BP series is specially designed for adhesives application. Characterised by lighter colour, less odour as well as wider compatibility and solubility, they are more suitable for hot melt adhesives, bookbinding, shoes adhesive and solvent adhesives etc.
C9 aromatic hydrocarbon resin is a petroleum by-product of pyrolysis C9 fraction which is produced by pre-treatment, polymerization and distillation processes. It is not a high polymer but a low polymer molecular weight between 300-3000. Light colored granule, low acid value, good miscibility, water,ethanol and chemical resistance, the chemical stability against acid, the good adjustment of viscosity and thermal stability. Generally, C9 aromatic hydrocarbon resin is not used alone, but as promoters, regulators, modifiers used with other resin. Applications: A. Paints Industry: In paint industry mainly use the high softening point of C9 aromatic hydrocarbon resin which can increase the gloss of paint and improve the adhesion, the hardness and the resistance ability of ac id and alkali. B. Tire and Rubber Industry: Natural rubber particles, and little affect on rubber vulcanization. Adding in rubber and tires, C9 aromatic hydrocarbon resin can increase the adhesion and the reinforcement and can also play as softener. C. Adhesives Industry: C9 aromatic hydrocarbon resin has good adhesion, added in the process of producing adhesives and pressure-sensitive adhesives can improve the adhesive bond strength, acid resistance, alkali resistance and water resistance, and also can reduce production costs effectively. D. Ink Industry: In ink industry, mainly use the high softening point of C9 aromatic hydrocarbon resin which can reach the effect of show color, quick-drying and brightening and improve printing performance, etc. F. Others, C9 aromatic hydrocarbon resin has unsaturated certain characteristic, can be used as paper glue, plastic modifier etc.
Products Specification� Property Test Method and Unit Specification Range Softening Point Ring&Ball,°C 90-150 Color Gardner,50%Toluene Solution 3-20 Acid Value mgKOH/g 0.5 max Ash Content wt.% 0.5 max Applications: A. Paints Industry: In paint industry mainly use the high softening point of C9 aromatic hydrocarbon resin which can increase the gloss of paint and improve the adhesion, the hardness and the resistance ability of ac id and alkali. B. Tire and Rubber Industry: Natural rubber particles, and little affect on rubber vulcanization. Adding in rubber and tires, C9 aromatic hydrocarbon resin can increase the adhesion and the reinforcement and can also play as softener. C. Adhesives Industry: C9 aromatic hydrocarbon resin  has good adhesion, added in the process of producing adhesives and pressure-sensitive adhesives can improve the adhesive bond strength, acid resistance, alkali resistance and water resistance, and also can reduce production costs effectively. D. Ink Industry: In ink industry, mainly use the high softening point of C9 aromatic hydrocarbon resin which can reach the effect of show color, quick-drying and brightening and improve printing performance, etc. E. others, C9 aromatic hydrocarbon resin has unsaturated certain characteristic, can be used as paper glue, plastic modifier etc Resins Characters: C9 aromatic hydrocarbon resin is a petroleum by-product of pyrolysis C9 fraction which is produced by pre-treatment, polymerization and distillation processes. It is not a high polymer but a low polymer molecular weight between 300-3000. �Light colored granule �low acid value, good miscibility, water,ethanol and chemical resistance, the chemical stability against acid, the good adjustment of viscosity and thermal stability. �Generally, C9 aromatic hydrocarbon resin is not used alone, but as promoters, regulators, modifiers used with other resin.
