4Mm To 19Mm Toughened Glass

Fully tempered glass is approximately four times stronger than annealed glass of the same thickness and configuration. Residual surface compression must be over 10,000 PSI for 6mm glass, according to ASTM C 1048 When broken, it will break into many relatively small fragments, which are less likely to cause serious injury. The typical process to produce tempered glass involves heating the glass to over 1,000 degrees F, then rapidly cooling to lock the glass surfaces in a state of compression and the core in a state of tension, as shown in the diagram Tempered glass is often referred to as â??safety glass,â?� because it meets the requirements of the various code organizations. This type of glass is intended for general glazing, and safety glazing such as sliding doors, storm doors, building entrances, bath and shower enclosures, interior partitions, and other uses requiring superior strength and safety properties.

About Clear Tempered Glass Clear tempered glass, also toughened glass, hardened glass, reinforced glass, ESG glass, impact resistant glass, is fabricated by heating� clear float glass to over 600�°C and cooling it rapidly, which locks the outer surfaces of the glass in a state of high compression, and the core or center of the glass in compensating tension. It is a safety glass which is used when strength, thermal resistance and safety are important considerations. Clear Tempered Glass Characteristic High Strength The tempered glass performs well in resisting bending and hitting owing to its high strength which is 3-5times that of normal float glass. It is able to withstand a surface pressure of 95Mpa. High Safety When the tempered glass is broken, it turns into alveolate granules with obtuse angles, which guarantee safety to make sure human harmless, and the toughening process greatly reduces the risk of thermal breakage to ensure less loss. Heat Stability The tempered glass is capable of withstanding a temperature change of 250 to 320 while normal annealed glass can only bear 20 to 100 Clear Tempered Glass Specification Available size: Maximum 3000*8000 mm, Minimum 150*300 mm, any customized size. Beveling edges, cutting notches, drilling holes, grinding corners, etc. all could be done, but must be done before tempering. Edge work Any edges could be done perfectly on clear toughened glass, like flat polished edge (T edge), pencil edge (C edge), beveled edge, ogee edge, matt edge, corner round edge. Holes and notches Tempered glass can be supplied with drilled holes (no matter straight or conical) and cut notches. We will consider hole and notch locations and size according to your drawings. Clear Tempered Glass Application â?¢ Used in interior like bathroom glass shelves, glass partition walls, etc. Used in exterior like window glass, greenhouse glass, etc. Used on furniture like table top glass, cabinet door glass, etc. Many Others.

1> Shower Screen Connector / Shower Support Bar Bracket. 2> Glass thickness : 6 mm~12 mm 3> Size: 19mm / 22mm / 25mm Diameter. 4> Material : Solid Brass 5> Chrome plated, Brushed Nickel, Brass Polished, Polished Chrome, Gold Plated, Oil Rubbed Bronze.

Specifications toughened glass 4mm Glaston toughened furnace 4mm clear glass facade Export to over 20 countries CCC,meet EN/BS/NZS/ANSI Widely used for windows & doors, shower room, balustrade, pool fencing, skylight, furniture desktop, partition, solar panel, curtain wall, greenhouses, etc. Tempered/toughened glass is made from annealed glass via a thermal tempering process in which the glass is heated till its softening point about 650 degrees and then quenching quickly to become Tempered glass or heat strengthened glass Characteristics A fully Tempered glass is 3 to 5 times stronger than annealed glass of similar thickness. A fully Tempered glass is regarded as a safety glass and when it breaks it disintegrates into small blunt pieces/ small oval-shaped pebbles which greatly reduce the chances of injuries 1) Strength - Fully low-e Tempered glass is generally 3 to 5 times stronger than annealed glass and twice as strong as heat strengthened glass of similar thickness, size and type. For fully Tempered glass the minimum surface compression is 10000 psi and for a heat strengthened glass is 4000-7000 psi for 6 mm glass. 2) Safety - When broken by impact, fully Tempered glass immediately disintegrates into small oval-shaped pebbles, thus greatly reducing the likelihood of cutting person Properties of Tempered glass Data Density (Approximate) 2.42-2.52 g/cm Tensile Strength 120 to 200 N/sq.mm Compressive Strength 1000 N/mm2 Modulus of Elasticity 70Gpa Coefficient of linear expansion 9 x 10-6 m/Mk U Value 5.7W/m2C for 6mm Tempered glass SF for 6 mm clear 81 % SC of 6 mm clear 0.93 Selectivity 1.0 VLT of 6 mm tempered glass 87% Clear Tempered glass thickness: 3mm, 3.2mm, 4mm,5mm,6mm,8mm,10mm,12mm,15mm,19mm Color: Clear, Ultra clear Tinted, Grey, green, bronze, blue etc. Reflective & low-e (including double silver low-e) etc. Main Products we process: a. Flat tempered/toughened glass b. Curved tempered/toughened glass c. Insulated glass d. Tempered/toughened insulated glass e. Laminated insulated glass f. Tempered low-e insulated glass g, Double silver low-e insulated glass h, low-e insulated glass with TGI spacer i. Silk screen printing glass j. Frosted glass/land blasted glass, acid etched glass k. Hot bent glass