Ks Traders

End use of Bottle grade chips mainly depends on the Intrinsic Viscosity (IV). PET Chips with IV 0.80 is mainly used for drinking water bottles and mineral water bottles. PET Chips with IV 0.82 is mainly used in making bottles for carbonated beverages, small bottle for edible oil, alcohol, medicines and pet sheets as they need better quality and high finished product rate. PET Chips with IV of 0.85 are mainly used for making huge packing bottles for carbonated beverages and 3-5 gallons water bottles as these bottles should to have great strength and resistance against high pressure. Bottle Grade PET Chips Features of bottle grade PET Chips are low processing temperature, wide scope in packaging, excellent transparency and high in finished product rate.

The main raw material of PTA and MEG is added with modifiers of third monomer and fourth monomer, etc., then subjected to copolymerization reaction to make modified polyester pellet with melting point at 100'C - 225C. Functional characteristics low melting point, good spinnability and excellent fiber adhesion effect Application scope manufacturing bi-component core-sheath fiber and filament yarns, etc. Specification - LOW MELTING PET CHIPS TRB FIBER GRADE 110-225.

Category PET Chips Tags polyester chips, semi-dull, textile grade Raw materials PTA + MEG Grade Bright/Semi-dull Form Slightly yellow/white granules Cationic Polyester Chips for BCF Yarn, mainly used for the development of cellulose-like fibers, with special post-spinning false twist processing, it can develop viscose and cotton-like fibers; It can also be used to some extent as a substitute for nylon 6 fibers.

PET Chip for Spunbond Non-Woven Fabric Semi-dull Grade Specialty Polymer for Nonwovens Product Description: Our non-woven fabric polyester chip is a high-viscosity PET material designed specifically for the production of spunbond nonwoven fabrics. Unlike traditional textile production processes, nonwovens are created directly from fiber or polymer without the need for yarn spinning. PET chips are an essential raw material in this process. This newly developed polymer is widely used in various industries, including medical treatment, home decoration, filtration materials, and insulating materials. The high-viscosity PET chips offer enhanced device performance and flexible polyester capacity, significantly improving the quality of non-woven products. Key Features: High Intrinsic Viscosity (IV): The intrinsic viscosity of regular polyester chips typically ranges between 0.64-0.68 dl/g. Our high-viscosity chips reach an IV of 0.71 dl/g, offering improved durability and product performance. Stable Carboxyl Terminal Value and Melting Point: Ensures consistency and quality during the manufacturing process. Enhanced Non-woven Product Quality: The high-viscosity nature of the chips improves the overall strength and reliability of the final non-woven fabric. SPECIFICATIONS: Intrinsic Viscosity: 0.711 dl/g Colour Value: L: 83.2 b: 5.9 COOH Content: 25.8 mol/t DEG Content: 1.14% Melting Point: 261.0C Water Content: 0.05% Ash Content: 0.03% Irregular Chip Content: 0% Powder Content: 0% TiOâ?? Content: 0.29% Weight (g/100 chips): 2.918 g Remarks: IV Testing Method: The solvent used is a 1:1 mixture of phenol and tetrachlorethane, tested at a temperature of 25C. Testing Standard: Complies with GB/T 14190-2017.

What is PET Open Agent Film Chips? PET Open Agent Film Chips are plastic chips made of polyethylene terephthalate (PET) that contain an open agent, which helps to improve the adhesion of inks and coatings to the surface of the film. It is uniformly depressed anti-adhesive, with excellent film-forming properties; polymerization of continuous device production makes the quality high and stable. As an opening agent to be used with film grade base materials to produce various types of films. It can be used in films with special requirement for optical and surface properties or ultra-films below 8u. Can be used directly in foodstuffs after FDA approval.

What is PET Open Agent Film Chips? PET Open Agent Film Chips are plastic chips made of polyethylene terephthalate (PET) that contain an open agent, which helps to improve the adhesion of inks and coatings to the surface of the film. It is uniformly depressed anti-adhesive, with excellent film-forming properties; polymerization of continuous device production makes the quality high and stable. As an opening agent to be used with film grade base materials to produce various types of films. It can be used in films with special requirement for optical and surface properties or ultra-films below 8u. Can be used directly in foodstuffs after FDA approval.

Low Melting PET Chip is a specialized form of polyethylene terephthalate (PET) that features a lower melting point compared to standard PET chips. This property enables easier processing and expands its potential applications across various industries. It is particularly well-suited for Hot Melt Yarn Masterbatch production and serves as an extrusion-grade polymer for hot-melt adhesive and glue coating processes. Key Features: Lower Melting Point: The chip exhibits a melting temperature range of 90C to 160C, allowing for faster, more energy-efficient processing during molding or extrusion. Excellent Compatibility: It can be blended or co-extruded with other PET grades, making it versatile in a variety of manufacturing processes. Cost Efficiency: The lower energy consumption and reduced processing time lead to significant cost savings.