Corrotech Industries

METHOD OF APPICATION: * Mastic compound application consist of two coats of. Primer ,Primer and followed by Mastic compound in recommended thickness, ranging from min. 12mm to 25mm in one or two layers to achieve desired thickness without any pin hole and crack. 1). Surface preparation and application of Primer: Refer application method of Primer. 2). After doing necessary surface preparation and application of primer coating, area to be installed with Mastic compound should be divided in to equal no. bays. To maintain even thickness required, place wooden or aluminum batten. Mastic compound is then broken in small pieces and put it in heating pan. While heating, keep material moving to avoid burning. It is heated until it comes in a uniform consistency and then applied on the surface and works it with wooden float, to achieve uniform thickness and smooth surface free from any pinholes. CHEMICAL RESISTANCE PROPERTIES: * Mastic compound has good resistance to weak, diluted acids, alkalis salts etc. It is not recommended to use against strong acids, oxidizing acid solvents, oil and fats STORAGE & PACKING: * Keep Mastic compound away from direct sunlight, heat solvents etc. Under this condition, its shelf life is unlimited. It is supplied in cake form and approx. wt. is 10 kgs. HEALTH & SAFETY: * Handle melted Mastic compound compound very carefully . Avoid contact with skin. It is advisable to wear protective wears at the time of use of Mastic compound and all other our products. This information, given in good faith, is based on results gained from experience and tests. However, all recommendations or suggestions are made without guarantee since the conditions of use are beyond our control.

DATA SHEET FOR EPOXY EPOXY COATING :- INTRODUCTION - EPOXY COATING (HYB) is a two part high solids solvent free epoxy phenolic resin based coating system designed for hard wearing, smooth surface finish for floors, walls and on steel structures. Nonskid surface finish can be achieved on floor, if required. FEATURES: 1) Hard Wearing 2) Non Dusting 3) Excellent Surface Finish 4) Non Smelling 5) Good Aesthetics 6) Highly Chemical Resistant APPLICATION: 1.Stir well before mixing Part A and Part B and mix in the prescribed ratio. 2.Apply one coat of EPOXY primer on the clean and dry surface. 3.EPOXY COATING (HYB) should be applied on the surface by brush or roller within 24 hrs. After application of primer coat it should be allowed to air dry for min. 4 hrs. Preferable in a dust free atmosphere. 4.Apply min. 2 coats with the intercoat interval of 6-8 hrs. PRODUCT SPECIFICATIONS: Application - Brush, Roller Mixing Ratio - As Directed on Packing Port Life - 30 Mins. Drying Time - Touch Dry- 30 Min, Hard Dry 6 Hrs. - Intercoat Interval 6-8 Hrs. Min. - Dry Film Thickness 125-150 Microns/per coat - depending on porosity Covering Capacity - 6-8 sq.met/kg per coat depending on porosity, roughness & method of application. Color Shades - All Standard Shades RECOMMENDED USES: 1) Food & Pharmaceutical 2) Work Shop 3) Clean Room Application 4) Chemical Resistant Coating for Concrete& Steel 5) Petrochemical, Fertilizer plants METHOD OF APPLICATION: SURFACE PREPARATION The long-term durability of the applied Epoxy coating (HYB) epoxy coating is dependent on the adhesion between sub-base and coating material. It is most important therefore, that the substrate surfaces are correctly prepared prior to application. 1.Before application of the Epoxy coating (HYB) surface should be free from loose partials, rust, oils, grease or earlier coatings and should be totally dry. 2.New concrete or cementations surface should be placed at least 28 days and have a moisture content of less than 5% before application of Epoxy coating (HYB) 3.After surface is dry, all repair work like sealing of joints, cracks filling of cavities and crevices should be carried out. HEALTH & SAFETY - Keep the containers tightly closed when not in use. Avoid contact with skin & eyes. It comes in contact with the body, wash affected parts with plenty of water and contact a doctor. Other known sector for Epoxy floor lining, Epoxy garage floor lining, Concrete epoxy lining, Concrete floor epoxy lining, Epoxy pipe lining, Marine epoxy lining, Sub marine epoxy lining, Basement lining epoxy floor shield, Louisiana, Oregon, Chip lining color epoxy floor, Aviation lining epoxy interior.

Bitumen Product Description : Bitumen is widely used in the construction of asphalt roads and bituminous membrane products. Bitumen is commonly used to build highways, motorways and rail networks. Bitumen has excellent water-proofing properties and is widely used for making roofing products along with a range of other household and industrial applications, from emulsion paints to sound-proofing. Penetration Bitumen and Bitumen Emulsions are used for the construction of railway tracks and by using special types of bitumen such as Polymer Modified Bitumen, the vibration and noise levels are reduced due to a dampening effect. Bitumen has been proven to be effective on both high-speed railway tracks and heavy load railway tracks. Bitumen is also used for surfacing airfield runways and air strips (PMB is preffered due to its fuel resistant properties) and taxi ways. For the Marine construction industry bitumen is used for hydraulic applications such as canal lining, underwater tunnels, river bank protection, dam construction and sea defences. There are also numerous industrial applications like roofing felt material, printing inks, packaging paper, linoleum, electrical cable / Junction box insulation, mastic for roofing of terraces, and duplex paper manufacture. Price of product ( USD price or FOB price) : 3.000 MT monthly market price. 10.000 MT monthly market price Less 5%. Product origin : Russia and Non Russia Key Specifications/Special Features : Specifications for types/grades of Oil Bitumen according to buyer specifications and/or will be given upon received buyer credible purchase request in the form LOI/ICPO docs. Minimum Order Size and Packgaing details : MOQ 3000 MT Bulk in tanker vessels. Drums 150/180/200 Kg. Jumbo bags 1000 Kg. Poly bags 32 Kg. Tanks 20 MT.

