Name: Agglomerated submerged arc welding flux SJ101
AWS: AWS/ASME SFA-5.17 F6A0-EL8 F7A2-EM12K F7A4-EH14
SAW wires: EL8, EM12K, EH14, etc.
Power supply: DC (DCEP), AC
Basicity: 1.8 BIIW
Grain size: 10-60 mesh (0.28-2.0mm)
Alloy transfer: nearly no transfer of Mn, Si to weld metal
Category: submerged arc welding mild steel & low-alloy steel
Industry: structural steel, pressure vessel, bridge building, ship building, pipeline, heavy equipment, spiral pipe mills, etc.
Description: fluoride based agglomerated flux. Granular size 10-60 mesh (0.28-2.0mm). Easy slag removal. Excellent mechanical properties. Smooth welding pass. Widely used for API grade X60, X65, X70 pipeline construction. Low diffusible hydrogen content (¡Ü50ml/100g) in weld metal gives it high toughness and high cracking resistance at low temperature.
Package: damp-proof packing, 25kg/bag
Certification: ABS, CCS, LR
Attention:
1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. As to welding, individual test results may vary depending on experience & technique, flux type, base metal, joint preparation,
flux preparation, ampere, voltage, etc.
2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350¡æ for 2 hours before usage.
3. Please clean the rust, oil, water on base metal before welding.
4. Add minumum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties.
5. Please control parameters properly, like preheat temperature, interpass temperature, cooling rate.
25KG/BAG
Stringent Quality Controls measures are adopted to ensure that welding wires are perfectly manufactured as per International Standards. ISO Quality Management system has been implemented as a result of which all products are of World-class Competence. Continuous efforts in the field of research and development are carried out so as to introduce new welding products and offer better services to all our customers. Special Jumbo Spools and Drums have been developed for specific applications / SPM's. The Steel Bobbins are supplied as per Customer Specification and Schedules. Regular feedback is recorded and necessary corrective actions are taken in case of any complaints/suggestions received. Emphasis on Product & Quality up gradation has been a constant endeavour. Welding Wires are uniformly and carefully Copper Coated. The coating thickness is maintained at optimum level so that fumes have minimum Copper. This is to protect welder's health and environment. Efforts are now focused to produce Copper Free Welding Wires.
Welding flux
Nova supply and distribute welding flux commonly used for steel structure construction, shipyard, offshore facilities, bridge construction, and automobile manufacturing.
Neutral fluxes(peony welding sj301)are designed to have little or no effect on the chemical analysis of the weld metal and therefore on the mechanical properties. They contain low silica, calcium silicate and alumina and do not add significant amounts of silicon and manganese to the weld.
1. Specification conformance Aws a5.20 e71t-1 gb/t10045-2001 e501t-1 / jis z3313 / yfw c50dr 2.Description Aws a5.20e71t-1 is a kind of ti type flux cored wire for co2 welding , it has high cladding efficiency, good welding technical performance in all-position welding, apply for low carbon steel and 500mpa grade strength steel welding, such as ships, pressure vessels, mechanical equipments and bridges. 3. Chemical composition of deposited metal (%) C161;¨¹0.18, mn161;¨¹1.75, si161;¨¹0.90, p161;¨¹0.03, s161;¨¹0.03, cr161;¨¹0.20, ni161;¨¹0.50, mo161;¨¹0.30, v161;¨¹0.08, cu161;¨¹0.35 4.Mechanical properties of deposited metal Yield point480 mpa, tensilestrength400 mpa, Elongation22%, test temp -20161;227;c, impact energy 27 j 5. Available diameter 0.8mm/0.9mm/1.0mm/1.2mm/1.4mm/1.6mm
Detailed product description of flux cored welding wire: Features: flux cored welding wire is available for both mild steel and stainless steel gas metal arc welding. A flux cored welding wire is a tubular wire with a metallic powder flux inside. The primary advantage to flux cored welding wire over gmaw or stick welding is higher deposition rates, deeper penetration, improved bead appearance and is more cost effective Packing: 15kg/vacuum aluminum foil bag Certificates: abs ccs dnv lr gl kr nk, iso9001:2000, and so on; Specification: 1.0mm, 1.2mm, 1.6mm. Packing:5kg, 10kg, 15kg or 20kg packed in plastic spool;5kg, 15kg in iron wire spool; 250kg and 350kg in drum. Packing: black good plastic spool, precisely winding, with water-proof paper, wrapped by plastic film and silica gel, and then a white neutral carton box, at last by pallet;
The flux-cored welding wire is intended to inert-gas shielded fusion welding of titanium and its alloys and includes a metal coating or tubular casting of titanium or its alloys and a powder flux core containing (per cent by weight): Baf2 -- 5 to 10, Fluoride of a rare-earth element -- 18 to 20, Caf2 -- 40 to 50, Srf2 -- the rest, The ratio of the weight content of the powder flux to the total weight content of titanium in the wire being from 0.3: 1 to 1: 1.
Nova supply and distribute Flux cored welding wire commonly used for steel structure construction, shipyard, offshore facilities, bridge construction, and automobile manufacturing.
1. Welding Wire for flux welding OE SD3 1NI 1/2 MO - (Air Liquide)-(2,4mm) - 316260kg 2. Welding Wire OK ARISTROD 13.08 - (ESAB) - (1mm) - 93060kg 3. Welding Wire OK AUTROD 12.66 - (ESAB) - (1mm) - 143265kg 4. Welding Wire (Hollow) with flux filling OK TUBROD 15.19 - (ESAB) - (1,2mm) - 3180kg 5. Welding Wire for flux welding OE TIBOR 33 - (Air Liquide) - (3,2mm) - 13108kg 6. Welding Electrode P 65 MR - (Air Liquide) - (3,2mm) - 270kg 7. Flux OP 132 - (Oerlikon) - 539425kg 8. Abrasive Grit - (Winoa) - 82725kg