Typical properties:
Alumina content: 92% alumina content: 95%
Volume density: 3.6g/cm3 volume density: 3.7g/cm3
Hardness (mohs): 9 hardness (mohs): 9
Wear rate: 0.02% wear rate: 0.005%
Water absorption: 0.01% water absorption: 0.01%
Applications:
Grinding media for industries of sanitary ceramics, refractory, cement and paint.
Typical properties: Alumina content: 92% alumina content: 95% Volume density: 3.6g/cm3 volume density: 3.7g/cm3 Hardness (mohs): 9 hardness (mohs): 9 Wear rate: 0.02% wear rate: 0.005% Water absorption: 0.01% water absorption: 0.01% Applications: Grinding media for industries of sanitary ceramics, refractory, cement and paint.
Product Advantages: The alumina produced by China Aluminum Corp. is used as the base material, which provides high purity, little impurity and stable quality. Production is implemented on kanban basis and the entire production process is controllable and traceable. Each batch of product is strictly tested. The process and result guarantee stable performance and proven quality of the final product.
Application: Wear-resistant material for surfaces of delivery equipment or liquid flowing pipes of petroleum, mining, cement,chemical,steel works and power plants, purposed to effectively resist the impact , corrosion and thermal impact from passing material, reduce abrasion and thereby significantly extends the service life of the equipment. It is the first choice for wear-resistant material for industrial application. It especially endure high temperature. Installation: Either by welding or by sticking with glue according to specific working condition Packing: in cartons plus pallet Product Advantages: Large variety, diverse sizes, small tolerance, accurate dimension
Application: With its high strength, high hardness, high wear resistance, large specific gravity, small size, heat and corrosion resistant and pollution free, the product is widely used in precision processing and deep processing of various ceramics, enamels, glasses and thick and hard materials in chemical factories, as grinding media for fine crushing machines like ball mills, can-type mills and vibration mills, with significantly higher crushing and milling efficiency and wear resistance than common ball stone or natural cobblestone.
Category CH90 CH92 CH95 Density 3.50 3.60 3.65 Al2O3 90% 92% 95% ZrO2+Y2O3 / / BendingStrengthMPa 180 220 250 CompressionstrengthMPa 970 1050 1300 FractureToughnessMPam1/2 3.5 3.7 3.8 HVHardnessN/mm2(MPa) 900 950 1000 WearVolume 0.28 0.25 0.20 Different kinds of products: Ceramic Mosaic Pieces, Ceramic Pipe Tiles, Ceramic Curved Tiled(with or without holes), Ceramic Tapered Tiles, Ceramic Cylinders, Stell Lined with Ceramic Tiles, Irregular Shaped Tile, Clipping Ceramic Tiles Interlocking Bricks. We have so many kinds of sizes. And we are also accept customized. Mineral Processing equipment operates in some of the harshest and remote locations. It is crucial to the Mineral Processing industries that this equipment continues to operate efficiently and its lifecycle is maximized to minimize downtime. By appropriately protecting equipment from the extreme wear caused by the high speed and flow rates of ore when processed as a slurry ensures better equipment longevity. The slurry is highly abrasive and can not only cause wear damage to wet processing equipment but also with the inclusion of chemicals and heat, there is a constant risk of corrosion and dangerous leakage. Wear Protection ceramic Linings are used throughout Mineral Processing to protect the steel surfaces of equipment from wear and corrosion. They are used on a range of equipment including pipes, tanks, chutes, pumps, flotation cells, thickeners, launders, and feed spouts or chutes 92% 95% Abrasive Alumina Ceramic Wear Liner
100*100*6-25mm etc. Support customzied. Wear resistant ceramic which are mainly composed of at least 90% Al2O3 are the most widely used in the world today. Our products are made from strictly selected alumina powder with uniform particle sizes and low CaO content.Wear resistant ceramics can be made through common dry press or isostatic pressing process and then sintering them at high temperature in the kiln. They are desirable lining materials for high wear equipment due to precise dimensions, high density,high alumina content,good flatness and stable quality.
Application:Industrial ceramic grinding mediaï¼?grinding Al2O3 content:92%,95% Making type:Rolling; ISP HRA: 85 Type:Ceramic Balls,alumina grinding media balls Appearance:Smooth and white Color:white Compressing strength:2000Mpa Size:0.5mm-95mm Advantage: High wear resistance Production temperature:1600 HS code:690912 Certificate:ISO 9000
Application:Industrial ceramic grinding mediagrinding Self Abrasion:0.0055-0.01% Density:3.60g/cm33.7g/cm3 Al2O3 content:92%,95% Making type:Rolling; ISP Moh's hardness:9 HRA: 85 Water absorption:0.01% Type:Ceramic Balls,alumina grinding media balls Appearance:Smooth and white Color:white Compressing strength:2000Mpa Size:0.5mm-95mm Advantage: High wear resistance Production temperature:1600 HS code:690912 Fe2O3:0.02% Certificate:ISO 9000
Alumina balls with the advanced production facilities, high technology, and abundant production experience. The alumina content could be 75%, 90%, 92%, 99%. The main production processing is super-fine powder grinding, cool- 90% microcrystal alumina lining bricks 75% alumina ball(cip) 75% alumina ball(rolling) 75% alumina beads for chemical industry 99% alumina ball for chemical industry 90% microcrystal alumina liner