Characteristics 1.Calcium Silicon Barium Inoculant ( CaSiBa ) increase the graphitization core, refinement of graphite, promote get A type graphite from the Grey iron castings, increase the intensity, for ductile iron parts, it can make the graphite in ductile iron ball small, round, improve the nodulizing grade. 2.Calcium Silicon Barium Inoculant ( CaSiBa ) effectively reduce molten iron super-cooling degree, promote the precipitation of graphite, significantly reduce chilling tendency, reduce the relative hardness, improve casting machinability. 3.Calcium Silicon Barium Inoculant ( CaSiBa ) easy to dissolve and absorb than the average inoculant. can reduce the gascontent in the molten iron. 4.Calcium Silicon Barium Inoculant ( CaSiBa ) hight ability to recession-proof. at the same time it prevent relevant nodulizing decline, wall thickness sensitivity is small, well-closed formation. Standard GradeChemical Element (%) SiCaBaAlPS â?¥(Min)â?¤(Max) Ca10Si50Ba1350.010.013.03.00.050.05 Ca13Si45Ba1045.013.010.0 Ca11Si45Ba1345.011.010.0 Ca9Si45Ba1345.09.010.0 Ca7Si45Ba1545.07.015.0 Ca5Si45Ba1545.05.015.0 The specification,packaging and granular size can be produce according to customer demand.
Ferro Silicon Ferro Silicon has a melting point of 1200°C to 1250°C with a boiling point of 2355°C and Ferro Silicon contains about 2% of calcium and alluminium. Ferro Silicon, as an additive to the production process of ferrous metals, will impart several desirable properties upon the resultant alloy. Some of the primary benefits of adding Ferro Silicon to an alloy is to improve the corrosion resistant properties of the new compound, as well as to add to the high temperature heat- resistance properties of the new alloy, for example, in the production of silicon steel for use in transformer cores. Ferro Silicon is an atomised alloy, which is formed by combining iron and silicon with a silicon content range of 15% to 90%. Ferro Silicon is a universal “heat-blocker” used in the production of carbon and stainless steels.
FerroSilicon uses coke, quartz (or silica) as raw material,and is made by electric furnace.Ferrosilicon is widely used in the steel making,iron casting ,low-carbon ferroalloy producing. Application: 1.In the steel making field,Ferrosilicon is used as deoxidizer and alloying agent to precipit and diffuse deoxidation.Adding a certain amount silicon of fe-si to the steel can obviously improve the strength ,hardness ,elasticity and permeability of steel. 2.In the iron casting,ferrosilicon is used as ball mile agent and alloying agent, especially in the nodular iron casting,Adding ferrosilicon to cast iron,it can prevent the formation of carbide and promote the precipitation of graphite and the nodulizing.then the mechanical capacity can be the same of steel's. 3.High-silicon ferrosilicon can be used for the production of the low-carbon reductant in ferro alloy industry. 4.In addition, ferrosilicon powder can be used as a suspended phase in the mineral processing industry and coatings for welding electrodes in the electrode manufactruing.
Fesi75-aSi 74.0~80.0Mn 0.4Ca 0.3Cr 0.1P 0.035S 0.02 Package: 1mt jumbo bag Dimensions: 0-10mm, 10-100mm
Ferro silic: 72%min / 75%min Al: 2%max C: 0.2%max S: 0.02%max P: 0.04%max Size: 10-60mm 90%min Packing in 1 mt bag and then put in containers