Specification of Consol AS1200
1.1. Raw material No. AISI 304
1.2. Yield Strength 1020N/mm²
1.3. Tensile strength 1150 N/mm²
1.4. Weld factor 0.70(Rm weld/Rm)
1.5. Hardness HV5 : 360-380
1.6. Modulus Elasticity E 196000MPA
1.7. Density 7.9g/cm³
1.8. Thermal expansion(20-200°C) 18x10-6 m/m
1.9. Thermal conductivity(100°C) 16W/m
1.10.Belt Operation Temperature -80~300
1.11.Belt Size 1500mm x 1.0mm
1.12 Belt size tolerance Thickness +/- 8%
Width 0-2mm ,Straightness 5mm
1.13 Surface Roughness Ra0.4 µm
1.14 Surface Flatness: h:l1:250, hmax3mm
1.15 Maximum allowed conveyor speed 60m/min
1.16 percentage elongation A % 22 weld joit 18%
1.17 Belt Joint open length with one end welding prepared
Martensite stainless steel belt MS1650 is made of precipitated, quenched, martensitic stainless steel, and this class has high strength, hardness and corrosion resistance. After heat treatment, the mechanical properties of the products will be more perfect and reach up to 200 mpa compressive strength.This class steel belt can be used at high or low temperature environment(450 �° c) . It has excellent corrosion resistance to the atmosphere and to dilute acids or salts,the same corrosion resistance as steel 304 and 430.
##Martensite steel belt characteristics
Hard surface with strong strength.
Excellent fatigue resistance.
Good corrosion resistance.
Easy to repair and maintain.
High welding technology, can be shipped endless.
Dynamic strength
The definition of fatigue limit is that under a certain alternating stress, 50% of the test samples can withstand the load cycle of 2 million times. Test at 20 dry environment, the fatigue limit of parent metal is + 630 N/mm squared (91 Ksi).
##Corrosion resistance
MS1650 shows good corrosion resistance under normal air conditions. However, the steel belt should not be applied to the environment with hydrochloric acid.
## Scope of supply
Length: customizable
Width: 1000/1200/1500/2000/3000.
Thickness: 1.0/1.2/1.6//2.0
CS1300 steel belt is tempered carbon steel, which has follow steel belt characteristics:
Good static strength
Outstanding fatigue resistance
Great thermal conductivity
Excellent fatigue and wear resistance
Easy to maintain and repair
CS1300 carbon steel belt has the hard and smooth surface, which has a layer of oxide on it. This steel belt is widely used in many fields with low causticity environment. Because of the outstanding thermal conductivity,CS1300 is very suitable for baking process, it also performs well in heating and drying liquid, paste and particle. Compare with stainless steel belt, carbon steel belt has better thermal conduction properties.
Steel-belt Cooler Granulation/pastillator Technology
Under the new situation,the advantages of the steel belt cooler pastillator have been continuously explored and become an indispensable production equipment in various industrial fields, a large number of companies who need powder and solidification are greatly used the steel belt cooler as core production line.