Our company supply various refractory material, such as 1). Fire bricks 2). High alumina brick 3). Insulation brick tm23, tm26, tm28 4). Resist aid brick 5). Ceramic fiber blanket 6). Castables, mortars , cements, ramming mixes The specification of fire brick is as follows: Fire bricks for general use Y-fb gfb40 gfb42 gfb45 Al2o3(%)min. 40 40 42 45 Fe2o3(%)max. 2.5 Refractoriness()min. 1710 1730 1750 1750 Refractoriness under load 0.2mpa()min. 1300 1350 1400 1400 Apparent porosity(%)max. 22 20 20 20 Cold crushing strength (mpa)min. 30 30 35 40 Linear change after reheating(%)max. At 1350íß2h +0.1 -0.4 At1400x3h +0.1 +0.1 +0.2 Also we can supply the product as per the customers' requirement. Fire bricks for general use Y-fb, gfb40, gfb42, gfb45 Al2o3(%)min.: 40%, 42%, 45% Refractoriness.:1710, 1730, 1750
Magnesium ingot: We can supply various kinds of magnesium related products .Such as magnesium ingot, magnesium alloy, magnesium granular(powder), etc. Magnesium ingot as below:(note:customers special request available!) Magnesium ingot Mg:99.9%min. Al: 0.02%max. Si 0.02%max. Mn 0.02%max. Magnesium ingot size: 7.5kg+/- 0.5kg High purity magnesium: Mg:99.95%min. Al: 0.0040%max. Fe 0.0045%max. Si 0.0070%max. Ni 0.0010%max. Mn 0.0070%max. Cu 0.0030%max. Magnesium ingot size: 7.5kg+/- 0.5kg Mg:99.99%min. Al: 0.0020%max. Fe 0.0045%max. Si 0.0020%max. Ni 0.0010%max. Mn 0.0020%max. Cu 0.0020%max. Magnesium ingot size: 7.5kg+/- 0.5kg Magnesium alloys such as : Az91d, az91hp , az63 , za10, am60, am50, am20, ze41a and so on with the standard of gb/t5153-2003, gb/t19073-2003 and astmb94-92. Magnesium ingot size: 7.5kg+/- 0.5kg Packed on pallets with plastic covering and steel tape to tighten
We are engaged in making Lead available in several forms including LME registered and non registered 99.97% and 99.99% as well as secondary ingots, foil, granules, powder, rod, shot, sheet, and wire. Lead is a bluish-white lustrous metal. It is very soft, highly malleable, ductile, and a relatively poor conductor of electricity. It is very resistant to corrosion but tarnishes upon exposure to air. Alloys include pewter and solder.
We offer a wide plethora of Zinc in many forms including LME registered and non registered Special High Grade Ingots and Jumbos, cathodes, dust, foil, granules, powder, pieces, anodize activated powder, shot, and a mossy form. Zinc is a bluish-white, lustrous metal. It is brittle at ambient temperatures but is malleable at 100 to 150°C. It is a reasonable conductor of electricity, and burns in air at high red heat with evolution of white clouds of the oxide. Plating thin layers of zinc on to iron or steel is known as galvanizing and helps to protect the iron from corrosion.
We are able to supply Tin in many forms including LME registered and non registered, ingots, slabs, bars, foil, granules, powder, anodized activated powder, shot, wire, sticks, ingots, and “mossy tin”. Tin is a silvery-white metal, is malleable, somewhat ductile, and has a highly crystalline structure. The element has two colours, with a cubic structure which changes at allotropic forms. On warming it is grey, the ordinary form of the metal. When Tin is cooled below 13.2°C, it changes slowly from white to grey or tetragonal structure. This change is affected by impurities such as Aluminium and Zinc, and can be prevented by small additions of Antimony or Bismuth.
We hold immense expertise in making available Copper in many forms including LME registered and non registered cathodes, billets, rods, cakes, bars, foil, sheet, granules, plates, powder, shot, turnings, wire, insulated wire, mesh and “evaporation slugs”. Copper is one of the most important metals. Copper is reddish with a bright metallic lustre. It is malleable, ductile, and a good conductor of heat and electricity (second only to silver in electrical conductivity). Its alloys, brass and bronze, are very important. Monel and gun metals also contain copper. The most important compounds are the oxide and the sulphate, (blue vitriol
We put forward a high quality of assortment of Nickel which is available in many forms including LME registered and non registered cathodes, cut cathodes, briquettes, pellets, disks, shots, granules, foil, powder, flakes, sheet, wire, mesh, spheres, “evaporation slugs”, and rods. Nickel is a silvery white metal that takes on a high polish. It is hard, malleable, ductile, somewhat ferromagnetic, and a fair conductor of heat and electricity
Magnesia Bricks Description Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application. Magnesia Bricks Features: It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature. Magnesia Bricks Application Basic open-hearth furnace for steelmaking Electric furnace bottom and wall Permanent lining of oxygen converter Non-ferrous metal metallurgy furnace Hyperthermia tunnel kiln Lining of rotary cement kiln Heating furnace bottom and wall Regenerative chamber of glass furnace Magnesia Bricks Properties High Refractoriness Good alkaline slag erosion resistance High apparent initial softening temperature Good thermal conductivity High thermal expansion Magnesia Bricks Manufacturing Process Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : RED SHALE Type Acid Resistant Brick Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions Heavy thermal shock Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick Characteristic RED SHALE ACID RESISTANT BRICK Test Standard Bulk Density, gm/cc - 2.3 to 2.35 ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968 Apparent Porosity, % -0.5 to 1.75 S 4860 Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279 Modulus of Rupture, PSI -2133 to 3555 ASTM C-67 Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968 Abrasion Resistant , Volume in mm3 -69 to 85 EN 102 Surface Hardness, MOHS Scale - 7