C9 petroleum resin is a petroleum by-product of pyrolysis c9 fraction which is produced by pre-treatment, polymerization and distillation processes. It is not a high polymer but a low polymer molecular weight between 300-3000. C9 petroleum resin resin has light colored granule C9 petroleum resin resin has low acid value, good miscibility, water, ethanol and chemical resistance, the chemical stability against acid, the good adjustment of viscosity and thermal stability. Generally, c9 petroleum resin resin is not used alone, but as promoters, regulators, modifiers used with other resin. Applications: A. C9 petroleum resin resin used in paints industry: in paint industry mainly use the high softening point of c9 aromatic hydrocarbon resin which can increase the gloss of paint and improve the adhesion, the hardness and the resistance ability of ac id and alkali. B. C9 petroleum resin resin used in tire and rubber industry: Natural rubber particles, and little affect on rubber vulcanization. Adding in rubber and tires, c9 aromatic hydrocarbon resin can increase the adhesion and the reinforcement and can also play as softener. C. C9 petroleum resin used in adhesives industry: C9 petroleum resin resin has good adhesion, added in the process of producing adhesives and pressure-sensitive adhesives can improve the adhesive bond strength, acid resistance, alkali resistance and water resistance, and also can reduce production costs effectively. D. C9 petroleum resin used in ink industry:
water white to yellowish hydrocarbon resin, C5, C9 and modified hydrocarbon resin.
hydrogenated C9 hydrocarbon resin which compete and substitute C5 resin in Hot Melt Adhesive and Road marking paint
High compatibility c9 aromatic hydrocarbon petroleum resin for hot melt adhesive Quick detail: Hsu™ hs110-4 is c9 aromatic hydrocarbon petroleum resin. Description: Hsu™ hs110-4 is a low odor, light color thermoplastic hydrocarbon resin produced from purified aromatic petroleum-derived monomers with a naphthalene elimination process. It is characterized by low odor and high level compatibility. It is compatible with many resins, mineral oils and polymers. Good compatibility with major solvents in industrial paints and adhesives. It is mainly used in industrial paints and adhesives. High compatibility c9 hydrocarbon resin Applications: Wood working adhesive, hot melt adhesives, rubber compounding. High compatibility c9 hydrocarbon resinhigh compatibility c9 hydrocarbon resin High compatibility c9 hydrocarbon resin Specifications: Grade no. Hsu™ hs110-4 Softening point(°c) 110±5 Color g# 4# max Acid value(mg koh/g) max. 0.3 Competitive advantage: • excellent compatibility with various base polymers • good chemical stability • high heat resistance and water resistance • excellent tack and peel properties • low volatility and low odor Packaging & shipping 1. Packed in 25kg paper bag, pp bag or paper and pp compounding bag 17 mt without pallets or 14.5mt with pallets for 1*20fc Also can use 750kg container sack, 15mt with pallets for 1*20 fcl. 2. Payment: irrevocable l/c at sight, or 30%t/t in advance 3. Shipment: in 20 days after 30% t/t deposit High compatibility c9 hydrocarbon resin Storage & protection They are non-hazardous product, it should be stored in dry and cool place with fire fighting facilities. Far away from fire, sunshine, moisture and pollution.
Gd-dh series hydrocarbon resin is water white dcpd hydrogenated hydrocarbon resin derived from cyclic ingredients. Dcpd hydrogenated petroleum resin is designated to tackify for a variety of adhesive polymers including eva, sis, hma, hmpsa, sbpsa. Soluble in most aliphatic and aromatic and chlorinated hydrocarbons. Insoluble in alcohols and water. Application: Adhesive, hot melt pressure sensitive adhesive, solvent-borne adhesive, rubber, varnish, coating etc.
Resins characters: Â?¢light colored and transparent granule Â?¢applied in tyre rubber compounding, which have an excellent compatibility with a wide variety of elastomers including natural rubber (nr), synthetic rubber, polyethylene, polypropylene, styrene-isoprene-styrene (sis), styrene-ethylene-butadiene-styrene (sebs) and ethylene vinyl acetate (eva), and also have a good compatibility with the natural sticky resins (such as terpene, rosin and thereof derivatives). Additionally, the product can be used in rubber compounding as tackifier agent, reinforcement agent, softening agent as well as the filling agent, etc. Â?¢excellent stickiness property. Â?¢has a good softening and reinforcement properties in rubber mixing process, can enhance the ductility and peel resistance of rubber compounding. Â?¢can improve the stickiness of raw rubber, without effecting the curing time and cured property of rubber compounding. Â?¢.Avoiding the sticky problem to rubber processing machines. Â?¢contributes to a uniform dispersion of filler material in rubber compounding. Application: Rubber industry, tyre industry
Resins characters: Light colored and transparent granule Make the initial adhesion performance; cohesive strength and peel strength reach the best balance Super aging resistance performance Good fluidity which can improve the wetting property of master material. Narrow molecular weight distribution Low volatility and no odor Excellent compatibility with cinnamene copolymers (such as sis, sbs, sebs and seps), nr, sbr, eva and natural sticky resins(such as terpene, gum resin and its ramification). Application: Hot melt adhesive, solventborne adhesive, pressure sensitive adhesive, rubber compounding, tyre.
