Item Test Condition Test Method Value Unit MFR 190 C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Tests Value Unit Melt Flow Rate (MFR) 3.2 g/10min Density 0.939 g/cm3 Melting Point 127 C Tensile Yield Strength 21 Mpa Tensile Strength at Break 28 Mpa Elongation at Break 1,100 % Flexural Modulus 750 Mpa Brittle Temperature
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
Hello, We can supply, as much as you want, top quality and clean PET Flakes mix color, hot washed, no caps, no labels, no residue, made in USA. Price: US$540.00 per metric ton FAS Port of Long Beach CA for minimum 4 X 40ft containers. US$585.00 per metric ton FAS Port of Long Beach CA for less than 4 X 40ft containers. Please contact us for your requirements.
Hello, We can supply, as much as you want, top quality and clean PET Flakes mix color (80% green, 20% mix color), hot washed, no caps, no labels, no residue, made in USA. Price: US$540.00 per metric ton FAS Port of Long Beach CA for minimum 4 X 40ft containers.
HMW HDPE drum regrind available. All clean. Post-Industrial. 3-4 40ft containers monthly. US$778.00 per metric ton FAS Cincinnati, OH (USA). 20-22 Metric tons per 40ft HC container.
LDPE Mix Color Chunk/Purge and Regrind. 1x40ft HC container = 18 metric tons (Minimum) - Average 2 containers monthly available for shipment. Melt flow = 0.602. It's a hard scrap from a film line (Post-Industrial). Pricing: - US$325.00 per metric ton (Regrind) FAS Houston Port, TX (USA) - US$225.00 per metric ton (Chunk/Purge) FAS Houston Port, TX (USA)
PET clear thermoformed tray regrind, upto 3% EVOH All Clean / Post Industrial 2 x 40ft containers readily available and ongoing monthly. Approx 16 metric tons per 40ft container. Price: US$217.00 per metric ton ex-warehouse USA.
HDPE Mix Color Pallet Shred Melt flow: 1-4 Shred size: 2" Quantity: 1 x 40ft HC container (18 metric tons approx) Price: US$317.00/MT EXW Houston, TX, USA.
PE/PP mix color floor sweep (natural & blue color) = 6.8 tons PE mix color floor sweep with fillers, color concentrates, etc (Dark & Light colors) = 13.6 tons Minimum quantity: 1 x 40ft HC container (18 tons) - available for shipment in 10 days. Price: US$198.00 / MT Ex-warehouse Houston, TX, USA.