Stainless steel shot
Cast steel shot: s780 s660 s550 s460 s390 s330 s280 s230 s170 s110 s70
Hardness: 40-50hrc density: 7.4g/cm3
Cast steel grit: g14 g16 g18 g25 g40 g50 g80
Hardness: gp 46-50hrc gl 56-60hrc gh 63-66hrc
Density: 7.6g/cm3
Chemical compositions
C 0.7-1.20% mn 0.60-1.20% si 0.4 -1.2 % s 0.05% p 0.05%
Steel cut wire shot: cw1.0 cw1.5
Hardness: cw1.0 51-53 hrc
Cw1.5 41-45 hrc
Density: 7.8g/cm3
Chemical composition:
C 0.45-0.75% mn 0.40-1.20% si 0.10-0.30% s 0.04 % p 0.04%
25kg in one bag, 40bags on one pallet
Stainless steel shot long life time: 6000 times Size: 0.3-3mm High efficiency Surface treatment Sus304 stainless steel shot and stainless steel cut wire shot: Size: 0.2mm-2.0mm Hardness: 308-509 hv (32-50hrc) Chemical elements: c:
Stainless steel shot SUS304, SUS302 Stainless steel cut wire shot and stainless steel shot Size: 0.3mm-1.5mm Hardness: HVC400-600 Chemical elements: C: í_ 0.12%; Gr: 17-19%; Ni: 7-10%; S: í_ 0.03%; P: í_ 0.035% Microstructure: Deformed Austenitic Density: 7.8g/cm3 SUS430 Stainless steel cut wire shot and stainless steel shot Size: 0.3mm-1.5mm Hardness: HVC400-600 Chemical elements: C: í_ 0.12%; Gr: 17-19%; Ni: 4-7%; S: í_ 0.03%; P: í_ 0.03% Microstructure: Martensite Density: 7.8g/cm3 25kg in one bag,40bags on one pallet
Introduction: The product is widely used in spraying and polishing surfaces of copper, aluminum, zinc and stainless steel workpieces, and has the advantages of matte effect, metallic character highlighting and rust-less property, ect. To processed workpieces, the processed workpiece do not need addtional cleaning of steel, and the durability is 3-5 times of steel shots, and the product can reduce the production costs. Features of blasting media stainless steel shot: A. High strength, high ductility, long service life; B. Low breakage, low wear, little dust; C.Low wear of the equipment, long life of accessory; D. Reduce dedusting system load, lengthen usage time of dedusting equipments. Blasting media stainless steel shot is always used for: A. Ship-building and ship-repariring B. Coating and corrosion processing of steel structures C. Railway vehicle coating D. Preventing corrosion of engineering machiner E. Preventing corrosion of welded pipes F. Preventing corrosion of port machinery G. Coating containers H. Strengthening surfaces of castings and forgings I. Intensifying surfaces of polished and sprayed shots J.Cleaning non-ferrous and stainless steel
Stainless steel cut wire shot Steel shot: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780 Steel grit: G14,G16,G18,G25,G40,G50,G80,G120 Steel cut wire shot: 1.0mm ,1.5mm ,2.0mm Stainless steel cut wire shot, 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm. Stainless steel shot 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm Copper and Aluminium shot ,0.3, 0.4, 0.5, 0.6, 0.8, 1.0, 1.2, 2.0mm Zinc Shot: 0.3-1.5mm 25KG
Steel shot The main products are cast steel shot , cast steel grit , steel cut wire shot , stainlees steel shot. Cast steel shot : s780 s660 s550 s460 s390 s330 s280 s230 s170 s110 s70 Hardness: 40-50hrc Density: 7.4g/cm3 Cast steel grit: g10 g12 g14 g16 g18 g25 g40 g54 g80 Hardness: gp 46-50hrc gl 56-60hrc gh 63-66hrc Density: 7.6g/cm3 Chemical compositions C 0.7-1.20% mn 0.60-1.20% si 0.4 -1.2 % s
Steel shot Steel shot: S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780 Steel grit: G14,G16,G18,G25,G40,G50,G80,G120 Steel cut wire shot: 1.0mm ,1.5mm ,2.0mm Stainless steel cut wire shot, 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm. Stainless steel shot 0.3mm,0.4mm,0.5mm,1.6mm,0.8mm,1.0mm Copper and Aluminium shot ,0.3, 0.4, 0.5, 0.6, 0.8, 1.0, 1.2, 2.0mm Zinc Shot: 0.3-1.5mm 25kg
Duplex 2205 is a nitrogen-enhanced duplex stainless steel that was developed to combat common corrosion problems encountered with the 300 series stainless steels. Duplex ? describes a family of stainless steels that are neither fully austenitic, like 304 stainless, nor purely ferritic, like 430 stainless. The structure of 2205 duplex stainless steel consists of austenite pools surrounded by a continuous ferrite phase. In the annealed condition, 2205 contains approximately 40-50% ferrite. Often referred to as the work horse grade, 2205 is the most widely used grade in the duplex family of stainless steels The advantage of a duplex structure is that it combines the favorable qualities of a ferritic alloy (stress corrosion cracking resistance and high strength) with those of an austenitic alloy (ease of fabrication and corrosion resistance). Usage of 2205 Duplex stainless steel should be limited to temperatures below 600 F. Extended elevated temperature exposure can embrittle 2205 stainless.
Duplex 2507 is a super duplex stainless steel designed for applications which demand exceptional strength and corrosion resistance. Alloy 2507 has 25% chromium, 4% molybdenum, and 7% nickel. This high molybdenum, chromium and nitrogen content results in excellent resistance to chloride pitting and crevice corrosion attack and the duplex structure provides 2507 with exceptional resistance to chloride stress corrosion cracking. Usage of Duplex 2507 should be limited to applications below 600�?�° F (316�?�° C). Extended elevated temperature exposure can reduce both the toughness and corrosion resistance of alloy 2507. Duplex 2507 possesses excellent mechanical properties. Often a light gauge of 2507 material can be used to achieve the same design strength of a thicker nickel alloy. The resulting savings in weight can dramatically reduce the overall cost of fabrication. The advantage of a duplex structure is that it combines the favorable qualities of a ferritic alloy (stress corrosion cracking resistance and high strength) with those of an austenitic alloy (ease of fabrication and corrosion resistance). Usage of 2205 Duplex stainless steel should be limited to temperatures below 600 F. Extended elevated temperature exposure can embrittle 2205 stainless
Supplier: Stainless steel shot, stainless steel cut wire, aluminum cut wire, zinc cut wire, zinc shot