Standard number: 2006 GB/T13542.6-2006
Application range: The polyimide film is to be produced by cast method, which has High temperature resistance, resistance to radiation and excellent dielectric properties, applicable to electrical insulating of the class H electric motor and other electrical equipments , and other use electrical insulating materials.
A. Technical requirements
1. Appearance: Film surface is bright and clean, not due, tear, particle, bubbles,
Pinhole and foreign material defects ;Edge is tidy, without damage; Films supply in rolls.
2. Size
2.1. Thickness and allowable deviation:
The standard thickness(um) 12.5 25 40 50 75 100 125 175 200
The allowable deviation(um) +1 +2 +2 +2 +3 +4 +4 +5 +5
-1 -1 -2 -2 -3 -3 -4 -5 -5
Note: Supplying according to customer request with thickness 12.5-22.5 um, allowable deviation can be negotiated by both sides.
2.2. Width: no less than 250 mm, deviation +/-1.6mm. According to the needs of the users, tape can be cut with different specifications.
2.3. Length: Supplying according to the requirement of customer.
2.4. Performance requirements
Serial number Index name Unit Index
25um 40um 50um 75um 100um
1 density Kg/m3 1425 10
2 tensile strength horizontally Mpa Y165
vertically
3 elongations horizontally and vertically % Y40 Y50
4 shrinkage rate horizontally
and vertically 150 400 % 0.35 2.5
5 industrial frequency electric strength
48H2 62H2 v/um Y240 Y200 Y180 Y160
6 surface resistance,200 Y1.0X1014
7 Volume resistance,200 M Y1.0X1010
8 Relative permittivity
48 62Hz - 3.5 0.4
9 dielectric power factor
48 62Hz - 4.0X103
10 long-term heat resistance temperature index - Y180.
1. Film should be wrapped in a tube on core and supply in rolls; Each volume in a plastic bag packing and seal, placing in dry and clean case
2. Each box packaging should specify model or type, product name, specification, batch number, gross weight, net weight, manufacturing date, manufacture ¡¥s name, and product test report. At the same time, marked "Moisture proof" "Prevent Impact" and other words in packing body.
3.Film should be stored in a dry and clean indoor, from the date of original shipment, shelf life for two years, more than storage life according to the standard check again, qualified can still use.
4. In storage and transport process, should avoid damp and mechanical damage.
High temperature resistance: Short term temperature resistance 300°C Long term temperature resistance 260°C Static resistance High electrical strength Insulation class H
The most outstanding characteristics of Polyimide film is for its high temperature endurance and insulation ability. To make a polyimide film, first form the film by condensing pyromellitic dianhydride(PMDA)and Diamino diphenyl ether(DDE) in strong solvents, and then be treated by imine at a high temperature It exhibit excellent thermal resistance, high insulation resistance, engineering properties, chemical stability, radiation resistance, inflammability and fire resistance rated at 94V-0. The product is halogen-free, and meets the environmental protection standard for its heavy metal and other restricted organic materials. Electronic parts, mechanic components, insulation on electrics, insulation tube, composite insulators.
The most outstanding characteristics of Polyimide film is for its high temperature endurance and insulation ability. To make a polyimide film, first form the film by condensing pyromellitic dianhydride(PMDA)and Diamino diphenyl ether(DDE) in strong solvents, and then be treated by imine at a high temperature It exhibit excellent thermal resistance, high insulation resistance, engineering properties, chemical stability, radiation resistance, inflammability and fire resistance rated at 94V-0. The product is halogen-free, and meets the environmental protection standard for its heavy metal and other restricted organic materials. According to customer's requirements.
Polyimide Film is produced by cast method, which has high temperature resistance, resistance to radiation and excellent dielectric properties. It is applicable to electrical insulating of the class H electric motor and other electrical equipments, and other use electrical insulating materials.
The polyimide film produced by our company is the main product specification model: 5um, 7.5um, 12.5um, 25um and 50um. The main international PI film manufacturers are: DuPont, Ube Japan, Japan Bell Chemicals, South Korea SKC kolon Polyimide film production process: casting, stretching. The color is yellow and transparent, and its relative density is 1.39 to 1.45. It has outstanding high temperature resistance, radiation resistance, chemical resistance and electrical insulation properties. It can be used in air at 250-280C for a long time. The glass transition temperatures were 280C (Upilex R), 385C (Kapton), and 500C or more (Upilex S). The tensile strength is 200 MPa at 20C and greater than 100 MPa at 200C. Particularly suitable for flexible printed circuit board substrate and a variety of high temperature electrical insulation materials.
