A general-purpose alkyd based primer with anticorrosive red iron oxide pigment for the protection of steel surfaces against moderate corrosive environments.It is an economical anticorrosive primer for general-purpose applications.
USES
It is recommended for mild steel structures and surfaces in domestic and mild corrosive environments. It is suitable for interior and exterior use.
PROPERTIES
Colour, Dry Film : Red
Finish, Dry Film : Smooth/Matt
Volume Solids, % 51�± 2
Specific Gravity : 1.46�± 0.05
Theoretical Spreading Range : 11-12 M2/L
Recommended Dft Range (Dry Film Thickness) : 35-45 Microns/Coat
Recommended Wft Range (Wet Film Thickness) : 75-90 Microns/Coat
Flash Point : 38 �° C
Flexibility : Good
Drying Time : @ 30 �° C (Temperature, humidity, air movement, film thickness and number of coats all affect the drying time.)
Dry To Recoat/Overcoat : 12 Hours
Hard Dry : 24 Hours
Zinc Enriched Red Oxide Primer Price : 0.90 Ltr - USD 2.2 3.60 Ltr -USD 7.4 18 Ltr- USD 31.1
Red Oxide Primer -premium Quality
Synthetic Red Oxide Primer
Epoxy Red Oxide Primer
Description Red Oxide Metal Primer can be used as an undercoat for ferrous metal substrates. It offers good opacity, coverage, flow & leveling & Protection against corrosion. Unique Features & Benefits Ease of Application Excellent durability Good Corrosion Resistance Super silky and Glossy finish. Excellent flow characteristics to form smooth and uniform finish Excellent color and color retention Excellent coverage
Nuvent Red Oxide synthetic primer is formulated for preventing Rust. This primer is used primarily on ferrous metal either Interior/Exterior surfaces in mild corrosive environment. Coverage Area : 47 to 49 Sq.ft*/litre (2 coats) Drying time : 40 min (Recoat frequency : 2 hrs)
Supplier: Refractory bricks, high alumina bricks, acid proof bricks, tiles and castables, all mortars and fire clay, low cement castables, insulating castables, conventional dense refractory bricks, insulation bricks, cold face, hot face insulation bricks, hot face insulation bricks, acid resistant bricks/components, membranes, acid resistant cement, construction chemicals, class 1 ar tiles and bricks 38mm and 75mm, 4457 vitrified ar tiles with 0% water absorption, 20mm & 25m, primer, mastics, pot. silicate cement, coerce cement, furnace based cement, crushed refractory boiler bed material, acid resistant tiles, acid resistant brick fireclay type, acid resistant brick red shale type, bitumen primer, epoxy resin & hardner, furan powder and syrup solution,
Supplier: Red Oxide Primer
A vinyl acrylic primer designed for priming masonry surfaces PROPERTIES Colour : Full range- as per shade card Finish : Smooth / Matt Solids(volume): 24 �±2% Specific gravity: 1.40 �± 0.05 Theoretical Coverage 7-8 m2/ltr @ 40 DFT DRYING TIME :AT 25 Touch dry: 2 hours To Recoat: 4 hours