product Composition: Waterborne Acrylic Modified Saturated Polyester Resin, Cosolvent 2, Typical Data: Type of polymer Waterborne acrylic modified saturated polyester resin Non-volatile(%) 70±2 Viscosity( 25, mpa*s) 30-70* PH ---- Neutral.agent Non neutralization OH value on solids (mgKOH/g) 105 Air dry Inapplicable Cross-Linking with amino resin Applicable Grinding Applicable Drying speed better Corrosion resistance better weatherability better PS:The Viscosity with*is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether 3, Product Properties: Good hardness (>4H), high gloss; Good flexibility; Good solvent resistance; Low temperature fast cross-linking (110 20minutes); Excellent shear stability, can be grinded with dispersions directly. 4, Instructions: WL-182 can be diluted with water after neutralization by N,N-dimethyl ethanolamine the amount of which is about 4-5%of WL-182.It has tocombine waterborne amino resin to make baking coating. The suggested amount is about 20-30% of WL-182 by weight. The baking temperatureis above 120â??. The baking conditions and film properties are related with the amino resins used. Right amount of waterborne acidic catalysts canbe added when using methyl etherified amino resin(recommended adding amount is 0.5-1% of WL-182), which can accelerate solidifying. PH value of the coating system can always be adjusted with organic amine or ammonia. Viscosity of the dispersion will increase as the PH valueincreases. The resin can help to wet pigments, so wetting agent may reduce. 5, Storage: It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections. 6, Applications: Amino-baking top coatings. 7, Note: The specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.
Mirror-like effect coatings resin BC5043 Mirror-like effect paint is a new developed paint, which is composed of special resins and precious metal pigment. The metal flashing is very similar to electroplating. BC5043 Physical and Chemical Data: Test item Standard Appearance Silver liquid Hardness 48h:Grade F Adhesion 48h:
Water-based hydroxyl acrylic dispersion for floor coatings Hydroxyl Acrylic copolymer emulsion Product Description Wl-156 is an anionic hydroxylated styrene acrylic copolymer emulsion. It is recommended to use with amino resins for baking coatings, which requires high gloss, good hardness and outstanding solvent resistance. Biocide: CMIT/MIT 3:1 49ppm, and MIT 240ppm. Properties 1. Excellent resistance to boiling water 2. High gloss, high hardness 3. Excellent solvent resistance 4. Excellent recoatabilit Note:Be sure to adjust the pH of WL-156 over 7 with the pH adjustment in use. Characteristic data* Property Value Unit Method Appearance Translucent to milky white Weight Solids 47�±1 % pH 3.5-5.5 GB 6920-1986 Viscosity 10-1000 mPs Brookfield,LV,62#,30rpm,25C MFFT 40-42 C GB/T 9267-2008 OH content 1.3 % Calculated on solid resin Density 1.04 g/cm3 GB/T 4472-2011
Water based Alkyd resins for industrial coatings Alkyd resins represent, both historically and commercially, the class of chemical compounds used in the field of paints and stains. Their chemical structure is a continuous and waterproof film which can protect surfaces from multiple strenuous agents conducting an anti-corrosive. The commercial paints based on these resins, the molecules of the structure, in particular, create strong structural interactions involving the formation of films able to cover any type of surface by protecting against aging, weather and wear. the paints made from alkyd resins have been among the first to be used in the construction industry, in particular in the production of exterior paints and enamels, and in the production of products for the treatment of surfaces exposed to particularly arduous conditions, for example various ferrous metal substrates such as structural steel, railings, equipment and machinery. We offers alkyd resins that have achieved high functionality through modification with other resins such as acrylics, urethanes, epoxies. Features: Good storage stability, no ease to hydrolyze; Environment friendly product, VOC of less than 7%; Fast dry, and excellent gloss; unnecessary to add drier during paint preparation; Excellent shear stability, and can directly use for pigment paste grinding; Excellent anti-corrosivity, and good initial water resistance; The finished product paint has good versatility and good in-can appearance, and can replace oil based alkyd anti-rust paint, alkyd ready mixed paint, alkydenamel, etc Waterborne Acryle Resin Product No. WL-310 Acryle modified akyd dispersion Solids content: 42±2 Viscosity(25,mPa·s): 2000 Air dry: Oxidation Cross-linking Property:Low VOC; High gloss; Excellent corrosion resistance. Application:Waterborne alkyd enamel ready mixed paint and anti-rust paint PS:(1) The Viscosity withï¼?is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ether.
