Carbon Fiber Cloth is made of carbon fiber by woven unidirectional, plain weaving or twill weaving style. The carbon fibers we use contain high strength-to-weight and stiffness-to-weight ratios, carbon fabrics are thermally and electrically conductive and exhibit excellent fatigue resistance. When properly engineered, carbon fabric composites can achieve the strength and stiffness of metals at significant weight savings. Carbon fabrics are compatible with various resin systems including epoxy, polyester and vinyl ester resins.
There are unidirectional carbon fiber fabric used as reinforcement clothing for bridge, road and building. The bidirectional carbon fiber fabric are woven with Plain ,Twill style,satin weave and other pattern.
Material: 100% carbon fiber/
Features: Abrasion-Resistant, Anti-Static, Heat-Insulation, Waterprof
Weight: 100-600 gsm
Width: 100-1500mm
Size: 100m/roll
Style: plain/ twill
Thickness: 0.10-0.64mm
Uses: Any construction, sports industry, automobiles industry, Etc
Carbon fiber plate is carbon fiber impregnated resin curing and continuous pultrusion in the mold. It's made of high-quality carbon fiber and good epoxy resin by yarn tension uniformity, maintaining the strength of carbon fiber and product stability. Tensile strength up to 2800Mpa, elastic modulus up to 170Gpa.
Material: 100% carbon fiber and resin
Width: 5cm 10cm, 20cm
thickness: 1-4mm
Tensile strength: 2400-2800 mpa
Size: 100m/roll
Uses: Building, bridge and any civil work reinforcement.
poxy resin glue is epoxy fiber adhesive of high performance, can be used for the effective penetration bonding between many substrate materials, such as concrete, steel material, ceramic, stone, wood component and many fiber plate such as carbon fiber plate, basalt fiber plate, glass fiber plate etc. It is mainly used for the strengthening and reinforcement of buildings, bridge and civil construction.
Classification: Double components adhesive
Mixing Ratio: 2:1 (A:B)
Viscosity: 4000-6000 Pa.s
Appearance: Viscous Liquid
Color: White & Black
Uses: Construction, Fiber & Garment, Footwear & Leather, Packing, on concrete substance etc.
Aramid fiber fabric has ultra-high strength, high modulus and high temperature resistance, acid and alkali resistance, light and other good performance, its strength is 5-6 times of steel wire, the modulus is 2-3 times of the steel wire or glass fiber, its toughness is 2 times of the steel wire while it only weighs about 1/5 of steel wire. In around a temperature of 560, it does not decompose and melt. I t has a good insulation and anti-aging properties with a long life cycle.
Main application:
Tires, bullet-proof vest, aircraft,spacecraft, sporting goods, conveyor belts, high strength ropes, constructions and cars etc.
Material: 100% Aramid fiber
Weight: 80-500 gsm
Weave: Plain/twill/unidirectional
Thickness: 0.1-1mm
Width: 100-1500mm
Features: anti static, bulletproof and chemical resistant.
Glass fiber rebar or GFRP is a new kind of composite material which is used as reinforcement materials that combines with epoxy resin and curing agent then through pultrusion molding process.
Products Feature:
1. High Corrosion Resistance:The base materials used by the bolt are durable materials, and they are molded through the composite process. The life span is up to 100 years. They can be used as permanent support materials;
2. High Tensile Strength:The load is approximately double that of a steel bar with the same diameter;
3. Low weight-The weight is only 1/4 that of a steel bar with the same diameter, therefore, the labor intensity is greatly reduced, and the transportation cost is reduced at the same time
5. Anti-static-It has no electrical conductivity, and no sparks will be produced when being cut, it's particularly suitable for high gas zones;
6. Non-flammable-It's non-flammable and has high thermal isolation;
7. Culpability-It avoids damages to cutter heads, and does not delay excavation
8. Save cost-Use this material as reinforcing bars for road and bridge, could reduce secondary repair cost.
Material: 100% glass fiber and epoxy
Surface: all thread
Diameter: 3-40 mm
Tensile strength: 780-1200Mpa
Density: 1.9-2.1 g/cm3
E-Modulus: >45 gpa