Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
MATERIAL : HDPE Film A Grade CATEGORY :HDPE TYPE :Film GRADE :A SPECIFICATION :HDPE has a slight stain on the surface due to the press machine.Has some lables ORIGIN : Japan LOADING WEIGHT : 18-20 Tons CNF (USD/Ton) : " $580 -780 Haiphong $530 - 730 Malaysia "
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
HDPE Film A Grade Plastic Scrap For Sales MATERIAL : HDPE Film A Grade CATEGORY : HDPE TYPE : Film GRADE : A SPECIFICATION : HDPE has a slight stain on the surface due to the press machine. ORIGIN : Japan LOADING WEIGHT : 18-20 Tons CFR (USD/Ton): 550-750 Vietnam
Material: HDPE (High Density Polyethylene) Grade: Blown Film Melt Flow Index: 0.3 to 0.5 g/10min Density: 0.951 g/cm3 Packing: Jumbo Bags on Pallets Loading Port: Jeddah, Saudi Arabia Loading Capacity: 25 to 28 TONS Origin: Saudi Petrochemical Industry
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50°C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 °C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
ITEM - HDPE FILM GRADE (PRIME) MFI - 0.18 g/10 min (190/ 2.16 Kg) ORIGIN - MIDDLE EAST QTY - 200 MT PACKAGING - 25 KG PRINTED BAGS AND PALLETIZED PAYMENT TERM - LC / TT APPLICATION - THIS HIGH MOLECULAR WEIGHT, HEXENE COPOLYMER IS TAILORED FOR BLOWN FILM APPLICATIONS.
We supply only high quality first generation & post Pre-consumer factory virgin plastic, recycled & pelletized in LLDPE, LDPE and HDPE film grades. All our raw materials are sourced from only large plastic convertors First generation & post pre-consumer clean factory virgin plastic Guaranteed. 1) LDPE CLEAR 0.83 USD per/kg virgin clear 2) LDPE SMOKEY 0.72 USD per/kg - very light smokey 3) LDPE SMOKEY 0.70 USD per/kg Standard smokey 4) LDPE BLACK/MIX 0.70 USD per/kg 5) LDPE BLACK 0.72 USD per/kg with 2% masterbatch 6) LDPE COLOURS 0.72 USD per/kg white, blue, ect 2% masterbatch 7) LLDPE CLEAR 0.83 USD per/kg virgin clear 8) LLDPE COLOURS 0.72 USD per/kg 9) HDPE CLEAR 0.83 USD per/kg 10)HDPE COLOURS 0.72 USD per/kg Our high-quality product has been Laboratory tested and approved. Unlike 2nd Grade; 3rd Grade or 4th Grade granules; our HDPE & LDPE Granules are able to produce the highest-grade recycled products. We are also able to tailor the product based on buyer specifications or colour requirements. Request a Lab Report & Video from us or samples to see our Superb product quality we offer. Delivery can be arranged.
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50°C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 °C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.