Property Unit
Typical Value
Mass density g/cm 3 0.941-0.959
Melt flow Rate(190 centidegree /2.16kg) g/10min 1.0
Tensile yield strength MPa 19.0
Flexural modulus Mpa 965
Elongation@ break % 400
Impact Embrittlement temperature centidegree MAX -118
Dielectric Constant 100KHZ 2.32
1MHZ 2.31
Loss Tangent 100KHZ MAX 0.0001
1MHZ MAX 0.0001
Volume resistivity OHM-CM MIN 1x10 15
Application
Mainly used for the production of high toughness of the telephone,cable insulation material
LDPE:
Physical Properties Test Method Nominal Value Unit
Density ISO 1183 0.921 g/cm3
Melt Mass-Flow Rate (MFR) ISO 1133 1.9 g/10min
Hardness
Shore Hardness (shore D) ISO 868 45
Mechanical Properties
Tensile Modulus ISO 527-2 175 MPa
Tensile Strength Yield, ISO 527-2 9.0 MPa
Break, 13.0 MPa
Tensile Strain(Break) ISO 527-2 850 %
Modulus of Elasticity Internal Method 250 MPa
Thermal
Vicat Softening Temperature ISO 306/A50 89.0 �°C
Melting Temperature (DSC) DIN 53765 108 �°C
Peak Crystallization Temperature (DSC) DIN 53765 97.0 �°C
Heat of Fusion DIN 53765 110 J/g
Electrical
Volume Resistivity ASTM D257 8.5E+15 ohm â?¢cm
Dielectric Strength ASTM D149 30.0 kV/mm
Dielectric Constant (60Hz) ASTM D150 2.20 %
Dissipation Factor (60 Hz) ASTM D150 0.00050
LLDPE
Properties Test conditon Test method Test data Unit
Density 0.91
MFI 2
Drop impact strength ASTM D-1709 90 g
Elongation ,vertical/horizontal ASTM D-882 600/800 %
tensilestrength,thermal resistance ASTM D-1004 105/95 Kg/cm
elongation ASTM D-638 930 %
tensile strength ASTM D-638 180
tensile strength,vertical/horizontal ASTM D-882 380/350
Vicat softening point ASTM D-1525 103 C
melting point ASTM D-2117 126 C
Turbidity ASTM D-1009 12 %
45 glossness ASTM D-2457 75 %
Specification:
Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
Application:
HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.
Application
Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.