Foundry Pig Iron is suitable for iron castings used in general engineering, machine
tools and parts for the automotive industry. Due to the high proportion of iron ore
used in the production of Foundry Pig Iron, the formation of pearlite in the finished
casting is promoted. This effect is enhanced when more than 10% of Pig Iron per
charge is used.
The use of Foundry Pig Iron promotes graphite formation, reduces primary chill and
improves machinability, particularly important in thin-walled castings The use of costly chill reducing inoculants can be minimised through increased addi-
tions of Foundry Pig Iron.
The high density and high carbon content of Foundry Pig Iron improves melting rates
or reduces energy consumption. In an electric induction furnace savings can be as
high as 50 kWh/t of molten metal. In a cupola furnace savings of up to 50 kg coke/t
of molten metal can be achieved.
The higher bulk density of pig iron relative to scrap means lower storage space re-
quirements, less handling during charge make-up, fewer charge buckets and lower
charging time.
â?¢ The lower surface area : volume ratio relative to scrap means lower oxide (rust) for-
mation and thus lower slag volume.
The carbon content is chemically combined and thus goes into solution more quickly
with lower energy requirement than when adding a recarburiser to scrap
Weight of each sheet: 125kgs /- 1%
Net weight of each pallet: 2M/T /- 1%
Min. weighs in each container: 20 M/T appr
Gross weight of each container: 22.2M/T appr.
Galvanized pipes are more preferred pipes than other pipe types because they are stainless. Galvanized pipe is widely used in indoor and outdoor applications due to its stainless structure. The fact that steel pipes become unusable by rusting causes both material loss and environmental pollution. Pipes such as water pipes to be used in greenhouses should not be corroded or rusted. Rust contaminating the water to be transported adversely affects the growth of plants. Rusting of these pipes is harmful to human health. Therefore, galvanized pipes are preferred especially in pipes where fresh water passes. As a structure, galvanized pipes are more robust than other pipes. The protective layer on the surface of galvanized pipes, which are more resistant to external factors, prevents the pipe from being scratched. In order to prevent these situations from occurring, the demand for galvanized pipes has increased. The fact that they provide resistance to temperature changes and humidity has increased their use in greenhouse construction. Galvanized pipe for greenhouse construction is made from plain carbon steel with hot dipped zine coated, low cost made of stainless steel. It is suitable for mechanical processes. Galvanized pipes can be used for many years without any deformation in extreme cold or hot ambient conditions.