Description: This kind of c5 aliphatic hydrocarbon resin is applicable for hot melt road paint, which can enhance the tenacity, hardness and adhesive force of the paint, then form smooth paint surface, and could keep its stability in different temperatures of seasons by adding auxiliary agent. Resins characters: Pale yellow thermoplastic granule resin. Better compatibility with gum resin. Good fluidity Make the filler dispersed uniformly and no sedimentation High anti-abrasion Promote fast drying speed of paint Increase paint's strong dirt-resistant Application: Hot melt road marking paint
Resins character: 59c series copolymerized hydrocarbon resins are thermoplastic resins, c5, c9 fraction of petroleum by-product of decomposition with processing pre-treatment, polymerization and distillation. Â?¢59c series copolymerized hydrocarbon resins have advantages both of c5 and c9 petroleum resins: Â?¢low acid value, good miscibility, waterproof, ethanol resistance and chemical resistance and other characteristics of acid resistance, chemical stability in acid-bases, adjustment in viscosity, good thermal stability, weather resistance and light aging resistance because of non-polar groups in its structure. Â?¢59c series copolymerized hydrocarbon resins has good solubility in organic solvents especially in oil solvent, as well as good compatibility with other resins. It also has brittle, increasing viscosity, cohesiveness and plasticity. Â?¢generally, they are not used alone, but used as accelerant , regulator and modifier together with other resins. Applications: A. 59c series copolymerized hydrocarbon resins can be used in hot melt adhesives, pressure sensitive adhesive and so on in adhesives industry. In adhesives industry, 59c series copolymerized hydrocarbon resins can not only provide better initial cohesiveness, but can also be used like rosin resins to adjust and improve viscosity durability and strength of mixture of glue and resins. B. Especially in radial tire with the effects of not only increasing adhesion between particles but also improving adhesion between particles and cord; C. Paint industry D. Ink industry E. Rubber and tyre industry
Color is light, heat resistance, weather resistance, low softening point, and nonpolar polymer compatibility, and polar polymer incompatible. Small tank 10 tray 15 dollars/ton Twenty tray thirty dollars Big tank and a tray $15 Forty tray thirty dollars Add double plate ten dollars
C9 aromatic hydrocarbon resin, C5 aliphatic hydrocarbon resin, C5/C9 copolymerized hydrocarbon resin, C5 hydrogenated hydrocarbon resin, C9 hydrogenated hydrocarbon resin, DCPD hydrocarbon resin and DCPD hydrogenated hydrocarbon resin.
59C Series Copolymerized hydrocarbon Resins are thermoplastic resins, C5, C9 fraction of petroleum by-product of decomposition with processing pre-treatment, polymerization and distillation. 59C Series Copolymerized hydrocarbon Resins have advantages both of C5 and C9 petroleum resins: Low acid value, good miscibility, waterproof, ethanol resistance and chemical resistance and other characteristics of acid resistance, chemical stability in acid-bases, adjustment in viscosity, good thermal stability, weather resistance and light aging resistance because of non-polar groups in its structure. 59C Series Copolymerized hydrocarbon Resins has good solubility in organic solvents especially in oil solvent, as well as good compatibility with other resins. It also has brittle, increasing viscosity, cohesiveness and plasticity. Generally, they are not used alone, but used as accelerant , regulator and modifier together with other resins. Applications: A. 59C Series Copolymerized hydrocarbon Resins can be used in hot melt adhesives, pressure sensitive adhesive and so on in adhesives industry . In adhesives Industry, 59C Series Copolymerized hydrocarbon Resins can not only provide better initial cohesiveness, but can also be used like rosin resins to adjust and improve viscosity durability and strength of mixture of glue and resins. B. Especially in radial tire with the effects of not only increasing adhesion between particles but also improving adhesion between particles and cord.
