Product feature
1.High strength, high elasticity, excellent stickiness and cohesion
made stickiness/airproof more flexible and resistent.
2.One-component, moisture curable, non-sagging, no dropping on stand
surface, convenience construction.
3.No solvent, no corrosion to base materials, no pollution to the
environment.
4.Excellent sealing, puncture resistance, good aging, oil and water
resistance.
Applications
1.Elastic bondings for windshield and side glass of automobile repair.
Technical Data
Test items Performance
Density: 1.25+/-0.05g/cm3
Touch dry time: 10~60 min
Curing in 24h: 3~5mm
Volatile content: <=4%
Strength at break: >=6.0MPa
Shore A hardness: 55+/-5A0
Elongation at break: >=450%
Extrudability: 150g/min
Application temperature: +5~+35 C;
310 ml cartridge packing/400ml, 600ml sausage packing
CHARACTER:
1. One component, needless blending, convenient construction, no
sagging, no dropping on stand surface.
2. No solvent, no poison could be used in producing food places, no
pollution to environment.
3. High strength, low modulus,, excellent cohesion, making sealing
parts flexible and durable.
4. Excellent adhesion to concrete, tile, brick, stone, Aluminum, glass
and wood etc. And could coat many kinds of paintings on the surface.
5. No corrosion, no pollution to base materials.
6. Excellent sealing, puncture resistance, good aging, oil and water
resistance etc.
TECHNICAL DATA
DENSITY: 1.4+/-0.1g/cm3
TOUCH DRY TIME: 15~180min
CURING SPEED: 3~5mm/d
VOLATILE CONTENT: <=4%
SHORE A HARDNESS: 20~40Ao
STRENGTH AT BREAK: >=1.5MPa
ELONGATION AT BREAK: >=400%
100%STABLE STRETCH MODULUS: <=0.4MPa
APPLICATION TEMPERATURE: -40~+85C
LOW TEMPERATURE FLEXIBILITY: -40C
STABLE STRETCH ADHESION: NO DAMAGE
ELASTIC RECOVERY: >=75%
CONSTRUCTION TEMPERATURE: +5~+35 C
SHELF LIFE: >=6 MONTHS
310ml cartridge packing/ 400ml,600ml sausage packing.
Product feature
1.High strength, high elasticity, excellent stickiness and cohesion
made stickiness/airproof more flexible and resistent.
2.One-component, moisture curable, non-sagging, no dropping on stand
surface, convenience construction.
3.No solvent, no corrosion to base materials, no pollution to the
environment.
4.Excellent sealing, puncture resistance, good aging, oil and water
resistance.
Applications
1.Elastic bondings for windshield and side glass of automobile repair.
Technical Data:
Test items Performance
Density: 1.3+/-0.01g/cm3
Touch dry time: 10~60 min
Curing in 24h: 3~5mm
Volatile content: <=4%
Shore A hardness: 60+/-10Ao
Strength at break: >=4.0MPa
Packed in cartridge/sausage, carton packing with 20 pcs units.