Hydroxyl Acrylic Resin SE6651 K SE 6651 K is an hydroxyl functional acrylic resin that, when combined with appropriate aliphatic polyisocyanates, provides excellent durability and outstanding gloss retention. It should be used in solid color paints and clearcoats for vehicle refinishing and in industrial topcoats. Se 6651K is used in combination with aliphatic isocyanates it exhibits good exterior durability, good build and gloss, high end hardness and good adhesion results on metallic base coats. 1. Features High gloss, good levelling property, high hardness, excellent chemical resistance and pigment dispersity 2. Applications PU top coat, automotive refinishing paint, colored paint 3. Properties Componen:Acrylic ester copolymer Appearance :Clear Fe-Co Color:ï¼?1 Viscosity Pa.s/25â??: 2-5 Non-volatile%:60�±2 Acid value mgKOH/g: 4-8 Solvent: XYL/S-100 Hydroxyl value:86 4. Compatibility and solubility XYL + BCS + TYL + CAC + BAC + CYC + Remark:+ show soluble in/compatible in 5. Reference formula Two component (brilliant black paint) Diluent (A component) SE6651K 70 XYL 40 BBG333 0.2 TOL 5 BBG306 0.3 BAC 25 BBG110 2.0 CAC 15 BAC 24.3 PMA 15 Carbon black 3.0 10% sn 0.2 (B component) Bayer N3390 A component: B component: diluent=100: 15: 80~100 6. Process conditions Baking condition: (1) 65 x 60min, place 24hours for test (2) Air drying Substrate: Sand plate tin 7. Test technical index Test Item Test Method Reference Standard Test Standard Test Result (reference value) Surface drying Blow cotton ball method ------ Not stick cotton ball 25min(2m) Hard drying Finger pressing method ------ No finger print 24h(25m) 8h hardness Pencil scratch GB/T6739-96 -----
Water Borne Peelable Resin PU-3018A Product Introduction PU-3018A is a protective resin made of water borne polyurethane dispersions, using high performance additives and advanced processing technology. The waterborne peelable coating made of this resin has bright color, and fine particle size, coated on the surface of automobiles, furniture, electrical appliances and other objects as a protective coating, with good protection, can form a continuous, uniform, strong protective coating on the surface of complex shapes, can isolate the erosion medium, protect the surface of the substrate not easy to be worn, abrased, scratched, meanwhile, moisture-proof, rust-proof, corrosion â??proof, improve the commodity value of coated products. Upon completion of the protection period, the film can be conveniently removed to restore the original appearance of the object. Physical Property ModelPU-3018ACompositionPolyurethane organosilicon copolymerAppearanceMilky liquid with blue shadeSolid content35�±2%PH7.1-8.0IonicityAnionViscosity (Brookfield 25â??)50-160mpa.s Performance Features High peeling strength, not easy to break High strength, good water resistance Excellent low temperature resistance, weather resistance, air permeability and moisture resistance, and universality of different substrates Applications All kinds of metal surface, for example, temporary protection of products such as automobiles and stainless steel appliances Temporary protection of all kinds of glass products Temporary protection of all kinds of plastic products Can be used as temporary protection for coating, ink coating Can be used as temporary protection for other products Application Guide Can be directly painted on the surface of the construction surface, or add the right amount of water after dilution Can be added talc, silica and other inorganic split materials Can also add resin-free pigment paste to do color temporary protection coating The peelable film dry completely, when it needs to be removed, please tear out a long mouth along the edge of the film, and then slowly peel the film from the coated surface with a force of about 4-5kg Packaging and Storage Condition 50KG, 120KG, 200KG plastic drum; Stored in a 100% light â??proof sealed container; Stored in a cool and dry place indoor at 5-30â??; Under high temperature or exposure, the shelf life will be significantly shortened; Shelf life is 12 months from the date of production under condition that the drum is not opened. Special Tips This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.