White Fused Alumina polishing was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling.It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.
Moh's hardness 9.0 Bulk density 1.75-1.95g/cm³ Real density 3.95g/cm³ Melting point 2250 Maximum service temperature 1900
Moh's hardness 9.0 Bulk density 1.75-1.95g/cm³ Real density 3.95g/cm³ Melting point 2250 Maximum service temperature 1900
Hot sale White fused alumina/corundum/WA for polishing and grinding White fused alumian/corundum is an artificial corundum abrasive, the main component of aluminum oxide (Al2O3), and contains a small amount of iron oxide, silicon oxide, etc., the color was white. White corundum high quality alumina powder as raw material, refined crystalline and fused into, there are dense texture, high hardness, high temperature, acid corrosion, thermal stability properties. particles cusp form for use in the manufacture of ceramics, resin bonded abrasives and grinding, polishing, blasting, precision casting, can also be used to manufacture advanced refractory. Characteristic 1.High hardness 2.High purity 3.Good self-sharpening 4.Strong grinding ability 5.Acid-alkali corrosion resistance 6.High temperature resistance and 7.Good thermal stability Application 1.Spraying and grinding. 2.High-end products, crafts or hardware products surface beautification processing. 3.Precision casting, silicon crystal cutting, advanced refractories and ceramic additives. 4.Bonded abrasives and coated abrasives. 5.Processing harder and stronger tensile strength materials such as quenching steel, alloy steel, high speed steel and high carbon steel. 6.Ultra-precision Grinding and Polishing in Crystal and Electronics Industry, Precise Surface Treatment of Metal and Optical Products 7.Contact media, insulators and precision casting sand.
White Fused Aluminium Oxide (WFA)� is widely used for Abrasive Tools, Sandblasting, Polishing, Surface Preparation. Our WFA is a hard, dense and iron-free material with highest purity, hence is an ideal abrasive material. It also has above 95% Al2O3 content, high degree of whiteness, extreme hardness and a wide range of precise grit sizes.
Brown fused alumina polishing Brown aluminum oxide crystals is made of bauxite/anthracite coal, and smelted in electric-arc furnace of high temperature more than 2000degrees.Abrasives tools made by brown fused alumina are suitable for metal with high tensile (like:steel, malleable iron, bronze etc).and suitable for grinding, polishing, blasting, precision casting etc.Brown aluminum oxide crystal is also used for refractory material. Brown aluminum oxide crystals with characteristics like: high purity, good crystalline liquidity, low coefficient of linear expansion, corrosion resistance, high temperature, high strength. Chemical analysis: Al2O3(min) 92% SiO2(max) 2% Fe2O3(max) 2% TiO2(max) 4% Physical characteristics: color Brown Mohs Hardness 9.0 Melting point 2250â?? Maximum service temperature 1850â?? Bulk density 1.53-1.99g/cm3 Specific gravity 3.6-3.9g/cm3 Purpose: 1.grinding for konescope/glass/monocryst alline silicon/lens/jadeware 2.abrasion-proof material for expressway/airstrip/dock/ parking lot/stadium 3.bonded abrasives and coated abrasives 4.surface preparation and finishing 5.Thermal Spraying(Plasma Spraying) 6.Super Refractories, Ceramics and Tiles 7.Lapping & Micro-blasting applications Other models: Grain 0-1mm 1-3mm 3-5mm 5-8mm Fine powder 0-100mesh 0-200mesh 0-320mesh Grit 8# 10# 12# 14# 16# 20# 22# 24# 30# 36# 40# 46# 54# 60# 70# 80# 90# 100# 120# 150# 180# 220# Micro powder (FEPA)F230 F240 F280 F320 F360 F400 F500 F600 F800 (JIS) #240 #280 #320 #360 #400# #500 #600 #700 #800 #1000 #1200 #1500 #2000
Brown Fused Alumina is fused and crystallized under the high temperature of above 2250°C with high quality bauxite, carbon and iron as raw material. Our product characterized by high purity, good crystal, strong fluidity, low coefficient of linear expansion, good corrosion-resistance and so on. Could not burst, no pulverization and crArtificial brown corundum / brown fused alumina gritack in using course of refractory.
Product Description Brown Fused Alumina is fused and crystallized under the high temperature of above 2250°C with high quality bauxite, carbon and iron as raw material. Our product characterized by high purity, good crystal, strong fluidity, low coefficient of linear expansion, good corrosion-resistance and so on. Could not burst, no pulverization and crack in using course of refractory. Advantage 1. Brown corundum is characterized by high purity, dense texture, large stacking density, strong self-sharpness, good toughness and extremely low magnetic content; 2. The grinding tool made of it has the advantages of sharp grinding, low heating rate, high grinding ratio and less adhesion in use; 3.The sintered abrasive tool has the characteristics of deep blue color, no network crack and no rust spot after firing.
white fused alumina Al2O3: >99%, SiO2:
Bond Abrasive White Fused Aluminum Oxide Alumina 99% WFA F20 F30 F36 Abrasion Resistant Description: Product Color: Prue White Mohs Hadness: 10 Mohs Melting Temperature: 2250 Degree Min Refractory Temperature: 1900 Degree Min Density: 3.45 G/cm3 Min Name: White Fused Aluminum Oxide High Light: white fused aluminium oxide,white corundum white fused alumina electrically fused in arc furnace with high grade processed alumina as raw material. It has higher hardness and slight lower toughness comparing with brown fused alumina. It is also characterized by its high purity, ability of self-sharpening, better cutting, less heat emit, higher efficiency. White fused aluminum oxide becomes the first choice for the sandblasting technics, meanwhile, it is also the ideal material for sandblasting and workpiece cleaning, and polishing. Specification: property of aluminum oxide/white aluminum oxide: Purpose Specification Chemical composition(%) Magnetic material content(%) Al2O3 Na2O SiO2 CaO For abrasive F 12# 80# 99.2Min 0.4Max 0.4 Max 0.003 Max 90# 150# 99.0Min 0.4 Max 0.003 Max 180# 240# 99.0Min 0.4 Max 0.4 Max 0.002 Max Particle size : F8, F10, F12, F14, F16, F20, F22, F24, F30, F36, F40, F46, F54,F60, F70, F80, F90, F100, F120, F150, F180, F220 Packing:1 MT big bag or 25kg paper bag *40 bags on one pallet ; As per customers requirement Fused White Alumina advantages: 1, High grade processed alumina as raw material. 2, High hardness, big specific gravity, 3, Good chemical stability and unique self-sharpening Bond Abrasive White Fused Aluminum Oxide Alumina 99% WFA F20 F30 F36 Abrasion Resistant 0