Polyimide film is synthesized by polymerizing pmda and oda in strong polar solvents through the process of forming film and imine treatment at high temperature, which possesses excellent physical, chemical, and electrical properties, atomic radiation resistant, solvent resistant, low & high temperature resistant, it performs successfully in the wide range of temperature as low as -452f(-269c) and as high as +752f(+400c).
Polyimide film coated fep resin is uesd for magnet wire in oil pump which is similar to fn019 and fn919. Any further information , please kindly contact us.
Polyimide fep film (kypifep) is polyimide film coated with fep(f46) resin on one side(fh) or double sides(fhf) through the sintering process at high temperature, which combines the excellent properties of polyimide film and fep(f46) resin, high& low temp resistant, radiation resistant, excellent electrical properties, superior dimensional stability and heat sealable properties. It performs successfully in the wide range of temperature as low as -112f(-80c) and as high as +500f(+260c), widely used for insulation in motor, electrical apparatus and wrapping of cable and magnet wire. It can be melt and formed soon as desired at defined temperature. Carton
Company Introduction: Shandong Xinhongyun New Material Technology Co., Ltd.Located in weifang city, shandong provience., is a ISO certified professional & reliable manufacture of electrical insulation materials-BOPI FILM(polyimide film). our annual prodcution capacity is 150-200MT.main thickness 12.5um,25um & 50um, main width 514mm,520mm,1028mm&1040mm.main color: yellow, red, matte black. we have strict quality inspection system ,we trust we can supply you best quality product with high quality Description Polyimide (PI) is a polymer of imide monomers, aslo know as heat resistant film or high temperature film. With their high heat-resistance, polyimide enjoys diverse applications in roles demanding rugged organic materials.� Polyimide film� is ideal for insulating circuit boards, high temperature powder coating and transformers manufacturing. Polyimide film provides excellent electrical, thermal, physical and chemical properties over a wide temperature range between -269ºC (-452F) and 40ºC (752F) making them superior for electrical insulation applications Polyimide film can be laminated, metalized, punched, formed or adhesive coated. BOPI film has better thickness tolerancem,highter physical, chemical,and electrical properties. It� is the recommended choice for applications that require an all-polyimide film with an excellent balance of properties over a wide range of� temperatures. we can provide both standard and custom polyimide film solutions for a customer depending on their needs. Slitting and Packging Width:520mm~1040mm Core ID:76mm(3'')or 152mm(6''),Core materials:Paper or plastic Packaging:PE film packaged,with aluminum foil and foam,Suspended packing. Storage:The film should be stored in a dry and clean indoor,should be suspended in the box. Should not erect,close to the fire,heat or direct sunlight. Applications Wire&cable Insulation, slot liner insulation,interlayer insulation in Motor,transformer etc. Backing material for Polyimide coating or composites Flexible Printed Circuits Board(F-PCB) Polyimide Label Polyimide tubing
Apperance: Smooth&bright Colour: transparent Thickness: 25um(1mil)~125um(5mil) Width: 0.05~1m Alternative: Dupont kapton polyimide film HN Storage: In dry condition Shelf life: 8 years if storage safety Materials: PMDA, ODA and DMAC Application condition: High temperature and voltage condition Major customer: Alston and Moto China Factory This polyimide film is similar Dupont Kapton HN, but compared with Kapton HN that is more economical. Like properties of other polyimide film, this thermal conductive polyimide film with good thermal conductive property, could work at the condition from -269â?? up to 400â??. This polyimide film designed by our factory is absolutely alternative to dupont kapton HN, has excellent dielectric strength, electric dissipation factor, wide temperature range, chemical resistance at elevated temperatures, compared with Dupont Kapton HN that is more economical. Certification: ISO9000:2008, UL, SGS Mainly used in electrical and electric insulation application: 1) Formed coil insulation 2) Substrates for FPC 3) Motor solt liner 4) Magnet wire insulator 5) Transformer and capacitor insulation 6) Magnetic and PSA tape 7) Tubing Thickness from 25um up to 175um, width from 5mm up to 1m could be cut by customerâ??s requirement. The film will be provided in rolls and fixed on to the pipe core. Each roll is well packed in plastic bag to be placed into dry and clean box. Delivery Time: prompt Our other high performance materials: Polyimide film coated with FEP Polyimide film PSA tape coated with Acrylic Pressure Sensitive Adherence Corona resistant polyimide film Corona resistant polyimide coated with fep CR polyimide film mica tape CR polyimide film PSA tape For more information on Kapton (polyimide) film or other high performance materials, Please contact your representative.