We deals in the following products :- 1) PVC Resin 2) Caustic Soda Flakes

Crystals Benzoin Siam Crystals

We are supplier and exporter of Ferro Silicon. Ferro silicon Specs: Si:75%min. and Si:72%min. C:0.2%max. S:0.02%max. P:0.04%max. Al:2.0%max.1.5%max.and 1.0%max .Commodity: Ferro Silicon Low Al Specs: Si:75%min. C:0.2%max. S:0.02%max. P:0.04%max.Al:0.1%max.0.3%max.and0.5%max. In 1mt plastic woven bags. Ferro Silicon Ferro Silicon has a melting point of 1200�?�°C to 1250�?�°C with a boiling point of 2355�?�°C and Ferro Silicon contains about 2% of calcium and alluminium. Ferro Silicon, as an additive to the production process of ferrous metals, will impart several desirable properties upon the resultant alloy. Some of the primary benefits of adding Ferro Silicon to an alloy is to improve the corrosion resistant properties of the new compound, as well as to add to the high temperature heat- resistance properties of the new alloy, for example, in the production of silicon steel for use in transformer cores.

Bitumen Primer * Bitumen Primer is Bituminous air curing ready mixed Acid & Alkali resistant special primer. Application * Concrete surface must be clean, dry and rough. No primer should be applied over smooth and wet surface. * After cleaning the concrete surface, one coat of Bitumen Primer should be applied with brush and allow to dry thoroughly. * The drying time will depend upon the temperature. * 24 Month at the temperature 30C (+2OC) Packing * Bitumen Primer: 25 Liter Drum Note * Bitumen Primer contains volatile and slightly toxic solvent. Keep away from spark and open flames at working area. * Bitumen premier it is manufactured using bitumen solution which is used for sealing of prime porous and non-porous surface, and also to protect residential and commercial building. * Bitumen Primer is used to protect substrate against corrosive attack, is suggested to apply anti-corrosive primer.It is best for protection against sub-striate against atmospheric corrosion and chemical corrosion. It is a mixed substance made up of organic liquids that are highly sticky, water proof, viscous,acid proof as with all surface coating, good Bitumen Premier is used for long life of the system. it is applied by brush or roller and allowed to dry before any water proofing treatment so to avoid solvent it is used in defects such as cracks, broken mortar joints, etc. are to be repaired prior to Bitumen primer application. Product Details: Grade Standard Technical Grade Physical State - Liquid Usage - Industrial Color - Black Characteristics: Appearance/Color - Pasty liquid/ black Chemical Base - Bituminous rubber emulsion. Density - 1.0 kg/l Curing Speed/ Rate - 3 - 4 hours Tack free after - 5 - 10 hours Cured after - 2 - 4 days (Dependent on ambient Solid Content by - temperature, substrate temperature, Weight - relative Water Content by weight - humidity and thickness of the coating) Bitumen Content - 41% by weight - Thixotropic (The viscosity can be adjusted by - Viscosity adding up to max. 5% of clean water. - Stir well prior use) - For light protection: 1.0 mm min. Coating - For greater protection: ~ 1.5 - 2.0 mm Thickness applied - in two coats. Water Penetration - 48 h, 1 bar: 78.5 cm2: 0 ml under Hydrostatic - 96 h, 4 bar: 78.5 cm2: 33 ml Pressure - Water vapor 6 x 10-7 mg / hmPa Permeability Service - -30 C to 200 C Temperature - Adhesion Concrete - Very good, Timber: Very good, Metal: Moderate Glass: Poor

APPLICATION OF SK-HB K-SILICATE MORTAR : * K-SILICATE is used for jointing Acid Resisting brick in construction of vessels in suited for construction of fume chambers and stacks handling hot, dry Acid fumes and vapors. It is also used for jointing chemical resisting stoneware pipes. K-SILICATE cement is good bedding material for Acid â?? Resisting bricks and tiles. The concrete surface needed protection should be dryed, clean and rough. The bricks or tiles will be set with K-SILICATE cement over concrete surface applied with a suitable an impermeable interliner. When Bedding and Jointing Materials are the same. On the treated surface bricks or tiles are bedded to a thickness of about 6 mm and tamp gently with a wooden piece till the paste squeezes out of joints. The paste that is squeezed out of the joint should be removed by trowel with good finishing. After the mortar of the joint is dryed treat the joints with 20% Hydrochloric Acid Solution by means of brush. A.R.lining should be always in contact with Acid and not with water. Concrete subtract like Floor, Wall, tanks and similar surface should be protected with a membrane of Bitrok Mastic or compound steel tanks should be protected with rubber or PVC subjected to chemical conditions and temperature of chemical media. The Brick lining is recommended over the protective layer of Bitrok Mastic. When Bedding and Jointing Materials are Different. Spread the silicate type mortar about 6 to 8 mm thick on the back of the tile or brick. Press the tile on the bed leaving required space for joints between tiles for bricks. After the bedding mortar is set, fill Mp the joints with specified cement.PRODUCT DATA SHEET FOR SK-HB ( K-SILICATE) MORTAR A general purpose cement for acid conditions Resistant to High & medium concentrations of most of the common organic and inorganic acids except Hydroflouric acid. Recommended where the concentration of the acid is high suitable for high temperature. Unsuited to aqueous solutions, alkaline conditions. PREPARATIONS OF MORTAR : * Measure 1 part by weight of K-SILICATE solution into a suitable mixing pan. * Add slowly and gradually 3 parts by weight K-SILICATE mortar and mix thoroughly to form a smooth mortar. * In hot season very large batches of mortar will become stiff quite rapidly therefore small batches, not exceeding 4 to 8 kgs. Will be prepared. * The cement mortar will be used before it starts setting.