Refractory bed material.
Alumina as al2o3
30% - 40%
Silica as sio2
50-60% max.
Alkalies na2o + k2o
Less than 1%
Iron as fe2o3
Less than 2.5%
Titanium oxide tio
Less than 1%
Physical properties
Particle density
2.00 gm/cc
Bulk density
1000-1100 kg/m³
Initial deformation temperature
> 1300° c
Maximum particle size
2.80 mm
Minimum particle size
0.85 mm
Note : other sizes also available on request
40 kg hdpe bags packing(in proper condition, without breakage)
Shape : Grains For Use in Floor, Partition Walls Resistance Durability : Fire Resistant
Used in cfbc / fbc boiler , captive power plant.
JANTA Group provides Refractory Boiler Bed Material (Refractory Grog) of Low Ferric High Temperature product, which is processed from selected super heat duty refractory aggregates of moderate alumina contents and of highly dense texture. This very special Bed Material of Refractory Aggregates fired at a temperature of 1400 Centigrade has many special characteristics that make it a perfect material for obtaining smooth and perfect fluidization in Fluidized Bed Combustion boilers with high economy of operations. Special Characteristics: Exceptional Chemical Purity with Low Alkali and Low Iron Contents Fully Screened Material with Accurately Controlled Particle Size Distribution Free From Dust/ Fine & Over Sized Particles Perfectly Controlled Particle Density and Bulk Density
Alumina as al2o3 30% - 40% Silica as sio2 50-60% max. Alkalies na2o + k2o Less than 1% Iron as fe2o3 Less than 2.5% Titanium oxide tio Less than 1% Physical properties Particle density 2.00 gm/cc Bulk density 1000-1100 kg/m³ Initial deformation temperature > 1300° c Maximum particle size 2.80 mm Minimum particle size 0.85 mm Note : other sizes also available on request 40 kg hdpe bags packing(in proper condition, without breakage)
Magnesia Bricks Description Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application. Magnesia Bricks Features: It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature. Magnesia Bricks Application Basic open-hearth furnace for steelmaking Electric furnace bottom and wall Permanent lining of oxygen converter Non-ferrous metal metallurgy furnace Hyperthermia tunnel kiln Lining of rotary cement kiln Heating furnace bottom and wall Regenerative chamber of glass furnace Magnesia Bricks Properties High Refractoriness Good alkaline slag erosion resistance High apparent initial softening temperature Good thermal conductivity High thermal expansion Magnesia Bricks Manufacturing Process Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : RED SHALE Type Acid Resistant Brick Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions Heavy thermal shock Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick Characteristic RED SHALE ACID RESISTANT BRICK Test Standard Bulk Density, gm/cc - 2.3 to 2.35 ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968 Apparent Porosity, % -0.5 to 1.75 S 4860 Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279 Modulus of Rupture, PSI -2133 to 3555 ASTM C-67 Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968 Abrasion Resistant , Volume in mm3 -69 to 85 EN 102 Surface Hardness, MOHS Scale - 7
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : FIRECLAY Type Acid Resistant Brick Size (mm) : 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : * We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: * Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions - Heavy thermal shock Characteristic Fireclay Type Acid Resistant Brick - Test Standard Bulk Density, lbs/ft3 - 2.25 to 2.30 ASTM C-20 Water Absorption, % - 0.1 to 1.8 ASTM C-20 Apparent Porosity, % - 4.05 to 4.14 ASTM C-20 Acid Solubility (H2SO4), Loss in Mass,% - 6.1 to 6.8 ASTM C-279 Modulus of Rupture, Mpa - 14.6 ASTM C-67 Compressive Strength, PSI - 15500 to 17250 ASTM C-67 Abrasion Resistant , Volume in mm3 - 71 to 96 EN 102 Surface Hardness, MOHS Scale - 7 Thermal Conductivity, BTU-in/hr-ft-F - 6.94 to 7.12 ASTM C-236 Thermal Expansion Coefficient,in/in/Fx10-6 - 2.6 to 2.8 EN 103
Supplier: Refractory bricks, high alumina bricks, acid proof bricks, tiles and castables, all mortars and fire clay, low cement castables, insulating castables, conventional dense refractory bricks, insulation bricks, cold face, hot face insulation bricks, hot face insulation bricks, acid resistant bricks/components, membranes, acid resistant cement, construction chemicals, class 1 ar tiles and bricks 38mm and 75mm, 4457 vitrified ar tiles with 0% water absorption, 20mm & 25m, primer, mastics, pot. silicate cement, coerce cement, furnace based cement, crushed refractory boiler bed material, acid resistant tiles, acid resistant brick fireclay type, acid resistant brick red shale type, bitumen primer, epoxy resin & hardner, furan powder and syrup solution,
Technical Data Sheet Of Accoset-50 ALUMINA MORTAR (Test Certificate) General Properties A. Max service temperature - 1500 oC B. Maximum grain size - 0 - 1.5 mm C. Water required for mixing - 22 - 30% D. Setting - Airsetting E. Sintering Temp - 1550 oC Chemical Properties A. Al2O3 - 50.00% B. SiO2 - 31.00% c. Fe2O3 - 5.00% D. LOI - 7.00% Physical Properties A. Dry Density - kg / m3 B. CCS - 17 kg / cm2 after drying at 110C / 24 hr C. MOR - 20 kg / cm2 at 110 oC/ 24 hr 18 kg/cm2 at 800 C/ 3 hr Thermal Properties - A. Refractoriness ( Orton / C) - 31.5 orton cone/1699 oC Packaging - 25 - 50 kg bags Storage Life - 12 months Delivery State - Dry