The molecular weight of ultra-fine powder of PTFE is only 1% of the general PTFE which not only maintained the excellent performance of original, but also has high crystallinity dispersion,and easy to uniformly mixed with other materials.It is widely used in the synthesis material modification,and can significantly improve the lubricity,wear resistance,non-adhesive and fire retardant of the substrate.It also can be used as rubber ,lubricant grease,printing links, coatings,engineer plastic and other additives and additive
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
The molecular weight of ultra-fine powder of PTFE is only 1% of the general PTFE which not only maintained the excellent performance of original, but also has high crystallinity dispersion,and easy to uniformly mixed with other materials.It is widely used in the synthesis material modification,and can significantly improve the lubricity,wear resistance,non-adhesive and fire retardant of the substrate.It also can be used as rubber ,lubricant grease,printing links,
1. Exterior: white fine powder
2. Moisture content: less than 0.03
3. Average particle size: less than 5 micron
4. Tensile strength: 8 Mpa
5. Fracture elongation: 60%
6. Appaent density: 0.56g/ square centimeter
7. Thermal gravitational: less than 0.2%Wt
8. Corrosion resistance: No change
9. Melting point: 327 more or less centigrade
10. Decomposition temperature: 430 centigrade
11. Melt viscosity: 102-106 Pa.S
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
1 Exterior:white fine powder
2. Moisture content:less than 0.03
3 Average particle size: 20-100 micro
4 Tensile strength: 27.5 Mpa
5. shrink rate: less than 4.5
6: Appaent density: 2.13-2.19
7. elogation: more than 280
8. Corrosion resistance: No change
9. Melting point: 327 Centigrade
The molecular weight of ultra-fine powder of ptfe is only 1% of the general ptfe which not only maintained the excellent performance of original, but also has high crystallinity dispersion, and easy to uniformly mixed with other materials.It is widely used in the synthesis material modification, and can significantly improve the lubricity, wear resistance, non-adhesive and fire retardant of the substrate.It also can be used as rubber , lubricant grease, printing links, coatings, engineer plastic and other additives.
1. Exterior: white fine powder
2. Moisture content: less than 0.03
3. Average particle size: less than 5 micron
4. Tensile strength: 8 mpa
5. Fracture elongation: 60%
6. Appaent density: 0.56g/ square centimeter
7. Thermal gravitational: less than 0.2%wt
8. Corrosion resistance: no change
9. Melting point: 327 more or less centigrade
10. Decomposition temperature: 430 centigrade
11. Melt viscosity: 102-106 pa.S
1. Exterior: white fine powder
2. Moisture content: less than 0.03
3. Average particle size: 20-100 micro
4. Tensile strength: 8 Mpa
5. Fracture elongation: 60%
6. Appaent density: 0.56g/ square centimeter
7. Thermal gravitational: less than 0.2%Wt
8. Corrosion resistance: No change
9. Melting point: 327 more or less centigrade
10. Decomposition temperature: 430 centigrade
11. Melt viscosity: 102-106 Pa.S