CS-613W is 2-component water-based premium epoxy product. CS-613W as admixtures can improve the properties, particularly in relation to water absorption reduction, toughness enhancement, vibration damping and increase of the bond strength of cement to reinforcements other than being used as admixtures, CS-613W is used partial replacement of fine aggregate, for coating, sealing and repairing concrete and for coating steel reinforcing bars for corrosion protection. AREA OF APPLICATIONS Repair mortar for concrete areas. Industrial flooring. Bonding agent for new to old concrete. As water based primer. Can be applied with damp surface. FEATURE Weatherproof and waterproof of capabilities that help prevent the deterioration of the ground-coat material. Low odor. Washable with water including tools. Best to wash as soon as possible before it hardens.100% water resistant when cured.
CA-010P as a water-based primer in relation to water absorption reduction and increase the bonding strength of cement to reinforcements other than being used as admixtures increase the mechanical properties and the adhesion of the hardened material. AREA OF APPLICATIONS Repair mortar for concrete areas Industrial flooring Bonding agent for new to old concrete Enhance adhesion strength of mortar
DESCRIPTION Bituminous Primer is product containing oxidized bitumen and a mix of technical quick drying solvents. APPLICATION Bituminous Primer is recommended to block the dust and the porosity of concrete surfaces allowing the quick application o f the bituminous polymer membranes, both with flame application and cold bonding with bituminous sealants or with self adhesive membranes.Bituminous Primer allows quick film drying, has an excellent penetration and adhesion to the support for the absence of surface stickiness. INSTRUCTIONS FOR USE Concrete surfaces must be dry, clean and free from oil, dust or release agents. This type of primer is ready for use after mixing it. Bituminous Primer can be either sprayed or applied by means of roller or brush. In case of hot application of membranes with flame, the primer can be used only if surfaces are completely dry. On the contrary, if the surface is damp, it is recommended to use a bituminous primer specific for damp surfaces. The drying time depends on concrete porosity, on the quantity of product applied and on the temperature of both the surface and the environment. Usually the film gets dry after 2-4 hours from the application. The drying time can increase in case of cold temperature and with low a bsorption surfaces. PACKING 5 gallon Bucket SHELF LIFE The product can be stocked in closed buckets and in dry area, far from UV rays for 12 months. TOOL CLEANING After use clean tools with common solvents.
DESCRIPTION CC-600SP is a two component, solvent-free epoxy system with high chemical resistance and high bond strength. The epoxy may be applied as a primer for most high end industrial coatings, like Epoxies, PU. CHARATERISTIC Easy apply Low odor High bond strength Abrasion resistant Chemical resistant APPLICATION Concrete coating Cement
IMPARTIAL ENTERPRISES offer an exclusive range of Men's Leather Causal Coat available in several designs. Men's Leather Coat: Gender : Men Color : All Color Available custom demand Material : Leather(100%Sheep) Technics:Plain Dyed Closure : Button Fit : Regular Sizes: S,M,L,XL Lining: As per custom demand
dysprosium oxide dy2o3 nanopowder 1. Used for making metal dysprosium material, glass, additive of ndfeb permanent magnet; 2. Also used for metal halogen lamp, magneto optical memory materials, yttrium iron or yttrium aluminum garnet, atomic energy industry.
Nanometer lanthanum oxide used in piezoelectric materials, electric materials, thermoelectric materials, magnetic resistance materials, luminescence materials (powder) hydrogen storage materials, optical glass, laser materials, all kinds of alloy materials, preparation of organic chemical products of catalyst, and automobile exhaust catalyst, light conversion agricultural film.
The main USES of nano-cerium oxide are: 1. Cerium oxide is used as a glass additive to absorb ultraviolet and infrared rays and has been used in automobile glass.Not only can prevent ultraviolet ray, also can reduce the temperature inside the car, thereby save air conditioning electricity.2. The application of nano-cerium oxide to automobile exhaust purification catalyst can effectively prevent a large amount of automobile exhaust gas from being discharged into the air.3. Nano cerium oxide has been widely used in polishing materials.4, nanometer cerium oxide can also be used in hydrogen storage material, thermoelectric materials, nano oxide cerium tungsten electrode, ceramic capacitors, piezoelectric
solvent free flooring epoxy system two components used for producing high quality epoxy smooth flooring with high glossy surface. Where it based on epoxy resin and agents which are specially selected for their ability to withstand chemical attack Properties @ 25 c Color: White , grey , all required colors Gloss: Glossy Solid content by (WT): 100 % Mixing Ratio: 4 A : 1 B Specific gravity (mix ): 1. 60 0.03 g/cm3 Pot life: 35 min. Temp. of Application: ( 15 35 ) C Full curing time: 7 days Rate of use: 3 -5 m2/ kg ( depending on surface conditions )
Setapol 260 1C is an elastic coated polyurethane membrane of one component for long-lasting waterproofing.It has hydrophobic resistance to sun and frost while it is breathable with anti-corrosion properties.Setapol 260 1C is ideal for the sealing of roofs , balconies ,rooms , gardens , pots and for the protection of thermal insulation foam polyurethane. It also has coverage of 1.5 - 2.0 kg / m2 in two or three layers.
Setapol 450ML 1C is an elastic paint of aliphatic polyurethane base of a component with good mechanical strength.It has a particularly high resistance to sun and frost.There is also no yellowing on the surface.Setapol 450ML 1C is ideal as a finishing coat resistant to light alloys.
Desnamel Fast Dry is a fast -drying alkydic final coating with good gloss and preservation of hue.It is used as a primer as long as a final coating for steel in a slightly corrosive environment.
Desmopol Topcoat is a semi-acrylic polyurethane coating of two-components aliphatic isocyanate with good gloss .It is used as a final coating for the protection of structural steel in extremely corrosive environment, when light steadiness and preservation of the gloss is required.The minimum heat for drying is -10
Setapol 400ML 1C is an elastic paint of aliphatic polyurethane base of a component with good mechanical strength.There is no yellowing on the surface.Setapol 400ML 1C is ideal as a final sealant on moderate pedestrian traffic surfaces.It has coverage of 0.15 - 0,25 kg / m2 in two or three layers.
Setapol 400ML 1C is an elastic paint of aliphatic polyurethane base of a component with good mechanical strength.There is no yellowing on the surface.Setapol 400ML 1C is ideal as a final sealant on moderate pedestrian traffic surfaces.It has coverage of 0.15 - 0,25 kg / m2 in two or three layers.
Desmalkid Prime is a zinc phosphorus primer with an alkyd base which dries relatively quickly.It is usually used as a general purpose primer for Desmalkid Prime Systems for the protection of steel structures in mild to moderate corrosive atmospheres.
Desnamel 200 is a fast-drying zinc phosphorus primer with an alkyd base.It is an ideal primer to prevent rust in steel.It is also indicated for mechanical parts and where fast drying is required.
Desoprime is an epoxy polyamide primer of two components with zinc phosphate as a preventive dye of the corrosion. When dried completely it creates a rust - resistant ,high strength coating.It is used as an epoxy primer for general use according to the painting instructions.
Desmozinc 500 is an epoxy polyamide primer of two components rich in zinc.When dried completely it creates a high strength coating very weather-resistant.It provides cathodic protection against local mechanical damage.It is used as an epoxy primer according to the painting instructions.
Desmepox 1000 is a two-component epoxy amine coating which when dried produces a coating whith excellent resistance to different chemical substances.It is used as an internal tank coating according to the painting instructions.