High temperature resistance: Short term temperature resistance 300°C Long term temperature resistance 260°C Static resistance High electrical strength Insulation class H
Standard number: 2006 GB/T13542.6-2006 Application range: The polyimide film is to be produced by cast method, which has High temperature resistance, resistance to radiation and excellent dielectric properties, applicable to electrical insulating of the class H electric motor and other electrical equipments , and other use electrical insulating materials. A. Technical requirements 1. Appearance: Film surface is bright and clean, not due, tear, particle, bubbles, Pinhole and foreign material defects ;Edge is tidy, without damage; Films supply in rolls. 2. Size 2.1. Thickness and allowable deviation: The standard thickness(um) 12.5 25 40 50 75 100 125 175 200 The allowable deviation(um) +1 +2 +2 +2 +3 +4 +4 +5 +5 -1 -1 -2 -2 -3 -3 -4 -5 -5 Note: Supplying according to customer request with thickness 12.5-22.5 um, allowable deviation can be negotiated by both sides. 2.2. Width: no less than 250 mm, deviation +/-1.6mm. According to the needs of the users, tape can be cut with different specifications. 2.3. Length: Supplying according to the requirement of customer. 2.4. Performance requirements Serial number Index name Unit Index 25um 40um 50um 75um 100um 1 density Kg/m3 1425 10 2 tensile strength horizontally Mpa Y165 vertically 3 elongations horizontally and vertically % Y40 Y50 4 shrinkage rate horizontally and vertically 150 400 % 0.35 2.5 5 industrial frequency electric strength 48H2 62H2 v/um Y240 Y200 Y180 Y160 6 surface resistance,200 Y1.0X1014 7 Volume resistance,200 M Y1.0X1010 8 Relative permittivity 48 62Hz - 3.5 0.4 9 dielectric power factor 48 62Hz - 4.0X103 10 long-term heat resistance temperature index - Y180. 1. Film should be wrapped in a tube on core and supply in rolls; Each volume in a plastic bag packing and seal, placing in dry and clean case 2. Each box packaging should specify model or type, product name, specification, batch number, gross weight, net weight, manufacturing date, manufacture ¡¥s name, and product test report. At the same time, marked "Moisture proof" "Prevent Impact" and other words in packing body. 3.Film should be stored in a dry and clean indoor, from the date of original shipment, shelf life for two years, more than storage life according to the standard check again, qualified can still use. 4. In storage and transport process, should avoid damp and mechanical damage.
The most outstanding characteristics of Polyimide film is for its high temperature endurance and insulation ability. To make a polyimide film, first form the film by condensing pyromellitic dianhydride(PMDA)and Diamino diphenyl ether(DDE) in strong solvents, and then be treated by imine at a high temperature It exhibit excellent thermal resistance, high insulation resistance, engineering properties, chemical stability, radiation resistance, inflammability and fire resistance rated at 94V-0. The product is halogen-free, and meets the environmental protection standard for its heavy metal and other restricted organic materials. Electronic parts, mechanic components, insulation on electrics, insulation tube, composite insulators.
The most outstanding characteristics of Polyimide film is for its high temperature endurance and insulation ability. To make a polyimide film, first form the film by condensing pyromellitic dianhydride(PMDA)and Diamino diphenyl ether(DDE) in strong solvents, and then be treated by imine at a high temperature It exhibit excellent thermal resistance, high insulation resistance, engineering properties, chemical stability, radiation resistance, inflammability and fire resistance rated at 94V-0. The product is halogen-free, and meets the environmental protection standard for its heavy metal and other restricted organic materials. According to customer's requirements.
Polyimide Film is produced by cast method, which has high temperature resistance, resistance to radiation and excellent dielectric properties. It is applicable to electrical insulating of the class H electric motor and other electrical equipments, and other use electrical insulating materials.
FEP Film has the characteristics of extremely excellent heat resistance, chemical resistance, non-stick and non-flamability capabilities, and is suitable for mold releasing film since it also has heat adhesiveness (heat seal) and adhesiveness (surface treated on one side) simultaneously.