Features Of Granulated Blast Furnace Slag (GBFS)
Granulated Blast Furnace Slag or GBFS is formed when Blast Furnace Slag or BFS is successively at a fast rate quenched from the furnace rather than left for cooling. It has a density of about 60% to 70% that of natural sand. This material has a much increased resistance to sulfate attack.
This eventually leads to better performance in countering acids of any type. In GBFS, no type of reaction related to alkali and silica occurs. Also the material provides a huge saving in connection to carbon dioxide emission which is an extra boon. What constitutes GBFS are its properties that consist of durability, appearance, higher ultimate strength than concrete which is made up of Portland cement and high sustainability level of the product made out of this material.
Moisture - 18.2% SiO2 - 32.3% Ai2O3 - 13.6% Fe - 0.71% TiO2 - 0.70% Sulphur - 0.07% CaO - 40.1% MnO - 0.59% MgO - 6.70% We have supply granulated blast furnace slag, if interest kindly please send an inquiry to us.
We can offer Granulated Blast Furnace Slag from India. Cao 32 to 41 SiO2 31 -39 Al2 O3 13- 21 MgO 6 - 11 FeO 4 MnO 2 Moisture Avg 12% maz 20% Glass content 93% max
About THE Product : Blast furnace slag is used in the production of cement (iron Portland and blast furnace cement). Air-cooled blast furnace slag is formed by allowing the molten slag to cool relatively slowly under ambient conditions; final cooling can be accelerated with a water spray. The cooled material is hard and dense, although it can have a vesicular texture with closed pores. After crushing and screening, air-cooled slag can be used in several applications. Granulated slag is formed by quenching molten slag in water to form sand-sized particles of glass. The disordered structure of this glass gives the material moderate hydraulic cementitious properties when very finely ground into granulated blast furnace slag, but if it can access free lime, the granulated blast furnace slag develops strong hydraulic cementitious properties. Pelletized or expanded slag is cooled through a water jet, which leads to rapid steam generation and the development of innumerable vesicles within the slag. The vesicular texture reduces the overall density of the slag and allows for good mechanical binding with hydraulic cement paste. Blast Furance Slag is a nonmetallic co-product which is produced in the process of iron manufacturing, Granulated Blast Furnace Slag is a glassy granular material formed when molten blast furnace slag is rapidly cooled by direct water. Rapid cooling prohibits the formation of crystals and forms glassy, non-metallic, silicates and alumino silicates of calcium. GBFS : (Granulated Blast Furnace Slag) Source : Granulated BF Slag From Gujarat State, India Supply Quantity : 50,000 Metric Tons Per Month Packing: Bulk Parameters (% BY MASS) CaO 30-38 Al2O3 15-20 SiO2 30-40 Glass Content 85-97 MgO 8-11 Fe2O3 0.5-1.5 Moisture 10 MAX Size -5mm Min 95, +5 mm Max 5 Relative Gravity 2.9 Bulk Density(Bagged) 1200 KG/M3
Granulated Blast Furnace Slag(GBFS) We are capable to supply granulated blast furnace slag(GBFS) from India on regular basis as per below mentioned speifications Usage : This product is used in construction projects as a alternate of river sand Interested buyers may please contact us with their serious tarde inquiry. Supply Ability: 50000 Metric Ton/Metric Tons per Month Packaging & Delivery Packaging Details Loose or as required by the buyer Port Chennai
Supplier: Granulated blast furnace slag (gbfs)
Supplier: Fly ash, granulated iron blast furnace slag (gbfs), potassium feldspar , sodium feldspar , stpp sodium tripolyphosphate, zirconium silicates & zirconium flours
GGBFS Ground granulated blast furnace slag (GGBFS) The ground granulated blast furnace slag (GGBFS) is a by-product of iron manufacturing which when added to concrete improves its properties such as workability, strength and durability. This material is obtained by the heating of iron ore, limestone and coke at a temperature about 1500 degree Celsius. The process is carried out in a blast furnace. The formation of GGBFS is not direct. The by-product of iron manufacturing is a molten slag and molten iron. The molten slag consists of alumina and silica, also with the certain amount of oxides. This slag is later granulated by cooling it. For this, it is allowed to pass through a high-pressure water jet. This result in quenching of the particles which results in granules of size lesser than 5mm in diameter. The main constituents of blast furnace slag are CaO, SiO2, Al2O3 and MgO. These are the minerals that are found in most of the cementitious substances. The particles are further dried and ground in a rotating ball mill to form a fine powder, known as ground granulated blast furnace slag cement. Now different methods can be employed to perform the main process called as the quenching. Applications & Benefits of GGBFS: In concrete: The incorporation of ground granulated blast furnace slag in concrete manufacture gains many advantages which are mentioned below: GGBFS in concrete increases the strength and durability of the concrete structure. It reduces voids in concrete hence reducing permeability GGBFS gives a workable mix. It possesses good pumpable and compaction characteristics The structure made of GGBFS constituents help in increasing sulphate attack resistance. The penetration of chloride can be decreased. The heat of hydration is less compared to conventional mix hydration. The alkali-silica reaction is resisted highly. These make the concrete more chemically stable. Gives good surface finish and improves aesthetics. The color is more even and light. Lower chances of efflorescence. The maintenance and repair cost of structures are reduced thus increasing the life cycle of concrete structures. Unlike cement, GGBFS does not produce carbon dioxide, sulphur dioxide or nitrogen oxides. White Cement: White Portland Cement is of high quality, whiteness and strength, it essentially has the same properties and characteristics as gray cement, except for color. It is widely used in numerous applications such as precast concrete, cast-in-place concrete, terrazzo, median barriers, curbs, tile grout, paint, masonry units, swimming pools, glass fibre reinforced surface bonding mortars.
Granulated Blast Furnace Slag : Granulated blast furnace slag or gbfs is the residue of combustion in the furnace of the steel refining process. It is obtained by quenching molten iron slag from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder. Ggbfs or ground granulated blast furnace slag is formed when gbfs is further processed or ground using conventional cement clinker grinding technology. Uses and benefits of GBFS/GGBFS uses : - GGBFS or GBFS is the most used raw material in cement industry to make slag cement. - Lightweight fill - Raw material for the manufacture of glass - GBFS can be used as a substitute for sand in building materials - GGBFS can be used as a replacement for portland cement
Supplier: High quality granulated blast furnace slag (gbfs) for various industrial applications.
Services: Export