C5 aliphatic hydrocarbon resin, C9 aromatic hydrocarbon resin, C5/C9 copolymerized hydrocarbon resin.
Specification: Softening Point()ï¼? 80-90 90-100 100-110 110-120 Color(Gardner in 50% toluene),â?¤ 8-18 8-18 8-18 8-18 Ash(%),â?¤ 0.08 0.08 0.08 0.08 Acidity(mgKOH/mg),â?¤ 0.6 0.6 0.6 0.6 Recommended Application Adhesive Paint, Tyre Rubber Adhesive, Tire Rubber Adhesive, Tyre Rubber Application: 1. Used in Hot melt adhesive(HMA) and Solvent based adhesive(SBA) as tackifier resin 2. Solvent based paint 3. Printing Ink 4. Rubber Compounding 5. Asphalt emulsion mixtures Any inquiry, pls contact sofia.chu(at)zzdenglan.com freely.
DATA SHEET FOR EPOXY EPOXY COATING :- INTRODUCTION - EPOXY COATING (HYB) is a two part high solids solvent free epoxy phenolic resin based coating system designed for hard wearing, smooth surface finish for floors, walls and on steel structures. Nonskid surface finish can be achieved on floor, if required. FEATURES: 1) Hard Wearing 2) Non Dusting 3) Excellent Surface Finish 4) Non Smelling 5) Good Aesthetics 6) Highly Chemical Resistant APPLICATION: 1.Stir well before mixing Part A and Part B and mix in the prescribed ratio. 2.Apply one coat of EPOXY primer on the clean and dry surface. 3.EPOXY COATING (HYB) should be applied on the surface by brush or roller within 24 hrs. After application of primer coat it should be allowed to air dry for min. 4 hrs. Preferable in a dust free atmosphere. 4.Apply min. 2 coats with the intercoat interval of 6-8 hrs. PRODUCT SPECIFICATIONS: Application - Brush, Roller Mixing Ratio - As Directed on Packing Port Life - 30 Mins. Drying Time - Touch Dry- 30 Min, Hard Dry 6 Hrs. - Intercoat Interval 6-8 Hrs. Min. - Dry Film Thickness 125-150 Microns/per coat - depending on porosity Covering Capacity - 6-8 sq.met/kg per coat depending on porosity, roughness & method of application. Color Shades - All Standard Shades RECOMMENDED USES: 1) Food & Pharmaceutical 2) Work Shop 3) Clean Room Application 4) Chemical Resistant Coating for Concrete& Steel 5) Petrochemical, Fertilizer plants METHOD OF APPLICATION: SURFACE PREPARATION The long-term durability of the applied Epoxy coating (HYB) epoxy coating is dependent on the adhesion between sub-base and coating material. It is most important therefore, that the substrate surfaces are correctly prepared prior to application. 1.Before application of the Epoxy coating (HYB) surface should be free from loose partials, rust, oils, grease or earlier coatings and should be totally dry. 2.New concrete or cementations surface should be placed at least 28 days and have a moisture content of less than 5% before application of Epoxy coating (HYB) 3.After surface is dry, all repair work like sealing of joints, cracks filling of cavities and crevices should be carried out. HEALTH & SAFETY - Keep the containers tightly closed when not in use. Avoid contact with skin & eyes. It comes in contact with the body, wash affected parts with plenty of water and contact a doctor. Other known sector for Epoxy floor lining, Epoxy garage floor lining, Concrete epoxy lining, Concrete floor epoxy lining, Epoxy pipe lining, Marine epoxy lining, Sub marine epoxy lining, Basement lining epoxy floor shield, Louisiana, Oregon, Chip lining color epoxy floor, Aviation lining epoxy interior.