1,Blend dosage range is 0.5-1.2%. Appropriate blend dosage can be selected according to project object and the materials used during application.
2,FDN powder is recommended to be applied in solution. It can be used in dry form, but make sure mix it thoroughly with concrete.
3,If this product is applied with adoption of stagnant water blending method or post-blend approach, water reduction and dispersion will be better.
4,This product can be formulated with concrete additives of other varieties. It can be "double blended" with blending materials such as fly ash, ground slag, etc. But the blend dosage shall be calculated based on the total of cementing materials.
5,When this product is used for the first time or cement variety is changed, concrete trial preparation shall be conducted according to the adopted materials and construction requirements in the field. Construction mixing rate shall be adjusted based on testing result to serve as instruction for construction blending.
The raw material naphthalene superplasticizer (SNF/FDN/PNS) has strong dispersion effect on cement particles and good use effect of preparing super flowing concrete as well as cast-in-situ concrete and precast members with early strength and high strength requirements, can comprehensively improve various properties of the concrete, and is widely applied to highways, bridges, dams, harbors, tunnels, electric power, water conservancy as well as industrial and civil architecture, steam-cured and naturally-cured precast members and so on. Specifications Model SNF-A appearance Light brown powder Solid content â?¥93% PH value 7-9 Sodium sulfate ï¼?5% Chloride ion ï¼?0.3% Water reduction 22%-25% Cement paste fluidity â?¥250mm Water Insolubles â?¤2% Air content â?¤2% Application 1. Construction: 1. Widely used in precast & ready-mixed concrete, armored concrete and pre-stressed reinforced concrete in key construction projects such as dam and port construction, road building & town planning projects and dwelling erections etc. 2. Suitable for preparation of early-strength, high-strength, high-anti-filtration and self sealing&pumpable concrete. 3. Used for and widely for self-cured, vapor-cured concrete and its formulations. At the early stage of application, extremely prominent effects are shown. As the result, the modulus and site utilization can be drastically, the procedure of vapor cure is omitted in peak heat summer days. Statistically 40-60 metric tons of coal will be preserved when a metric ton of the material is consumed. 4. Compatible with Portland cement, normal Portland cement, Portland slag cement, flyash cement and Portland pozzolanic cement etc. Others: Because of the high dispersion force and low foaming characteristics, SNF has also been widely used in other industries as Anionic Dispersing Agent. Dispersing agent for disperse, vat, reactive and acid dyes, textile dying, wettable pesticide,paper,electroplating, rubber, water-soluble paint, pigments,oil drilling, water treatment,carbon black, etc.
The raw material naphthalene superplasticizer (SNF/FDN/PNS) has strong dispersion effect on cement particles and good use effect of preparing super flowing concrete as well as cast-in-situ concrete and precast members with early strength and high strength requirements, can comprehensively improve various properties of the concrete, and is widely applied to highways, bridges, dams, harbors, tunnels, electric power, water conservancy as well as industrial and civil architecture, steam-cured and naturally-cured precast members and so on. Specifications Model SNF-C appearance Light brown powder Solid content 93% PH value 7-9 Sodium sulfate 18% Chloride ion 0.5% Water reduction 18%-20% Cement paste fluidity 230mm Water Insolubles 2% Air content 2% Application 1. Construction: 1. Widely used in precast & ready-mixed concrete, armored concrete and pre-stressed reinforced concrete in key construction projects such as dam and port construction, road building & town planning projects and dwelling erections etc. 2. Suitable for preparation of early-strength, high-strength, high-anti-filtration and self sealing&pumpable concrete. 3. Used for and widely for self-cured, vapor-cured concrete and its formulations. At the early stage of application, extremely prominent effects are shown. As the result, the modulus and site utilization can be drastically, the procedure of vapor cure is omitted in peak heat summer days. Statistically 40-60 metric tons of coal will be preserved when a metric ton of the material is consumed. 4. Compatible with Portland cement, normal Portland cement, Portland slag cement, flyash cement and Portland pozzolanic cement etc. Others: Because of the high dispersion force and low foaming characteristics, SNF has also been widely used in other industries as Anionic Dispersing Agent. Dispersing agent for disperse, vat, reactive and acid dyes, textile dying, wettable pesticide,paper,electroplating, rubber, water-soluble paint, pigments,oil drilling, water treatment,carbon black, etc. Sodium sulfate content: 1. If the content is large, it may crystallize at low temperature which blocks pipes and valves, and reduces the water reducing capacity and strength.Because the solubility is affected by temperature change.When the outdoor temperature is below 20, the solubility will drop suddenly. When the outdoor temperature is below 16, the crystal of sodium sulfate is obvious.During crystallization, some effective components of naphthalene series superplasticizer will be adsorbed, which will affect the water reducing ability and strength of concrete.
