High alumina ball means alumina ball with aluminium oxide content higher than 90%, high alumina ball is high efficiency grinding media in today industry. The high alumina ball works together with the high alumina mill linings brick will benefits you:
> Less grinding time, doubled productivity.
> Less wear loss of the ball and linings, more clean you final product keep.
> Longer service life, less down time
Physical Properties:
1) Bulk Density : 60mm > 3.65, 50mm > 3.65, 40mm > 3.65, 30mm > 3.65, 20mm > 3.63
2) Self Wearloss (24h) : < 0.04
3) Water absorption : < 0.1%
4) Hardness (M0hs) : 9
5) Service Temp : > 1600 C
6) Color : White
Specification:
1) Appearance > Faint Yellow,
2) Bulk Density > 2.96g/cm3,
3) Self Wearing (Within 24hrs) > 0.04%,
4) Water Absorption > 0.008%,
5) Degree of Hardness > 7-8,
6) Temperature > 1400 - 1600 C,
Alumina Bricks (142mm x 42mm x 96mm)
325 mesh is used commonly in ceramics. The fibrous form of wollastonite can be very beneficial in bodies. In low fired ceramics wollastonite reduces drying and firing shrinkage and drying and firing warpage. It also promotes lower moisture and thermal expansion in the fired product and increases firing strength.
PHYSICAL PROPERTIES:
"L" > 96-98,
"A" > 0.5 - 0.7,
"B" > 3.25 -4.50,
Whitness > 87.44,
Water Absorption > 18.68%,
Shrinkage > 1.02,
Loss on Ignition > 6.86,
Dry M.o.R kg/cm2 > 27.1,
Fired M.O.R Kg/cm2 > 63.50,
Water of Plasticity > 36.80,
T.D.S > 251,
Temprature C > 1205/1215,
PHYSICAL PROPERTIES:
"L" > 89 - 90,
"A" > 1.98,
"B" > 7 - 9,
Whitness > 69.77,
Temprature C > 1207/1217,
T.D.S > 140,
Shrinkage > 9.46%,
Fired M.O.R Kg/cm2 > 228.6,
Dry M.o.R kg/cm2 > 32.04,
Loss on Ignition > 11.64 %,
Water Absorption > 10.14%,
Water of Plasticity > 44.02%,
Physical Properties:
Brightness > 90%,
Whitness > 93%,
Oil Absorption > 36.20 gm/100ml,
Water Absorption > 34.60ml /100 gm,
Bulk Density > 0.86 gm/cm,
PH Value > 8.7
Natural Clay Useful to increase whiteness of the end product best product for Ceramic and related industries Whiteness index about 91 Packed in 1.25 MT jumbo bags.
Physical Properties:
"L" > 96 - 97,
"A"> 0.2 - 0.6,
"B" > 2.5 - 3.5,
Whitness > 91.48,
Temprature C > 1209/1220,
Cycle Min. > 65,
T.D.S > 110,
Shrinkage > 8.24%,
Fired M.O.R Kg/cm2 > 141.2,
Dry M.o.R kg/cm2 > 31.8%,
Loss on Ignition > 12.53% ,
Water of Plasticity > 49.6%,
Water Absorption > 18.18%,
Physical Properties:
Brightness > 95.7%,
Whitness > 97.4%,
Oil Absorption > 58.60 gm/100ml,
Water Absorption > 58.80 ml/100 gm,
Bulk Density > 0.64 gm/cc,
PH Value > 8.4
Possessed with high density, high hardness, low wear, good seismic stability and good corrosion resistance, the products are the most ideal medium for grinding glaze, blank and mineral powder processing, and are used as the grinding medium of ball mill in ceramics, cement, paint, refractory.
Specification:
> Appearance : Faint Yellow,
> Al2o3 : 67.9 %,
> Bulk Density : 2.96g/cm3,
> Self Wearing (Within 24hrs) : 0.04%,
> Water Absorption : 0.008%,
> Use Raw Material : Fining High bauxite,
> Temperature : 1400-1600 C