The acid fluxes (peony welding sj501) contain substantial amounts of silica, silicates in the form of calcium and/or manganese silicate and manganese oxide. These fluxes react with the weld pool and will raise both silicon and manganese content of the weld together with a high oxygen content. The result of this is that the toughness of the weld is poor but the fluxes will tolerate rusty surfaces, will detach easily and give a good weld appearance. They are especially useful for single pass high speed welding such as fillet welding of web to flange girder joints.
Submerged arc welding welding flux lj-sj501 sintered flux Lj-sj501 welding flux aws a 5.17 f6a0-el12 soldering flux f7a2-em12k Flux type: aluminum-rutile Basicity index: 0.5-0.8 Remark: 1.Before welding, fluxes should be baked for two hours at 300-350ºc. 2.Removal of rust, oil, dirt, water, impurities, etc in welding areas. Packing: 25kg/bag, pallets are available. Lead time: 2 weeks Performance: vrey good weld bead appearance, excellent slag removal with narrow groove and fillet welds. High resistance to cracking and porosity and insensitive to oil, rust, scale and dirt on the surface to be welded. Applications: used for ordinary carbon steel, low alloy structure and boiler quality steel and high speed welding. Contact: miss helen duan Tel/fax: 0086-532-85641729 25kg/bag
Submerged arc welding welding flux lj-sj501 sintered flux Lj-sj501 welding flux aws a 5.17 f6a0-el12 soldering flux f7a2-em12k Flux type: aluminum-rutile Basicity index: 0.5-0.8 Remark: 1.Before welding, fluxes should be baked for two hours at 300-350ºc. 2.Removal of rust, oil, dirt, water, impurities, etc in welding areas. Packing: 25kg/bag, pallets are available. Lead time: 2 weeks Performance: vrey good weld bead appearance, excellent slag removal with narrow groove and fillet welds. High resistance to cracking and porosity and insensitive to oil, rust, scale and dirt on the surface to be welded. Applications: used for ordinary carbon steel, low alloy structure and boiler quality steel and high speed welding. Contact: miss helen duan Tel/fax: 0086-532-85641729 Packing: 25kg/bag, pallets are available.
Buy Copper Alloy Submerged Arc Welding Flux and Wire. Submerged Arc Welding Flux and Wire is a professional grade welding flux and wire. It is designed to help you weld faster and easier.
Name: Agglomerated submerged arc welding flux SJ101 AWS: AWS/ASME SFA-5.17 F6A0-EL8 F7A2-EM12K F7A4-EH14 SAW wires: EL8, EM12K, EH14, etc. Power supply: DC (DCEP), AC Basicity: 1.8 BIIW Grain size: 10-60 mesh (0.28-2.0mm) Alloy transfer: nearly no transfer of Mn, Si to weld metal Category: submerged arc welding mild steel & low-alloy steel Industry: structural steel, pressure vessel, bridge building, ship building, pipeline, heavy equipment, spiral pipe mills, etc. Description: fluoride based agglomerated flux. Granular size 10-60 mesh (0.28-2.0mm). Easy slag removal. Excellent mechanical properties. Smooth welding pass. Widely used for API grade X60, X65, X70 pipeline construction. Low diffusible hydrogen content (¡Ü50ml/100g) in weld metal gives it high toughness and high cracking resistance at low temperature. Package: damp-proof packing, 25kg/bag Certification: ABS, CCS, LR Attention: 1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. As to welding, individual test results may vary depending on experience & technique, flux type, base metal, joint preparation, flux preparation, ampere, voltage, etc. 2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350¡æ for 2 hours before usage. 3. Please clean the rust, oil, water on base metal before welding. 4. Add minumum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties. 5. Please control parameters properly, like preheat temperature, interpass temperature, cooling rate. 25KG/BAG
We have the largest automated factory in northern China.The annual production capacity of welding wire is 300,000 tons.There are varieties such as ER70S-G, ER70S-3, ER70S-4, ER70S-6, ER70S-6N, ER70S-8, ER90S-G, ER100S-G, ER110S-G, etc. The companya's products have successively passed the certifications of EU CE and ABS, CCS, LR, DNV, GL, KR, and NK classification societies. I can give you the best quotation. You can send me the specifications and Datasheet of the products you need.
Supplier: Submerged ARC welding flux, wire and electrodes
Supplier: Submerged ARC welding flux, welding flux, welding wire, saw flux
Supplier: Welding flux, submerged arc welding flux, sub arc flux, saw welding flux, agglomerated flux, fused flux