Stainless steel shot
SUS304, SUS302 Stainless steel cut wire shot and stainless steel shot
Size: 0.3mm-1.5mm
Hardness: HVC400-600
Chemical elements: C: í_ 0.12%; Gr: 17-19%; Ni: 7-10%; S: í_ 0.03%; P: í_ 0.035%
Microstructure: Deformed Austenitic
Density: 7.8g/cm3
SUS430 Stainless steel cut wire shot and stainless steel shot
Size: 0.3mm-1.5mm
Hardness: HVC400-600
Chemical elements: C: í_ 0.12%; Gr: 17-19%; Ni: 4-7%; S: í_ 0.03%; P: í_ 0.03%
Microstructure: Martensite
Density: 7.8g/cm3
25kg in one bag,40bags on one pallet
Stainless steel shot long life time: 6000 times Size: 0.3-3mm High efficiency Surface treatment Sus304 stainless steel shot and stainless steel cut wire shot: Size: 0.2mm-2.0mm Hardness: 308-509 hv (32-50hrc) Chemical elements: c:
Stainless steel shot Cast steel shot: s780 s660 s550 s460 s390 s330 s280 s230 s170 s110 s70 Hardness: 40-50hrc density: 7.4g/cm3 Cast steel grit: g14 g16 g18 g25 g40 g50 g80 Hardness: gp 46-50hrc gl 56-60hrc gh 63-66hrc Density: 7.6g/cm3 Chemical compositions C 0.7-1.20% mn 0.60-1.20% si 0.4 -1.2 % s 0.05% p 0.05% Steel cut wire shot: cw1.0 cw1.5 Hardness: cw1.0 51-53 hrc Cw1.5 41-45 hrc Density: 7.8g/cm3 Chemical composition: C 0.45-0.75% mn 0.40-1.20% si 0.10-0.30% s 0.04 % p 0.04% 25kg in one bag, 40bags on one pallet
Introduction: The product is widely used in spraying and polishing surfaces of copper, aluminum, zinc and stainless steel workpieces, and has the advantages of matte effect, metallic character highlighting and rust-less property, ect. To processed workpieces, the processed workpiece do not need addtional cleaning of steel, and the durability is 3-5 times of steel shots, and the product can reduce the production costs. Features of blasting media stainless steel shot: A. High strength, high ductility, long service life; B. Low breakage, low wear, little dust; C.Low wear of the equipment, long life of accessory; D. Reduce dedusting system load, lengthen usage time of dedusting equipments. Blasting media stainless steel shot is always used for: A. Ship-building and ship-repariring B. Coating and corrosion processing of steel structures C. Railway vehicle coating D. Preventing corrosion of engineering machiner E. Preventing corrosion of welded pipes F. Preventing corrosion of port machinery G. Coating containers H. Strengthening surfaces of castings and forgings I. Intensifying surfaces of polished and sprayed shots J.Cleaning non-ferrous and stainless steel
Stainless steel cut wire shot Steel shot: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780 Steel grit: G14,G16,G18,G25,G40,G50,G80,G120 Steel cut wire shot: 1.0mm ,1.5mm ,2.0mm Stainless steel cut wire shot, 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm. Stainless steel shot 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm Copper and Aluminium shot ,0.3, 0.4, 0.5, 0.6, 0.8, 1.0, 1.2, 2.0mm Zinc Shot: 0.3-1.5mm 25KG
Steel shot The main products are cast steel shot , cast steel grit , steel cut wire shot , stainlees steel shot. Cast steel shot : s780 s660 s550 s460 s390 s330 s280 s230 s170 s110 s70 Hardness: 40-50hrc Density: 7.4g/cm3 Cast steel grit: g10 g12 g14 g16 g18 g25 g40 g54 g80 Hardness: gp 46-50hrc gl 56-60hrc gh 63-66hrc Density: 7.6g/cm3 Chemical compositions C 0.7-1.20% mn 0.60-1.20% si 0.4 -1.2 % s
Steel shot Steel shot: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780 Steel grit: G14,G16,G18,G25,G40,G50,G80,G120 Steel cut wire shot: 1.0mm ,1.5mm ,2.0mm Stainless steel cut wire shot, 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm. Stainless steel shot 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm Copper and Aluminium shot ,0.3, 0.4, 0.5, 0.6, 0.8, 1.0, 1.2, 2.0mm Zinc Shot: 0.3-1.5mm 25kg
Duplex 2205 is a nitrogen-enhanced duplex stainless steel that was developed to combat common corrosion problems encountered with the 300 series stainless steels. Duplex ? describes a family of stainless steels that are neither fully austenitic, like 304 stainless, nor purely ferritic, like 430 stainless. The structure of 2205 duplex stainless steel consists of austenite pools surrounded by a continuous ferrite phase. In the annealed condition, 2205 contains approximately 40-50% ferrite. Often referred to as the work horse grade, 2205 is the most widely used grade in the duplex family of stainless steels The advantage of a duplex structure is that it combines the favorable qualities of a ferritic alloy (stress corrosion cracking resistance and high strength) with those of an austenitic alloy (ease of fabrication and corrosion resistance). Usage of 2205 Duplex stainless steel should be limited to temperatures below 600 F. Extended elevated temperature exposure can embrittle 2205 stainless.