Supplier: Lignosulfonate, sodium gluconate, SNF/FDN/PNS, naphthalene superplasticizer, polycarboxylate superplasticizer, SHMP
soidum lignosulphonate MN1: Index Items Standard Value Test results PH Value 10-13 12.98 Dry Matter â?¥92% 95 Lignosulphonate â?¥50% 52 Water insoluble matter â?¤3.0% 2.67 MN2: Index Items Standard Value Test results PH Value 9-11 9.5 Dry Matter â?¥92% 96 Lignosulphonate â?¥50 55 Water insoluble matter â?¤1.5% 0.7 Sodium Lignosulphonate ( lignosulfonate ) water reducer are mainly for concrete mixture as water-reducing additive. Low dosage , low air content , water reducing rate is high ,adapt to most kind of cement. Can confected as concrete early-age strength enhancer , concrete retarder , antifreeze , pumping aids etc. Nearly no precipitate product in the liquor additive which is made from The sodium lignosulphonate and Naphthalin-Group High-Efficiency Water Reducer .The sodium Lignosulphonate is fit for apply to building project, dam project, thruway project etc. If you are interested in our products, please do not hesitate to contact us! Best regards! Lorna
Physical and Chemical characteristics Properties: white crystalline granule or powder, easy to dissolve in the water Molecular formula: C6H11O7Na Quality standard Index items Standard value Test Results Appearance White or yellowish crystal powder Meets the requirement purity 98.5% 99.22% PH value 6.0 8.0 6.70 Sulphate 0.05% 0.03% chloride 0.07% 0.04% lead,ug/g 2% 1.38% loss on drying 0.5% 0.21% Reducing substances 0.7% 0.38%. Packing, storage & transportation: 1, Packing: 25kg in PP woven bag lined with plastic film. 2 ,Storage: Kept in dry and ventilating place, prevent from rain and moisture when storage; if agglomerated, please crush and make it into solution, and its effect will be the same. 3 ,Transportation:non-toxic, harmless, non-inflammable and non-explosive chemicals, it can be transported in truck and train.
Product Description High Range Water-Reducing Admixture Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture Uses Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation Sodium Naphthalene Sulphonate Formaldehyde Specification: Solid Content :96.42% PH value :8.3 Chlorides Content :0.25% Sodium Sulfate Content :4.4%. For powder: woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg.
Appearance yellow brown or brown powder Lignosulphonate ¦55% Dry matter ¦ 93% Ph(1% aq. Solution) 8-9 Moisture 7% Water insoluble matter 1% Total reducing matter 4% Calcium magnesium general quantity 0. 5% 25kg in pp woven bag lined with plastic film
Appearance yellow brown or brown powder Lignosulphonate 60% Dry matter content 93% Ph(1% aq. Solution) 5-7 Moisture 7% Water insoluble matter 2% Inorganic salt 5% Reducing sugars content 3% 25kg in pp woven bag lined with plastic film
Appearance yellow brown or brown powder Moisture 8% Dry matter ² 93% Ph(2% aq. Solution) >7 Total caso4 %2.0 - 4.0 Total fe % 4% Insoluble alkaline material %2.5% 1. Thinning performance Test results indicate the thinning performance in fresh water based mud under normal temperature is comparable to ferrochrome lignosulfonate (fcls). At elevated temperature, it performs better than fcls in either fresh water or salt-water based mud, particularly the later. The product is suitable for use in drilling under complex geological formation, in water with high tds, or in offshore drilling. 2. Good fluid loss control properties Its major advantage is the thinning effect in drilling mud with high solid content, and simultaneously controls the fluid loss. Its fluid loss control action is better than fcls and the mud cake formed is smooth and compressible, thus beneficial for well bore protection and fluid loss reduction under high-pressure condition. 3. Higher retention of solid The product has improved solid retaining capacity due to its excellent thinning properties. Even when the mud is mixed with large quantity of clay while drilling, the rock scarps can still maintain good mobility. In addition it is capable of withstanding contamination by calcium, magnesium and sodium electrolytes, making it an ideal thinning agent for heavy weight mud. 4. Recommended dosage For salt water and fresh water based mud, a range of 0.5 to 1.0% is recommended depending on the specific conditions. Under special situations such as high solid and metal electrolytes content, a slight increase in dosage is recommended but not to exceed 2.0%. 5. Packing It is packed in 25 kg net weight moisture proof multi-wall paper bags, with pe film inside. Other size packing is also available on request.