Item Test Condition Test Method Value Unit MFR 190 C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Tests Value Unit Melt Flow Rate (MFR) 3.2 g/10min Density 0.939 g/cm3 Melting Point 127 C Tensile Yield Strength 21 Mpa Tensile Strength at Break 28 Mpa Elongation at Break 1,100 % Flexural Modulus 750 Mpa Brittle Temperature
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
End use of Bottle grade chips mainly depends on the Intrinsic Viscosity (IV). PET Chips with IV 0.80 is mainly used for drinking water bottles and mineral water bottles. PET Chips with IV 0.82 is mainly used in making bottles for carbonated beverages, small bottle for edible oil, alcohol, medicines and pet sheets as they need better quality and high finished product rate. PET Chips with IV of 0.85 are mainly used for making huge packing bottles for carbonated beverages and 3-5 gallons water bottles as these bottles should to have great strength and resistance against high pressure. Bottle Grade PET Chips Features of bottle grade PET Chips are low processing temperature, wide scope in packaging, excellent transparency and high in finished product rate.
PP granules, all colors available. Please contact us for more information
Top quality virgin PET resin bottle grade
Physical Appearance:White powder,non-toxic,odourless. contact us for more details
High Quality Low Contents Of Impact Modifier Plastic Raw Material Nylon Pa6 Granules nylon regind pa6. please contact us for more details
100% biodegradable PBS resin / Polybutylene succinate granules / PBS pellets. Please contact us for more information
100% PLA biodegradable corn starch plastic granules for blowing film. Please contact us for more information