Duplex 2507 is a super duplex stainless steel designed for applications which demand exceptional strength and corrosion resistance. Alloy 2507 has 25% chromium, 4% molybdenum, and 7% nickel. This high molybdenum, chromium and nitrogen content results in excellent resistance to chloride pitting and crevice corrosion attack and the duplex structure provides 2507 with exceptional resistance to chloride stress corrosion cracking. Usage of Duplex 2507 should be limited to applications below 600�?�° F (316�?�° C). Extended elevated temperature exposure can reduce both the toughness and corrosion resistance of alloy 2507. Duplex 2507 possesses excellent mechanical properties. Often a light gauge of 2507 material can be used to achieve the same design strength of a thicker nickel alloy. The resulting savings in weight can dramatically reduce the overall cost of fabrication. The advantage of a duplex structure is that it combines the favorable qualities of a ferritic alloy (stress corrosion cracking resistance and high strength) with those of an austenitic alloy (ease of fabrication and corrosion resistance). Usage of 2205 Duplex stainless steel should be limited to temperatures below 600 F. Extended elevated temperature exposure can embrittle 2205 stainless
310S stainless steel is a highly alloyed austenitic stainless steel that is designed for use in high-temperature applications. It contains a high percentage of chromium and nickel, as well as a low amount of carbon, which gives it excellent resistance to oxidation, sulfidation, and other forms of high-temperature corrosion. Some of the key properties of 310S stainless steel include: High-temperature resistance: 310S can withstand high temperatures up to 1150�°C (2102�°F) without losing its strength or corrosion resistance properties, making it ideal for use in applications such as furnace parts, heat exchangers, and kilns. Corrosion resistance: 310S offers excellent resistance to oxidation, sulfidation, and other forms of high-temperature corrosion, as well as resistance to aqueous corrosion. Strength and toughness: 310S has good strength and toughness, making it suitable for use in demanding applications. Fabricability: 310S is easily formable using standard methods, and can be welded using common welding techniques. 310S stainless steel is commonly used in a range of high-temperature applications, including: Furnace parts, such as burners, heating elements, and retorts Heat exchangers and boilers Kilns and other high-temperature processing equipment Chemical processing equipment Power generation equipment, such as gas turbines and exhaust systems Overall, 310S stainless steel is a highly versatile and reliable material that is well-suited for use in a range of high-temperature applications where superior corrosion resistance and strength are required. The following are some of the commonly used international standards for 310S stainless steel: ASTM A240/A240M: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications ASTM A276/A276M: Standard Specification for Stainless Steel Bars and Shapes EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes EN 10095: Heat resisting steels and nickel alloys JIS G4304: Hot-rolled stainless steel plate, sheet and strip JIS G4305: Cold-rolled stainless steel plate, sheet and strip GB/T 4237: Hot rolled stainless steel plate, sheet and strip GB/T 3280: Cold rolled stainless steel plate, sheet and strip We can provide the following form:310S stainless steel coil; 310S stainless stee strip;310S stainless stee plate; 310S stainless steel sheets; 310S stainless steel tubes; 310S stainless steel pipe; 310S stainless steel flat; 310S stainless steel bar