Soundness in microstructures with homogeneous composition, littlegregation and lower MgO content. Stable and even lasting with high absorption of Mg.Much smaller and globular graphite and high nodularization efficiency when treated.
Nodularization temperature is recommended at 1400-1450 when melted from a cuppola,or at 1450-1500 when from an electric furnace. Added at 1.5%-1.6% when sulphur in the liquid cast iron is as high as 0.065-0.09%, or 1.4%-1.5% when sulphur is as high as 0.05-0.065%.
Supplied in the form of grain(5-25mm) or following special requirement. Packed in plastic braids with inner wet resistant plastic film. Per packed parcel is 25kg n.m.
Model Chemical Composition% Si Mg Ca Re Ba La Fe BN-126 38-44 6-7.5 1.0-3.0 1.8-2.5 - balance BN-127 38-44 6.3-7.5 2.0-3.5 2.5-4.0 1.2-2.0 balance BN-137 38-44 6.3-7.5 1.0-3.0 2.5-4.0 - balance BN-138 38-44 7.0-9.0 2.0-3.0 2.0-4.0 - balance BN-158 38-44 7.0-9.0 2.0-3.0 4.0-6.0 - balance BN-101 44-48 5.6-6.5 0.8-1.2 - ï¼?2.0 proper balance BN-104 44-48 5.5-6.5 1.0-1.5 0.4-0.6 proper balance Standard Size: 0.6-6mm,1-12mm,5-25mm,4-30mm Packing: 25kg woven plastic bag in 1mt jumbo bag. Note: Chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements. Characteristics 1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed. 2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products. 3.High mechanical strength and strong deoxygenation and desulfuration effects.
Characteristics 1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed. 2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products. 3.High mechanical strength and strong deoxygenation and desulfuration effects.
Trade markCodeChemical composition%Melting methodApplication range MgReSiCaAlTiFe Fesimg5re25-24.0-6.01.0-3.038-442.0-3.01.00.5RestElectric furnaceAll kinds of Di casting Fesimg6re16-15.0-7.00.5-1.538-442.0-3.01.00.5RestElectric furnaceAll kinds of Di casting Fesimg7re17-16.0-8.00.5-1.538-441.0-1.51.00.5RestElectric furnaceAll kinds of Di casting Fesimg7re37-36.0-8.02.0-4.038-442.0-3.51.00.5RestElectric furnaceAll kinds of Di casting Fesimg8re37-37.0-9.02.0-4.038-442.0-3.51.00.5RestElectric furnace or cupolaAll kinds of Di casting Fesimg8re58-57.0-9.04.0-6.038-442.0-3.51.00.5RestElectric furnaceAll kinds of Di casting Fesimg8re78-77.0-9.06.0-8.038-442.0-3.51.00.5RestElectric furnaceAll kinds of Di casting Fesimg10re710-79.0-11.06.0-8.038-442.0-3.51.00.5RestElectric furnaceAll kinds of Di casting Mainly used in automobile industry, mechanical casting, ductile iron pipes and other metallurgical industry.The addition of magnesium (mg) causes spheroidal graphite to grow. Packing: 25kg woven plastic bag in 1mt big bag Note: chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements. Packing: 25kg woven plastic bag in 1mt big bag
1). Cast iron rolls: Alloy chilled cast iron rolls. Alloy indefinite chilled cast iron rolls. Spheroidal graphite cast iron rolls (sga bainite nodular , sgp pearlite nodular )(centrifugal). High chrome cast iron rolls (centrifugal). 2). Cast steel rolls: Alloy cast steel rolls. Adamite steel rolls. Centrigugal casting hi-carbon adamite steel rolls. Graphite steel rolls. High speed steel rolls. High chrome casting steel rolls. Metal pallet, wooden pallet box.
Des. Casted parts/components Cast method Sand cast, die cast, Lost foam/wax, investment casting, centrifugal casting, Processing Precision CNC machining, grinding, tapping ,painting and assembly Finish treatment Tempering , quenching, annealing, normalizing Surface treatment -blast shooting -HDG,zince -Chrome plating -Powder coating -Anodizing -Polishing -Electrophoresis -Electrostatic color paining QA Caliper, roughness tester, strength tester, spectrograph, CMM, metalloscope and etc.. 3party inspection report is able to serve as your needs. Material range Die casting: Aluminum or alloy A360, A380, A390, ADC12,ADC10,ALSI09 etc. Ductile iron casting part: QT400 , QT450, QT500, QT550, QT600, QT700 Zinc & Zinc alloy. ZA-3,ZA-5,ZA-8 Sand casting:ZL101,ZL104,ZL102 and so on. Iron casting: HT150, HT200, HT250, HT300,etc. Standard: JIS, DIN, ASTM,BS, ISO,AISI Application scope -Woodworking hand tools, -Electrical high voltage fittings, -Cookware, BBQ grill, -Pump/valve body or accessories , -Drainage grate, -Construction accessories Package Standard seaworthy packing FOB Port CN DLC Standard ISO,GB,ASTM,BS,JIS,AISI,DIN and etc. 1. The property of company is OEM or trading business only? Where is the location of foundry? - More than decade experiences both on manufacturing and exporting of alloy castings. - The foundry , CNC workshop and assembly line are in Province Liaoning, construction area occupied total 20000m2. 2. The way to obtain the quotation. -We r always standby, the more accuracy parameters you provided, the more close price you will be obtained. The drawing in AUTOCAD, PROE,SOLIDWORKS and etc. what the general formats are preferred to. 3. Leading time, MOQ and delivery term. - Leading time or MOQ depends on the complexity ,casting structure and dimension. Any requirements could settle by mutual negotiating. for the Shipping transportation , the world top 10 ocean carriage brands for transporting period could be referred to . FOB ,CIF, CFR what types stipulated in incoterms 2010 are acceptable. For more just call or write to me with undersigned.
Nodular Pig Iron C: 3.5 -- 4.5% Si: 0.5 -- 1.0% or 1.00 -- 1.40% Mn: 0.08% max P: 0.035% max S: 0.013% max Ti: 0.035% max 7 - 8 KGS per ingot Delivery by container with jumbo bag
Marine Nodular Iron Globe Valve or Marine Ductile Iron Globe Valve is from small size DN15~DN40. Design Standard: JIS F7312-1996 Test Standard: JIS 7400-1996 Hydraulic Test Pressure: Body-1.05Mpa, Seat-0.77Mpa Flange size as per JIS B2220 -5K Material: Body/Bonnet-Ductile Iron FCD450 Seat-SUS (SCS2) /Bronze (BC6) Stem-SUS (SCS2) /Brass (C3771BD)
Pearlitic rolls are composed by nodular graphite and carbides arranged in a pearlitic matrix. It's properties are similar to Indefinite Chill except that the graphite structure is changed from flake to spheroidal forms. Pearlitic rolls will have higher strength than Indefinite Chill. Pearlitic roll can be produced by static casting (Monoblock) or by using the centrifugal cast (CC) Double-pour method.
a. Price of product - depends on customers product b. Product origin - Turkey c. Key Specifications/Special Features d. Minimum Order Size : 1 full Truck or 1 full container e. Packaging Details: Euro pallets- Wooden boxes or other customer-specific packaging details.