SVR5 rubber is manufactured to meet ISO 2000:2014 . standards
Application
Shoe soles and sandals
â?? Tubes and tires for cars, motorbikes and bicycles
â?? Belts, cables and wires
â?? Rubber parts on cars and passenger cars
Gaskets and other accessories
Packaging and loading specifications:
SVR5 rubber is compressed with 2 main weights of 33.33kg/bale and 35kg/bale, usually packed in PE bags.
We are PEXIM - a manufacturer of natural rubber materials from Vietnam such as : RSS1, RSS3, SVR 10, SVR 20, SVR 5, SVR 3L, SVR CV50, SVR CV 60, SVR 10CV. - Supply ability: 1000 mts/month for per type - Port of loading : Hochiminh city port - Min. order: 20 mts - Specification: as Vietnamese Standards - Payment: L/C or T/T - Time of shipment: 7 days after receiving L/C PEXIM always commit to supply goods with high quality and reasonable price for all customers. Our products has been satisfied by all our customers from Asia, EU, America,...
* Description SVR 5 SVR 5 is a quality natural rubber. It is produced wholly from field latex. Field latex is preserved with ammonia or sodium sulfite. This is type of rubber which production process is the same SVR 3L grade. The field latex is coagulated with formic acid, and then make crumbs by passing through a crusher, some crepers and a shredder. After the dried crumbs are cooled and then compressed into blocks. * Used for The Manufacturing -Bicycle tubes -Rubber threads -Gas masks -Components in passenger vehicles -Components in tires * Features • Dark color than coloured SVR 3L. • Higher ash and dirt content compare with SVR 3L • High tensile strength • Good heat ageing resistance. * Specification Dirt : 0.05 max Ash : 0.60 max Volatile Matter: 0.80 max Nitrogen : 0.60 max Initial Wallace plasticity (Po): 30 min Plasticity Retention Index (PRI) : 60 min Color (Lovibond): 6 max *At time of production, ML 1+ 4 (100 oC) * Packing • 33.33 kg/bales or 35kg/bales, 600 bales/fcl 20 feet • In loose bale or Wooden Pallet * Bale Packaging • Normal 0.03 mm PE bag wrapper with melting temperature under 109 oC. • Thick (0.13 mm) PE bag wrapper
Specifications: Dirt (retained on 45 micron aperture) % wt: 0.08 Max Ash % wt: 0.6 Max Volatile matter % wt: 0.8 Max Nitrogen % wt: 0.6 Max Initial wallace plasticity (P0): 30 Min PRI (P30/P0) x 100: 50 Min Packaging: 33.33kgs/pack; 36packs/pallet, 16pallets=19.2mts/20ft.
Dirt (retained on 45 micron aperture) % wt: 0.08 Max Ash % wt: 0.6 Max Volatile matter % wt: 0.8 Max Nitrogen % wt: 0.6 Max Initial wallace plasticity (P0): 30 Min PRI (P30/P0) x 100: 50 Min
SVR3L is made from latex harvested from our rubber plantation. It can meet customer's strict requirement about some of technicalities such as: the Po, Color (Lovibond), This product is being applied in many fields: advanced automobile tire, wire belt, wire cable, sole of shoes, medical products, industrial electronics,
SVR3L is made from latex harvested from our rubber plantation. It can meet customer's strict requirement about some of technicalities such as: the PO, Color (Lovibond), SVR3L is made from latex harvested from our rubber plantation. It can meet customerâ??s strict requirement about some of technicalities such as: the PO, Color (Lovibond), â?¦ Latex is preserved by ammonia or sodium sulfite. Then coagulated with formic acid, followed by shredding by passing through a rolling mill, washing system and hash. After the crumb rubber is dried, it will be compressed into blocks and packed in polyethylene bags
Natural Rubber SVR3L have good resilience, abrasion and surface friction properties and excellent compression set. It has low hysteresis and rolling resistance with high fatigue resistance and remains flexible at low temperatures. Natural rubber SVR3L has poor resistance to oil, sunlight and ozone and limited thermal capability. Natural rubber SVR3L is superior tear strength and excellent resistance to heat buildup continues to make it a favored ingredient for high-performance tires for race cars, trucks, buses and aircraft. Other applications include tank lining, engine mounts, seals, vibration dampening and diaphragms.
Property SVR3L Test method 1.Dirt (retained on 45m aperature ), max. %wt 0. 03 max TCVN 6089:2004 2.Ash, max. %wt 3.Volatile matter, max. %wt 4.Nitrogen, max. %wt 5.Initial Wallace Platicity (P0) range 6.PRI (P30/P0) *100 7.Colour (Lovibond scale) 0.50 max 0.80 max 0.60 max 35 min 60 min 6 max TCVN 6087:2004 TCVN 6088:2004 TCVN 6091:2004 TCVN 6092:2004 TCVN 6092:2004 TCVN 6093:2004 8.Mooney Viscosity ML(1'+4')100oC TCVN 6090:2004 Rubber SVR 3L. Property 1.Dirt (retained on 45m aperature ), max. %wt 2.Ash, max. %wt 3.Volatile matter, max. %wt 4.Nitrogen, max. %wt 5.Initial Wallace Platicity (P0) range 6.PRI (P30/P0) *100 7.Colour (Lovibond scale) 8.Mooney Viscosity ML(1'+4')100oC SVR5 0.05 max 0.60 max 0.80 max 0.60 max 30 min 60 min
SVR 10 is a mixture of cup lump (the dried latex left in the bottom of tapping cups), tree lace (the strings of dried Rubber left along the tapping groove of the trees after tapping), and sometimes field coagulum (any late coagulated by a smallholder either in a collection vessel or on the ground). Loose bale : 33.33kg/bale or 35kg /bale 20-21.5 MT/ 20'FCL Wooden pallet : 36 bales/pallet , 16 pallet/20'FCL : 19.2MT/FCL with 33.33kg 20.16MT/FCL with 35k