Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
13968 Plastic Raw Materials Suppliers
Short on time? Let Plastic Raw Materials sellers contact you.
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Tests Value Unit
Melt Flow Rate (MFR) 3.2 g/10min
Density 0.939 g/cm3
Melting Point 127 C
Tensile Yield Strength 21 Mpa
Tensile Strength at Break 28 Mpa
Elongation at Break 1,100 %
Flexural Modulus 750 Mpa
Brittle Temperature <-60 C
Tests Value Unit
Melt Flow Rate (MFR) 20 g/10min
Density 0.924 g/cm3
Tensile Strength MD12 Mpa
TD 10
Elongation at Yield 13 %
Elongation at Break 200 %
Dark Drop Impact 105 g
Brittle Temperature(F 50) -70 C
Vicat Softening Point 90 C
Tests Value Unit
Melt Flow Rate (MFR) 20 g/10min
Density 0.924 g/cm3
Tensile Strength MD12 Mpa
TD 10
Elongation at Yield 13 %
Elongation at Break 200 %
Dark Drop Impact 105 g
Brittle Temperature(F 50) -70 C
Vicat Softening Point 90 C
End use of Bottle grade chips mainly depends on the Intrinsic Viscosity (IV). PET Chips with IV 0.80 is mainly used for drinking water bottles and mineral water bottles. PET Chips with IV 0.82 is mainly used in making bottles for carbonated beverages, small bottle for edible oil, alcohol, medicines and pet sheets as they need better quality and high finished product rate. PET Chips with IV of 0.85 are mainly used for making huge packing bottles for carbonated beverages and 3-5 gallons water bottles as these bottles should to have great strength and resistance against high pressure. Bottle Grade PET Chips
Features of bottle grade PET Chips are low processing temperature, wide scope in packaging, excellent transparency and high in finished product rate.