Polyimide film is synthesized by polymerizing PMDA and ODA in strong polar solvents through the process of forming film and imine treatment at high temperture.Nominal thickness:0.025mm~0.25mmNominal width:5mm~1040mmApplication:Polyimide is an excellent H class insulating material, widely used for insulation of electrical equipment in special environment.
Corona resistance polyimide films ,not only with ordinary polyimide film electrical properties, good heat resistance and resistance chemicals, but also with the super corona resistance and good thermal conductivity performance, mainly apply to sintering electromagnetic winding wire ,traction motor, wind generators, and the special motor turn-to-turn insulation and heat insulation, the heat resistance level is a class C. The technical requirements: 1. Type CR type: Corona resistance polyimide film without any coating FCR type: Corona resistance polyimide film with F46 single side coating FCRF type: Corona resistance polyimide film with F46 double side coating 2. Appearance its appearance is golden brown, translucent, the surface is bright and clean, no wrinkles, tear, particles, bubble, pinhole and foreign material defects. Its edge is tidy, and without damage. 3. Thickness and allowable deviation Model CR type FCR type FCRF type Thickness(um) 25 38 50 Allowable deviation(um) 2 3 3 Note: coating thickness may be based on customer demand in 5 ~ 12.5 um range regulation. 4. Width and allowable deviation Width may cut according to the customer request within 600 -1050 mm. Each volume length is for 500-1000 m; Each volume joints for final product are not more than three, the proportion of volumes with joints vs the total volumes number in the one order is not more than 25%,the shortest length is more than 300 m; Single plate or roll products joint numbers are not more than three, the shortest length is more than 300 m. FCR type and FCRF type using thermal bonding lap. 5. Film marks: -Every single volume label marked: batch number, specification, net weight;Every single plate or roll labeling: specification. -Package should have obvious and firm mark; -The format of the packing cases is confirmed by purchase order related terms. Serial Number Type CR FCR FCRF 1 Corona resistance life (h) 1 KV voltage, frequency 20 KHz temperature 90 2 pulse rise time 400 ns Y80 Y80 Y80 2 Industrial frequency electric intensity (v/um) Y200 Y120 Y100 3 Surface resistivity 1X1014 1X1014 1X1014 4 Volume resistivity 1 1X1010 1X1010 1X1010 5 Relative permittivity (48-62 Hz ac) 3.2 0.4 3.2 0.4 3.2 0.4 6 Dielectric power factor (48-62 Hz ac) 13.5X10-3 13.5X10-3 13.5X10-3 7 Tensile strength (Mpa) : Y135 Y80 Y80 8 Elongation at break (%) Y40 Y40 Y40. 1. Testing method: According to the ICE62068-1-2003/ GB /T13542.6-2006 "electrical insulation, part 6," Polyimide film for electrical insulation regulation experimental method. 2. Film packaging: Film roll with plastic film packaging, outer with shockproof foam cushion packaging, and support in place in the package overhead, make the film in the transportation conditions often get fully protected without damage, each volume end article sticker marking. 3. Dust is strictly prohibited in the packing box internal. 4. Film should be stored in a dry and clean indoor, film roll to be supported in the box, placed suspended and not be erected. It should not be close to the fire, central heating or exposed to direct sunlight. 5. Products should avoid damp and mechanical damage in the storage and transport. 6. Film storage period is for two years after COA issued date. Expired films are still available after again qualified according to the product standards inspection.
Description: HN Polyimide Film has the excellent balance of electrical, thermal, mechanical, physical, and chemical properties over a wide range of temperatures as low as C269C and as high as 400C. Application: HN Polyimide Film can be used in a variety of electrical and electronic insulation applications: wire and cable tapes, formed coil insulation, substrates for flexible printed circuits (FPC), motor slot liners, magnet wire insulation, transformer and capacitor insulation, magnetic and pressure-sensitive tapes, and tubing. Size: Film Thickness: 0.013mm, 0.025mm, 0.040mm 0.05mm, 0.075mm, 0.100mm, 0.125mm, 0.150mm, 0.175mm, 0.200, 0.225mm. Film Width: 6mm to 1040mm Special thickness or width can be supplied according to customer. Rolls: 3 inch Core, max.width 1040mm Tapes: from 6mm width upwards Packing: approx.28kgs per roll in carton. Special size can be supplied according to customer.
Polyimide film is synthesized by polymerizing pmda and oda in strong polar solvents through the process of forming film and imine treatment at high temperature, which possesses excellent physical, chemical, and electrical properties, atomic radiation resistant, solvent resistant, low & high temperature resistant, it performs successfully in the wide range of temperature as low as -452f(-269c) and as high as +752f(+400c). Polyimide film coated fep resin is uesd for magnet wire in oil pump which is similar to fn019 and fn919. Any further information , please kindly contact us.