Product description
White corundum is made of high quality aluminum oxide powder as raw material, refined and crystallized by electric melting. It has high purity, good self-sharpening, acid and alkali corrosion resistance, high temperature resistance and stable thermal performance. Its hardness is slightly higher than that of brown corundum.It is suitable for grinding fine grain abrasive such as high carbon steel, high speed steel and stainless steel.
chemical component Physical characteristics
size AL2O3
8# 10# 12# 14# 16# 20# 22# 24# 30# 36# 40# 46# 54# 60# 70# 80# 90# 100# 120# 150# 180# 220# 240# â?¥99.5%
0-1mm 1-3mm 3-5mm 5-8mm â?¥99.5%
100#-0 200#-0 320#-0 â?¥99%
FEPA:F230 F240 F280 F320 F360 F400 F500 F600 F800 F1000 F1200 F1500 F2000
JIS:#240 #280 #320 #360 #400# #500 #600 #700 #800 #1000 #1200 #1500 #2000 #2500 #3000 #4000 #6000 #8000 â?¥99.2%
White Fused Alumina polishing was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling.It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.
Model: White fused alumina F320 Chemical compositions Al2O3: 99.50%min SiO2: 0.04%max Na2O: 0.26%max Fe2O3: 0.05%max. Physical properties Color: White Bulk density: 1.75-1.95g/cm3 Grain density: 3.90g/cm3min Morse hardness: 9 Content of magnetic substance: 0.0023%max. 25kg PVC bags + 1MT big bag
Moh's hardness 9.0 Bulk density 1.75-1.95g/cm³ Real density 3.95g/cm³ Melting point 2250 Maximum service temperature 1900
Polishing abrasive white carborundum powder White carborundum powder was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling.It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved. Physical Index color white Mohs Hardness 9.0 Melting point 2250 Maximum service temperature 1900 Bulk density 1.75-1.95g/cm3 Real density 1.75-1.95g/cm3 Chemical analysis Al2O3(min) 99.6% SiO2(max) 0.4% Fe2O3(max) 0.2% Na2O(max) 0.4%
Moh's hardness 9.0 Bulk density 1.75-1.95g/cm³ Real density 3.95g/cm³ Melting point 2250 Maximum service temperature 1900
White Fused Aluminum oxide polishing material Chemical Compositions: Al2O3:99.20-99.70% Fe2O3:0.04-0.10% Na2O:0.23-0.35% Physical Properties: B.D:1.75-1.95g/cm3 Specific Gravity:3.95g/cm3 Mohs Hardness:9.0 Application: Bonded abrasives and Coated abrasives Floor / Wall Laminates Thermal Spraying (Plasma Spraying) Lapping & Micro-blasting applications Super Refractories, Ceramics and Tiles Brake linings Available Size: JIS STANDARD: JIS#240 #280 #320 #360 #400# #500 #600 #700 #800 #1000 #1200 #1500 #2000 #2500 #3000 #4000 #6000 #8000 #10000 FEPA STANDARD: F230 F240 F280 F320 F360 F400 F500 F600 F800 F1000 F1200 F1500 F2000
Quick Details Place of Origin: Henan, China Brand Name: Yihong Polishing Wheel Model Number: YH-Unmounted Felt Wheel Type: Abrasive Disc Product name: 100% Felt disc Certificate: ISO9001: 2008 flap disc Exported countries: Germany, Italy, Turkey, Korea, India and other countries Colour: White Application: Especially for early stage and mirror finishing Material: 100% Felt Package: Standard Package MOQ: 1000pcs Advantage: High Working Efficiency Sample: Available Supply Ability Supply Ability: 100000 Piece/Pieces per Month
Rigger Glove (RSP 1001)-YB : Natural Cow Split Leather (Brown) Back Color Cotton (Yellow) 3 Finger Tips Knuckle Strap Rubberized Cuff Color Piping on Edge (Yellow).
Rigger Glove (RSP 1001)-PC : Natural Cow Split Leather (White) Back Color Cotton (Printed Cotton) 3 Finger Tips Knuckle Strap Rubberized Cuff â?¢ Color Piping on Edge.