PVC solvent cement
Appearance/ colour : liquid/ pale yellow.
Specific gravity at 230 c 0.94(+ 0.03).
Viscosity ford cup 4 sec's : 70 (+ 5)
Solid content % : 20 (+ 4)
Cementing /cure time hrs : 2.5 to 3.5
Service temperature deg.C : (-)10 to (+)85
Applications : for use with pvc conduit, drain, waste and vent pipe up to 4" diameter.
Tin containers of 125ml, 250ml, 500ml & 1 ltr only.
Ground granulated blast furnace slag
1. Fineness (m2 /kg): 370.
2. Soundness le-chatelier expansion (mm) : nil.
3. Initial setting time (min)
Not less than opc:220.
4. Insoluble residue(%):0.05
5. Magnesia content (%):9.5
6.Sulphide sulphar(%):0.60
7. Sulphite content (%):0.10
8. Loss on ignition (%):0.30
9. Manganese content (%):0.06
10. Chloride content(%):0.003
11. Moisture content(%):0.005
12. Glass content(%):94
13. Compressive strength (n/mm2):
After 7 days34.0
After 28 days53.0
14. Chemical moduli
A). Cao + mgo + sio2 :84.0
B). Cao + mgo /sio2 :1.30
C). Cao/sio2 :1.05.
Tonnes packed in i tonne or i.5 jumbo bags.
1. Fineness (m2 /kg): 370.
2. Soundness le-chatelier expansion (mm): nil.
3. Initial setting time (min)
Not less than opc:220.
4. Insoluble residue(%):0.05
5. Magnesia content (%):9.5
6.Sulphide sulphar(%):0.60
7. Sulphite content (%):0.10
8. Loss on ignition (%):0.309. Manganese content (%):0.06
10. Chloride content(%):0.003
11. Moisture content(%):0.005
12. Glass content(%):94
13. Compressive strength (n/mm2):
After 7 days34.0
After 28 days53.0
14. Chemical moduli
A). Cao + mgo + sio2 :84.0
B). Cao + mgo /sio2 :1.30
C). Cao/sio2 :1.05.
Tonnes( 1 tnnes and 1.5 tones in jumbo bags).