Chromite ore, also known as chromite ore, is a special sand for casting, is a natural spinel based on chromite, after crushing, grinding, screening into a specified size, suitable for molding (core) sand.
Cr2O3 46% Foundry grade chromite sand Cr2O3:46.0%min SiO2:1.0%max FeO:26.5%max CaO:0.30%max MgO:10.0%max Al2O3:15.5%max P:0.003%max S:0.003%max PACKING:1MT big bag SIZES:AFS 25-35 AFS25-30 AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65
ItemIndex Cr2O346.0% SiO21.0% FeO26.5% CaO0.30% MgO10.0% Al2O315.5% P0.003% S0.003% Cr/Fe1.55:1 Bulk Density2.5-3 ColorBlack PH7-9 The amount of the acid 2 ML Percent soil0.1% Percent Moisture0.1% The sintered1600 Percentage of free acid present in the sand0 filling density2.6g/cm³ sintering point> 1800°C melting temperature2180°C Regular size AFS 25-35 AFS25-30 AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65
Step1: chrome ore raw material is processed by water washing. Step2, drying raw materials to remove water; Step3, drying raw materials into the vibrating screen, screening out the size of the customer needs; Step4, the size of the sieve for magnetic separation, the purpose of iron and silicon removal. After magnetic separation, the chromium content reached more than 46% and the silicon content was less than 1%. Step5: package the finished product.
Foundry chromite sand is a natural process products of chromite through the broken screen classification, chrome ore, its main chemical composition of cr2o3, this kind of sand heated volume stability, high thermal conductivity, when in contact information with the molten metal, not only has good resistance to basic slag, not with ferric oxide and other chemical reactions, and itself has the characteristics of the solid phase sintering, can be a very good prevent the infiltration of molten metal, avoid to touch sand defects, suitable for all kinds of stainless steel, alloy steel and carbon steel gradually shape the original sand core and coating.
Cr2O3 46% AFS30-35 Top quality foundry chromite sand Top quality foundry chromite sand manufacturer (south africa).The chromite sand is a product of south africa natural chromite ore after crushing and sieving, and its main chemical composition is Cr2O3. *Melting point of 2150°C *Good thermal conductivity *Good resistance to thermal shock *Excellent resistance to metal penetration or burn-on *Resists slag attack *High dimensional stability
Export to Taiwan foundry chromite sand AFS35-40 We Import Chrome ore from South Africa,wash,dry,sieve,test,pack in China port,then export from China port. The specification is as follows: Cr2O3:46.0%min SiO2:1.0%max FeO:26.5%max CaO:0.30%max MgO:10.0%max Al2O3:15.5%max P:0.003%max S:0.003%max PACKING:1MT big bag SIZES:AFS 25-35 AFS25-30 AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65
Ramming mass is commonly used in metallurgy, building materials, non-ferrous metal smelting, chemical, machinery and other manufacturing industries. Ramming mass is widely used in non-core intermediate frequency furnace and core induction furnace. As an intermediate frequency furnace ramming material, refractory ramming is applied to melt gray cast iron, nodular cast iron, malleable cast iron, vermicular cast iron, and cast alloy steel; to melt carbon steel, alloy steel, high manganese steel, tool steel, heat resistant steel, stainless steel, molten aluminum and its alloys; to melt red copper, brass, white brass, bronze and its alloys, etc. Induction furnaces are used for melting cast iron, mild steel and various alloy steels in foundries and making of steel in mini steel plants using sponge iron The refined high silicon, low iron quartz sand and quartz powder are selected and the fused quartz sand is added as the refractory material., with no slag, no crack, damp proof, convenience of repair, and the corrosion resistance, thus greatly improving the furnace service life span and the economic benefit.. Silica ramming mass can safely be used up to an operating temperature of 1600 deg C. Since it expands very little, it is superior to both alumina and magnesia refractories to resist thermal shocks Acid ramming material is the premixed ramming mass of the lining material. The acid ramming mass is used to smelt a series of metal materials such as ordinary steel and carbon steel. The lining practice best suited to a particular furnace depends upon the capacity and design of the furnace, operation practice adopted during making of a heat, and furnace output.
Supplier: Silica sand, china clay, kaolin, bentonite, white coal, quartz powder, bhuj sand, silica powder, granules, foundry silica sand, glass grad silica sand
Supplier: Building & construction materials, minerals and chemicals, fly ash (astm c618 class f / bs en 450 / bs 3892), ggbfs / gbs, aggregates (crushed stones, stone chips), bentonite (drilling, pilling, foundry, construction), kaolin/china clay, salt/sodium chloride (industrial grade, food grade)
Services: Exports